AVALIAÇÃO DO COMPORTAMENTO ELETROQUÍMICO DOS AÇOS MARAGING 300 E 350 APÓS EXPOSIÇÃO EM ATMOSFERA DE CO2/VAPOR (H2O) PARA OBTENÇÃO DE ÓXIDOS SUPERFICIAIS

EVALUATION OF THE ELECTROCHEMICAL BEHAVIOR OF MARAGING 300 AND 350 STEEL AFTER EXPOSURE TO CO2/STEAM ATMOSPHERE

Autoria

Ribeiro, Joshua Alyson Freitas

Ribeiro, Joshua Alyson Freitas

Eu sou esse autor

DOI

10.5151/2594-5327-34677

Downloads

Resumo

OS AÇOS MARAGING SÃO DE EXTREMA IMPORTÂNCIA PARA A INDÚSTRIA ATUAL, DENTRE AS MUITAS APLICAÇÕES POSSÍVEIS DESSE MATERIAL, ESTÃO ALGUNS COMPONENTES DE ULTRACENTRÍFUGAS UTILIZADAS PARA ENRIQUECIMENTO DE URÂNIO. COM ESTRUTURA MARTENSÍTICA E ALTO TEOR DE ELEMENTOS DE LIGA, É MUITO COMUM QUE SE UTILIZE DE TRATAMENTOS TÉRMICOS PARA ADEQUAR AS PROPRIEDADES DO MATERIAL AO USO ESPECÍFICO. É SABIDO QUE A EXPOSIÇÃO DE TAIS AÇOS EM ATMOSFERAS E TEMPERATURAS ESPECÍFICAS ACARRETAM NA FORMAÇÃO DE ÓXIDOS SUPERFICIAIS COM MICROESTRUTURA DO TIPO ESPINÉLIO, QUE PODEM AJUDAR NA RESISTÊNCIA À CORROSÃO DO MATERIAL. A PESQUISA TEM COMO OBJETIVO O ESTUDO DA INFLUÊNCIA DOS ÓXIDOS FORMADOS APÓS A EXPOSIÇÃO DOS AÇOS EM ATMOSFERA DE CO2/ VAPOR DE H2O NAS PROPRIEDADES ELETROQUÍMICAS. AS ANÁLISES FORAM FEITAS POR MEIO DAS TÉCNICAS DE POTENCIAL DE CIRCUITO ABERTO, ESPECTROSCOPIA POR IMPEDÂNCIA ELETROQUÍMICA E POLARIZAÇÃO LINEAR. A COMPARAÇÃO FOI REALIZADA COM AS AMOSTRAS SEM O RECOBRIMENTO DE ÓXIDO NAS CONDIÇÕES SOLUBILIZADA E ENVELHECIDA A 480ºC POR 3 HORAS. OS EXPERIMENTOS FORAM REALIZADOS EM SOLUÇÃO DE ÁCIDO FLUORÍDRICO NA CONCENTRAÇÃO DE 0,01M.

MARAGING STEELS ARE EXTREMELY IMPORTANT FOR THE INDUSTRY, AMONG THE MANY POSSIBLE APPLICATIONS OF THIS MATERIAL, THERE ARE SOME COMPONENTS OF ULTRACENTRIFUGES USED FOR URANIUM ENRICHMENT. WITH MARTENSITIC MICROSTRUCTURE AND HIGH CONTENT OF ALLOYING ELEMENTS, IT IS COMMON TO USE HEAT TREATMENTS TO ADAPT THE PROPERTIES OF THE MATERIAL TO THE SPECIFIC USE. IT IS KNOWN THAT THE EXPOSURE OF SUCH STEELS TO SPECIFIC ATMOSPHERES AND TEMPERATURES LEADS TO THE FORMATION OF SURFACE OXIDES WITH SPINEL TYPE MICROSTRUCTURE, WHICH CAN HELP IN THE CORROSION RESISTANCE OF THE MATERIAL. THIS RESEARCH AIMS TO STUDY THE INFLUENCE OF OXIDES FORMED AFTER EXPOSURE OF STEELS IN A CO2 / H2O VAPOR ATMOSPHERE ON ELECTROCHEMICAL PROPERTIES. THE ANALYZES WERE PERFORMED USING THE TECHNIQUES OF OPEN CIRCUIT POTENTIAL, ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY AND LINEAR POLARIZATION. THE COMPARISON WAS MADE WITH THE SAMPLES WITHOUT THE OXIDE COATING IN THE SOLUBILIZED AND AGED CONDITIONS AT 480ºC FOR 3 HOURS. THE EXPERIMENTS WERE CARRIED OUT IN A 0.01M HYDROFLUORIC ACID SOLUTION.

Palavras-chave

Maraging; Recobrimento; Corrosão

Eletrochemical Properties; Spinel; Oxide; Coating