AVALIAÇÃO DE PARÂMETROS TECNOLÓGICOS DO CONCRETO COM CASCA DE ARROZ CARBONIZADA COMO SUBSTITUTA PARCIAL DO CIMENTO PORTLAND

EVALUATION OF TECHNOLOGICAL PARAMETERS OF CONCRETE WITH CARBONIZED RICE HULK AS A PARTIAL REPLACEMENT FOR PORTLAND CEMENT

Autoria

LIMA, THUANY ESPIRITO SANTO DE

LIMA, THUANY ESPIRITO SANTO DE

Eu sou esse autor

DOI

10.5151/2594-5327-40450

Downloads

Resumo

A INDúSTRIA CIMENTíCIA é UMA DAS PRINCIPAIS FONTES DE POLUIçãO AMBIENTAL DEVIDO à ALTA EMISSãO DE DIóXIDO DE CARBONO (CO2) DURANTE A PRODUçãO DO CIMENTO PORTLAND, CONTRIBUINDO PARA AS MUDANçAS CLIMáTICAS. ALéM DISSO, O AGRONEGóCIO NO BRASIL GERA UMA GRANDE QUANTIDADE DE RESíDUOS, COMO A CASCA DE ARROZ, QUE SãO NORMALMENTE DESCARTADOS DE MANEIRA ERRADA. NESSE CONTEXTO, O PRESENTE TRABALHO VISA AVALIAR PARâMETROS TECNOLóGICOS DO CONCRETO COM SUBSTITUIçãO PARCIAL DO CIMENTO PORTLAND PELA CASCA DE ARROZ CARBONIZADA (CAC), BUSCANDO REDUZIR A POLUIçãO E PROMOVER A SUSTENTABILIDADE NA CONSTRUçãO CIVIL, AO MESMO TEMPO EM QUE SE BUSCA ECONOMIZAR CUSTOS. COM ISSO, O OBJETIVO PRINCIPAL DESTE ESTUDO é INVESTIGAR O DESEMPENHO DO CONCRETO COM DIFERENTES NíVEIS DE SUBSTITUIçãO DE CIMENTO POR CAC (5%, 7% E 10%). PARA ISSO, REALIZOU-SE UM EXPERIMENTO PRáTICO, TRITURANDO A CAC PARA GARANTIR UMA MISTURA HOMOGêNEA E UTILIZANDO UM ADITIVO PLASTIFICANTE PARA MELHORAR A TRABALHABILIDADE DO CONCRETO. FORAM MOLDADOS OITO CORPOS DE PROVA PARA CADA TRAçO, TOTALIZANDO 32 AMOSTRAS. FORAM EXECUTADOS DIVERSOS ENSAIOS, INCLUINDO O SLUMP TEST PARA AVALIAR A CONSISTêNCIA, A RESISTêNCIA à COMPRESSãO AXIAL PARA VERIFICAR A CAPACIDADE DE SUPORTAR CARGAS VERTICAIS, A RESISTêNCIA à COMPRESSãO DIAMETRAL PARA ANALISAR A RESISTêNCIA à TRAçãO E ENSAIOS DE CAPILARIDADE PARA AVALIAR A DURABILIDADE E A ABSORçãO DE áGUA. OS RESULTADOS OBTIDOS MOSTRAM QUE A SUBSTITUIçãO DO CIMENTO POR CAC AFETA POUCO OS PARâMETROS TECNOLóGICOS DO CONCRETO, TENDO UMA TRABALHABILIDADE E ABSORçãO DE áGUA DENTRO DO PADRãO ESPERADO PARA UTILIZAçãO EM VáRIAS APLICAçõES DO CONCRETO NA CONSTRUçãO CIVIL. APESAR DA PERDA DE RESISTêNCIA NOS TRAçOS COM CAC, MANTEVE-SE NíVEIS ACEITáVEIS COM O TRAçO COM 7% DE SUBSTITUIçãO MOSTRANDO RESULTADOS MELHORES ENTRE OS TRAçOS COM CAC. ASSIM, ESTE ESTUDO BUSCA CONTRIBUIR PARA A REDUçãO DA EMISSãO DE CARBONO DA INDúSTRIA DA CONSTRUçãO CIVIL, PROMOVENDO O USO DE RESíDUOS AGRíCOLAS COMO ALTERNATIVA SUSTENTáVEL E ECONôMICA NA PRODUçãO DE CONCRETO. OS RESULTADOS OBTIDOS PODEM TER IMPLICAçõES IMPORTANTES NA ADOçãO DE PRáTICAS MAIS SUSTENTáVEIS NO SETOR DA CONSTRUçãO, BENEFICIANDO TANTO O MEIO AMBIENTE QUANTO A ECONOMIA.

