AVALIAÇÃO DE RESISTÊNCIA À TRAÇÃO DE PAPEL KRAFT RAFIADO COMO POTENCIAL REFORÇO HÍBRIDO EM COMPÓSITOS

TENSILE STRENGTH ANALISIS OF KRAFT PAPER AS A POTENTIAL HYBRID REINFORCEMENT IN COMPOSITES

Autoria

Moreira, Mariane Oliveira; Simonassi, Noan Tonini; Monteiro, Sergio Neves; Duarte, Felipe Perissé; Vieira, Carlos Maurício Fontes; Loiola, Rômulo Leite

DOI

10.5151/2594-5327-34693

Downloads

Baixar Artigo 9 Downloads

Resumo

O OBJETIVO DO ESTUDO É AVALIAR O POTENCIAL DE REUSO DOS SACOS REVESTIDOS COM POLIETILENO INTERNO COMO REFORÇO HÍBRIDO EM COMPÓSITOS POLIMÉRICOS. OS SACOS REVESTIDOS FORAM CORTADOS, LAVADOS, SECOS EM ESTUFA E PRENSADOS A QUENTE (200°C) PARA PRODUZIR UM LAMINADO. FOI AVALIADA RESISTÊNCIA MÁXIMA A TRAÇÃO (ASTM 3039) E A DEFORMAÇÃO NESSA RESISTÊNCIA MÁXIMA PARA LAMINADOS FABRICADOS COM DIFERENTES TEMPOS DE PRENSAGEM; 15, 20 E 25 SEGUNDOS. A SIGNIFICÂNCIA ESTATÍSTICA ENTRE OS TEMPOS DE PRENSAGEM FOI AVALIADA POR ANÁLISE DE VARIÂNCIA (ANOVA). OS RESULTADOS ESTATÍSTICOS MOSTRARAM QUE A VARIAÇÃO DE TEMPO NÃO FOI ESTATISTICAMENTE SIGNIFICATIVA PARA A RESISTÊNCIA MÁXIMA, ENTRETANTO FOI SIGNIFICATIVA PARA A ELONGAÇÃO. A DEFORMAÇÃO DIMINUI COM O AUMENTO DO TEMPO DE PRENSAGEM.

 

THIS STUDY AIMS TO EVALUATE THE POTENTIAL REUSE OF BAGS COATED WITH POLYETHYLENE AS A HYBRID REINFORCEMENT IN POLYMERIC MATRIX COMPOSITES. THE COATED BAGS WERE CUT, WASHED, KILN DRIED AND HOT PRESSED (200°C) TO PRODUCE A LAMINATED MATERIAL. THE TENSILE STRENGTH (ASTM 3039) AND ELONGATION FOR THE LAMINATED MANUFACTURED WITH DIFFERENT PRESSING TIMES WERE EVALUATED; 15, 20 AND 25 SECONDS. THE STATISTICAL SIGNIFICANCE BETWEEN THE PRESSING TIMES WAS EVALUATED BY ANALYSIS OF VARIANCE (ANOVA). THE STATISTICAL RESULTS INCREASED THAT SUCH TIME VARIATION WAS NOT STATISTICALLY SIGNIFICANT FOR THE MAXIMUM STRENGTH, HOWEVER IT WAS DEFINED FOR THE ELONGATION. DEFORMATION DECREASES WITH INCREASING PRESSING TIME.

Palavras-chave

Embalagens; Kraft; Compósitos; Resíduos; ANOVA

Packaging; Kraft; Composites; Waste; ANOVA