Título

AVALIAÇÃO DO COMPORTAMENTO MECÂNICO EM TRAÇÃO DOS COMPÓSITOS EPÓXI-CARANÃ

EVALUATION OF MECHANICAL BEHAVIOR IN TRACTION OF EPOXYCARANAN COMPOSITES

Autoria

Souza, Andréssa Teixeira; Junio, Raí Felipe Pereira; Neuba, Lucas de Mendonça; Oliveira, Michelle Souza; Monteiro, Sérgio Neves; Nascimento, Lucio Fabio Cassiano

DOI

10.5151/2594-5327-34080

Downloads

Baixar Artigo 32 Downloads

Resumo

PESQUISAS SOBRE COMPÓSITOS REFORÇADOS COM FIBRAS NATURAIS ESTÃO EM CRESCIMENTO, UMA VEZ QUE, É POSSÍVEL IDENTIFICAR UMA SÉRIE DE BENEFÍCIOS NAS FIBRAS NATURAIS LIGNOCELULÓSICAS (FNLS) COMO: BAIXA ABRASIVIDADE, BAIXO CUSTO, BAIXA DENSIDADE E ALTA RESISTÊNCIA ESPECÍFICA. ESSAS PROPRIEDADES ALIADAS À BIODEGRADABILIDADE DAS MESMAS AUMENTAM AINDA MAIS O INTERESSE NA PRODUÇÃO DE COMPÓSITOS POLIMÉRICOS REFORÇADOS COM FIBRAS NATURAIS (CFNLS). ASSIM SENDO, FORAM INVESTIGADOS NESTE TRABALHO AS PROPRIEDADES EM TRAÇÃO DOS COMPÓSITOS EPOXÍDICOS REFORÇADOS COM FIBRAS DE CARANÃ, SEGUNDO A NORMA TÉCNICA ASTM D3039. PELA PRIMEIRA VEZ NA LITERATURA FORAM OBTIDOS RESULTADOS SOBRE O LIMITE DE RESISTÊNCIA (MPA), MÓDULO DE ELASTICIDADE (GPA) E DEFORMAÇÃO MÉDIA (%) DESSA FIBRA AGREGADA A UMA RESINA POLIMÉRICA. AS ANÁLISES CONCLUÍRAM QUE FIBRAS COM 20% E 30% V/V SÃO EFICAZES COMO REFORÇO ENQUANTO QUE COM 10% V/V FUNCIONAM COMO CARGA DE ENCHIMENTO.

 

RESEARCH ON COMPOSITES REINFORCED WITH NATURAL FIBERS IS INCREASING, SINCE IT IS POSSIBLE TO IDENTIFY A SERIES OF BENEFITS IN NATURAL LIGNOCELLULOSIC FIBERS (FNLS) SUCH AS: LOW ABRASIVENESS, LOW PRICE, LOW DENSITY AND HIGH RESISTANT ESPECIFIC STRENGTH. THESE PROPERTIES COMBINED WITH THEIR BIODEGRADABILITY RAISE INTEREST IN THE PRODUCTION OF COMPOSITES REINFORCED WITH NATURAL FIBERS (CFNLS). THEREFORE, IN THIS WORK, THE TENSILE PROPERTIES OF COMPOSITES REINFORCED WITH CARANAN FIBER WERE INVESTIGATED, ACCORDING TO THE TECHNICAL STANDARD ASTM D3039. FOR THE FIRST TIME IN THE LITERATURE, RESULTS WERE OBTAINED ON THE STRENGTH LIMIT (MPA), ELASTIC MODULUS (GPA) AND AVERAGE DEFORMATION (%) OF THIS FIBER ADDED TO A POLYMERIC RESIN. THE STUDY CONCLUDED THAT THE FIBERS WITH 20% AND 30% V / V ARE APPLIED AS REINFORCEMENT, WHILE 10% V / V WORK AS A FILLER.

Palavras-chave

Caranã, Fibras naturais, Ensaio de tração, ASTM D3039.

Caranan, Natural fibers, Tensile Teste, ASTM D3039.