AVALIAÇÃO DE DESEMPENHO DE FERRAMENTAS DE AÇO AISI 1045 REVESTIDAS COM FILME DE TIN PARA PROCESSO DE SOLDAGEM POR ATRITO (FSW)

PERFORMANCE EVALUATION OF AISI 1045 STEEL TOOLS COATED WITH TIN FILM FOR FRICTION WELDING PROCESS (FSW)

Autoria

Aguilera, Leticia; Teodoro, Bruno Neves Targino; Oliveira, Paulo Rodrigues; Neves, Henrique Hochleitner; Silveira, José Luís Lopes da; Silva, Alexandre Mello de Paulo; Campos, José Brant de

DOI

10.5151/2594-5327-34751

Downloads

Baixar Artigo 29 Downloads

Resumo

A NECESSIDADE DE SE REALIZAR SOLDAS COM DEMANDAS CADA VEZ MAIS ESPECÍFICAS, COMO A UNIÃO ENTRE MATERIAIS DISSIMILARES E DEVIDO AO ALTO CUSTO QUE OCORRE NA REALIZAÇÃO DE SOLDAS EM LIGAS QUE TRADICIONALMENTE APRESENTAM DIFICULDADE DE UNIÃO PELOS PROCESSOS DE SOLDAGENS CONVENCIONAIS, SÃO DIFICULDADES IMPOSTAS NO RAMO DA SOLDAGEM. NESTE CENÁRIO, SURGE O PROCESSO DE SOLDAGEM POR FRICÇÃO DENOMINADO DE FRICTION STIR WELDING (FSW), QUE SE DESTACA DOS OUTROS PROCESSOS COMUNS DE SOLDAGEM, JUSTAMENTE POR SER CAPAZ DE RESPONDER A ESSAS SOLICITAÇÕES DE MANEIRA EFICIENTE. O OBJETIVO DESTE TRABALHO FOI AVALIAR A QUALIDADE DE UM FILME DE TIN DEPOSITADO POR MAGNETRON SPUTTERING EM FERRAMENTAS DE AÇO AISI 1045 PARA O PROCESSO FSW VISANDO O AUMENTO DA SUA VIDA ÚTIL. O FILME FOI CARACTERIZADO POR MICROSCOPIA ELETRÔNICA DE VARREDURA (MEV) E ESPECTROSCOPIA DE ENERGIA DISPERSIVA (EDS) QUANTO A MORFOLOGIA, HOMOGENEIDADE DA DEPOSIÇÃO E INTEGRIDADE APÓS ENSAIOS DE FRICTION STIR PROCESS (FSP). O DESEMPENHO DAS FERRAMENTAS FOI AVALIADO PELO ENSAIO FSP, COMPARANDO ESFORÇOS RESULTANTES E DEFORMAÇÕES ENTRE AS FERRAMENTAS COM E SEM O FILME.

 

THE NEED TO CARRY OUT WELDS WITH INCREASINGLY SPECIFIC DEMANDS, SUCH AS THE UNION BETWEEN DISSIMILAR MATERIALS AND DUE TO THE HIGH COST, THAT OCCURS IN PERFORMING WELDS IN ALLOYS THAT TRADITIONALLY HAVE DIFFICULTY IN JOINING BY CONVENTIONAL WELDING PROCESSES, ARE DIFFICULTIES IMPOSED IN THE FIELD OF WELDING. IN THIS SCENARIO, THE FRICTION WELDING PROCESS KNOWN AS FRICTION STIR WELDING (FSW) EMERGES, WHICH STANDS OUT FROM OTHER COMMON WELDING PROCESSES, PRECISELY BECAUSE IT IS ABLE TO RESPOND TO THESE REQUESTS EFFICIENTLY. THE OBJECTIVE OF THIS WORK WAS TO EVALUATE THE QUALITY OF A TIN FILM DEPOSITED BY MAGNETRON SPUTTERING ON AISI 1045 STEEL TOOLS FOR THE FSW PROCESS, AIMING TO INCREASE ITS USEFUL LIFE. THE FILM WAS CHARACTERIZED BY SCANNING ELECTRON MICROSCOPY (SEM) AND ENERGY DISPERSION SPECTROSCOPY (EDS) FOR MORPHOLOGY, DEPOSITION HOMOGENEITY AND INTEGRITY AFTER FRICTION STIR PROCESS (FSP) TESTS. THE PERFORMANCE OF THE TOOLS WAS EVALUATED BY THE FSP TEST, COMPARING RESULTING EFFORTS AND DEFORMATIONS BETWEEN THE TOOLS WITH AND WITHOUT THE FILM.

Palavras-chave

Magnetron Sputtering; Microscopia Eletrônica de Varredura; Friction Stir Process; Filme de TiN.

Magnetron Sputtering; Scanning Electron Microscopy; Friction Stir Process; TiN film.