AVALIAÇÃO DO COMPORTAMENTO MECÂNICO DE TECIDO HÍBRIDO REFORÇANDO A MATRIZ DE EPÓXI: ENVELHECIMENTO ACELERADO POR RADIAÇÃO UV*

EVALUATION OF THE MECHANICAL BEHAVIOR OF HYBRID FABRIC REINFORCING THE EPOXY MATRIX: ACCELERATED AGING BY UV RADIATION

Autoria

Oliveira, Michelle Souza; Caminha, Clara Beatriz Melo Moreira; Nascimento, Lucio Fabio Cassiano; Monteiro, Sergio Neves

DOI

10.5151/2594-5327-34167

Downloads

Baixar Artigo 10 Downloads

Resumo

OS COMPÓSITOS DE MATRIZ TERMOFIXA TÊM SIDO AMPLAMENTE UTILIZADOS EM DIVERSOS SETORES INDUSTRIAIS. MUITAS DESSAS APLICAÇÕES EXPÕEM O MATERIAL EM AMBIENTES QUE COMPROMETEM SEU USO, INDUZINDO O ENVELHECIMENTO, OU ATÉ ENVELHECENDO O MATERIAL. E AINDA, O USO DE FIBRAS LIGNOCELULÓSICAS NATURAIS (FLNS) MINIMIZA A POLUIÇÃO AMBIENTAL E OS CUSTOS DE PRODUÇÃO DE MATERIAIS COMPÓSITOS. COMPREENDER SOBRE O ENVELHECIMENTO DE FNLS TEM-SE TORNADO UM NOVO DESAFIO PARA A INDÚSTRIA DE COMPÓSITOS. O PROCESSO DE ENVELHECIMENTO ENVOLVE VÁRIOS MECANISMOS SIMULTÂNEOS E APARENTEMENTE INDEPENDENTES E, PORTANTO, MONITORAR A EVOLUÇÃO DAS VARIÁVEIS COM O TEMPO ESPECIFICADO É UM MÉTODO EFICIENTE PARA AVALIAR O COMPORTAMENTO DOS COMPÓSITOS POLIMÉRICOS REFORÇADOS COM FIBRAS NATURAIS EM CONDIÇÕES ACELERADAS DE ENVELHECIMENTO. O OBJETIVO DESTE TRABALHO É OBTER AS PROPRIEDADES DE TRAÇÃO DE UM COMPÓSITO EPOXÍDICO REFORÇADO COM TECIDO HÍBRIDO DE 50 MALVA/ 50 JUTA ANTES E DEPOIS DE REALIZAR O ENVELHECIMENTO ACELERADO POR RADIAÇÃO ULTRAVIOLETA. OS ACHADOS DESTE TRABALHO REVELAM QUE O COMPÓSITO HÍBRIDO APRESENTA UMA PERDA DE RESISTÊNCIA À TRAÇÃO NOS PRIMEIROS 30 MIN, E A RIGIDEZ DIMINUI A PARTIR DA PRIMEIRA EXPOSIÇÃO. ASSIM COMO ACONTECE COM OS SERES VIVOS, OS POLÍMEROS E SEUS COMPOSTOS TAMBÉM SÃO SUSCETÍVEIS À AÇÃO DA RADIAÇÃO ULTRAVIOLETA.

 

THERMOSET MATRIX COMPOSITES HAVE BEEN WIDELY USED IN SEVERAL INDUSTRIAL SECTORS. MANY OF THESE APPLICATIONS EXPOSE THE MATERIAL IN ENVIRONMENTS THAT COMPROMISE ITS USE, INDUCING AGING, OR EVEN AGING THE MATERIAL. IN ADDITION, THE USE OF NATURAL LIGNOCELLULOSIC FIBERS (FLNS) MINIMIZES ENVIRONMENTAL POLLUTION AND THE PRODUCTION COSTS OF COMPOSITE MATERIALS. UNDERSTANDING THE AGING OF FNLS HAS BECOME A NEW CHALLENGE FOR THE COMPOSITES INDUSTRY. THE AGING PROCESS INVOLVES SEVERAL SIMULTANEOUS AND APPARENTLY INDEPENDENT MECHANISMS AND, THEREFORE, MONITORING THE EVOLUTION OF VARIABLES WITH THE SPECIFIED TIME IS AN EFFICIENT METHOD TO ASSESS THE BEHAVIOR OF POLYMERIC COMPOSITES REINFORCED WITH NATURAL FIBERS UNDER ACCELERATED AGING CONDITIONS. THE OBJECTIVE OF THIS WORK IS TO OBTAIN THE TENSILE PROPERTIES OF AN EPOXY COMPOSITE REINFORCED WITH HYBRID FABRIC OF 50 MAUVE / 50 JUTE BEFORE AND AFTER PERFORMING ACCELERATED AGING BY ULTRAVIOLET RADIATION. THE FINDINGS OF THIS WORK REVEAL THAT THE HYBRID COMPOSITE SHOWS A LOSS OF TENSILE STRENGTH IN THE FIRST 30 MIN, AND THE STIFFNESS DECREASES FROM THE FIRST EXPOSURE. AS WITH LIVING THINGS, POLYMERS AND THEIR COMPOUNDS ARE ALSO SUSCEPTIBLE TO THE ACTION OF ULTRAVIOLET RADIATION.

Palavras-chave

Desempenho mecânico; Radiação UV; Envelhecimento de materiais; Ensaio de tração; Tecidos naturais; C

Mechanical performance; UV radiation; Aging materials; Tensile test; Natural fabric; Polymer composi