THE CEMENT INDUSTRY IS ONE OF THE MAIN SOURCES OF ENVIRONMENTAL POLLUTION DUE TO THE HIGH EMISSION OF CARBON DIOXIDE (CO2) DURING THE PRODUCTION OF PORTLAND CEMENT, CONTRIBUTING TO CLIMATE CHANGE. FURTHERMORE, AGRIBUSINESS IN BRAZIL GENERATES A LARGE AMOUNT OF WASTE, SUCH AS RICE HUSKS, WHICH ARE NORMALLY DISCARDED INCORRECTLY. IN THIS CONTEXT, THE PRESENT WORK AIMS TO EVALUATE TECHNOLOGICAL PARAMETERS OF CONCRETE WITH PARTIAL REPLACEMENT OF PORTLAND CEMENT BY CARBONIZED RICE HUSK (CAC), SEEKING TO REDUCE POLLUTION AND PROMOTE SUSTAINABILITY IN CONSTRUCTION, WHILE SEEKING TO SAVE COSTS. THEREFORE, THE MAIN OBJECTIVE OF THIS STUDY IS TO INVESTIGATE THE PERFORMANCE OF CONCRETE WITH DIFFERENT LEVELS OF CEMENT REPLACEMENT BY CAC (5%, 7% AND 10%). TO ACHIEVE THIS, A PRACTICAL EXPERIMENT WAS CARRIED OUT, CRUSHING THE CAC TO ENSURE A HOMOGENEOUS MIXTURE AND USING A PLASTICIZING ADDITIVE TO IMPROVE THE WORKABILITY OF THE CONCRETE. EIGHT SPECIMENS WERE MOLDED FOR EACH TRAIT, TOTALING 32 SAMPLES. SEVERAL TESTS WERE CARRIED OUT, INCLUDING THE SLUMP TEST TO EVALUATE CONSISTENCY, AXIAL COMPRESSION STRENGTH TO VERIFY THE ABILITY TO WITHSTAND VERTICAL LOADS, DIAMETRAL COMPRESSION STRENGTH TO ANALYZE TENSILE STRENGTH AND CAPILLARITY TESTS TO EVALUATE DURABILITY AND ABSORPTION. OF WATER. THE RESULTS OBTAINED SHOW THAT REPLACING CEMENT WITH CAC HAS LITTLE EFFECT ON THE TECHNOLOGICAL PARAMETERS OF CONCRETE, WITH WORKABILITY AND WATER ABSORPTION WITHIN THE EXPECTED STANDARD FOR USE IN VARIOUS CONCRETE APPLICATIONS IN CIVIL CONSTRUCTION. DESPITE THE LOSS OF RESISTANCE IN THE TRAITS WITH CAC, ACCEPTABLE LEVELS WERE MAINTAINED WITH THE TRAIT WITH 7% REPLACEMENT, SHOWING BETTER RESULTS AMONG THE TRAITS WITH CAC. THEREFORE, THIS STUDY SEEKS TO CONTRIBUTE TO REDUCING CARBON EMISSIONS FROM THE CONSTRUCTION INDUSTRY, PROMOTING THE USE OF AGRICULTURAL WASTE AS A SUSTAINABLE AND ECONOMICAL ALTERNATIVE IN CONCRETE PRODUCTION. THE RESULTS OBTAINED MAY HAVE IMPORTANT IMPLICATIONS FOR THE ADOPTION OF MORE SUSTAINABLE PRACTICES IN THE CONSTRUCTION SECTOR, BENEFITING BOTH THE ENVIRONMENT AND THE ECONOMY.

Palavras-chave

Concreto Sustentável; Casca de arroz carbonizada; Substituição parcial de cimento; Redução de poluiç

Sustainable Concrete; Charred rice husk; Partial replacement of cement; Pollution reduction.