O RAMO INDUSTRIAL EM GERAL GERA UMA QUANTIDADE CONSIDERáVEL DE RESíDUOS, COM ENFOQUE ESPECIAL A DO GRANITO, VEM GERANDO CONSIDERáVEIS VOLUMES DE RESíDUOS, ACARRETANDO EM IMPACTOS AMBIENTAIS NEGATIVOS OCASIONADOS PELO DESCARTE INADEQUADO. COM ESTE FATO EM FOCO, SURGE A OPORTUNIDADE DE VALORIZAR ESSES RESíDUOS ATRAVéS DA PRODUçãO DE ROCHAS ARTIFICIAIS, COMBINANDO SUSTENTABILIDADE COM DESEMPENHO TéCNICO E ECONôMICO FAVORáVEL. O PRESENTE ESTUDO VISA à PRODUçãO E CARACTERIZAçãO DE GRANITO ARTIFICIAL UTILIZANDO MATRIZ POLIMéRICA DE RESINA EPóXI COM A IMPLEMENTAçãO DE UMA FIBRA SINTéTICA NA QUAL FOI UTILIZADA A FIBRA DA MALHA DE VIDRO,ONDE A ROCHA é PRODUZIDA EMPREGANDO O MéTODO DE VIBROCOMPRESSãO à VáCUO. OS RESíDUOS DE CORTE DO GRANITO FORAM FRAGMENTADOS E, ATRAVéS DO MODELO SIMPLEX CENTRóIDE, DETERMINOU-SE A MISTURA GRANULOMéTRICA IDEAL PARA COMPACTAçãO. A QUANTIDADE MíNIMA DE RESINA NECESSáRIA PARA PREENCHER OS ESPAçOS ENTRE AS PARTíCULAS FOI CALCULADA. AS PLACAS DE ROCHA ARTIFICIAL FORAM PRODUZIDAS COM 85% EM MASSA DE PARTICULADOS DE GRANITO UTILIZANDO UMA GRANULOMETRIA ENTRE 10 E 40 MESH, COM UM TEOR DE 15% DE RESINA EPOXI. SOB VáCUO DE 600 MMHG, AS PLACAS FORAM SUBMETIDAS à PRESSãO DE COMPACTAçãO DE 10 TONELADAS, A 90°C PARA RAPO E 80°C PARA AS DEMAIS, DURANTE 20 MINUTOS. APóS LIXAMENTO E CORTE, AS PLACAS FORAM AVALIADAS QUANTO àS SUAS CARACTERíSTICAS FíSICAS (DENSIDADE, POROSIDADE APARENTE, ABSORçãO DE áGUA) E MECâNICA (RESISTENCIA AO IMPACTO). OS RESULTADOS OBTIDOS DEMONSTRAM QUE A ROCHA ARTIFICIAL POSSUI PROPRIEDADES ADEQUADAS PARA APLICAçãO EM REVESTIMENTOS.
THE INDUSTRIAL SECTOR IN GENERAL GENERATES A CONSIDERABLE AMOUNT OF WASTE, WITH A SPECIAL FOCUS ON GRANITE, IT HAS BEEN GENERATING CONSIDERABLE VOLUMES OF WASTE, RESULTING IN NEGATIVE ENVIRONMENTAL IMPACTS CAUSED BY INADEQUATE DISPOSAL. WITH THIS FACT IN FOCUS, THE OPPORTUNITY ARISES TO VALUE THIS WASTE THROUGH THE PRODUCTION OF ARTIFICIAL ROCKS, COMBINING SUSTAINABILITY WITH FAVORABLE TECHNICAL AND ECONOMIC PERFORMANCE. THE PRESENT STUDY AIMS AT THE PRODUCTION AND CHARACTERIZATION OF ARTIFICIAL GRANITE USING A POLYMER MATRIX OF EPOXY RESIN WITH THE IMPLEMENTATION OF A SYNTHETIC FIBER IN WHICH GLASS MESH FIBER WAS USED, WHERE THE ROCK IS PRODUCED USING THE VACUUM VIBRO COMPRESSION METHOD. THE GRANITE CUTTING RESIDUES WERE FRAGMENTED AND, USING THE SIMPLEX CENTROID MODEL, THE IDEAL GRANULOMETRIC MIXTURE FOR COMPACTION WAS DETERMINED. THE MINIMUM AMOUNT OF RESIN REQUIRED TO FILL THE SPACES BETWEEN THE PARTICLES WAS CALCULATED. THE ARTIFICIAL ROCK SLABS WERE PRODUCED WITH 85% BY MASS OF GRANITE PARTICLES USING A GRAIN SIZE THAT WAS CONSIDERED COARSE AND 15% POLYESTER RESIN (RAPO). UNDER A VACUUM OF 600 MMHG, THE PLATES WERE SUBJECTED TO COMPACTION PRESSURE OF 10 TONS, AT 90°C FOR RAPO AND 80°C FOR THE OTHERS, FOR 20 MINUTES. AFTER SANDING AND CUTTING, THE PLATES WERE EVALUATED FOR THEIR PHYSICAL CHARACTERISTICS (DENSITY, APPARENT POROSITY, WATER ABSORPTION), MECHANICAL (3-POINT BENDING TEST, WEAR), RESISTANCE TO CHEMICAL ATTACKS AND STAINING, AND MICROSTRUCTURE BY ELECTRON MICROSCOPY. SCAN. THE RESULTS OBTAINED DEMONSTRATE THAT ARTIFICIAL ROCK HAS SUITABLE PROPERTIES FOR APPLICATION IN COATINGS.
Palavras-chave
Rocha Artificial, Resíduos de Granito, Epóxi
Artificial Rock, Waste Granite, Epoxy
Como citar
JACINTHO, PABLO BARBOSA;
GOMES, MARIA LUIZA PESSANHA MENEZES;
LIRIO, JOSÉ LUCAS DECOTÉ DE CARVALHO;
CARVALHO, SÁVIO DOS SANTOS;
CARVALHO, ELAINE APARECIDA SANTOS;
VIEIRA, CARLOS MAURÍCIO FONTES.
AVALIAÇÃO DO EFEITO DA ADIÇÃO DA FIBRA DE VIDRO COMO REFORÇO EM ROCHAS ARTIFICIAIS
,
p. 617-625.
In: 22º Enemet - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas,
São Paulo, Brasil,
2024.
ISSN: 2594-4711
, DOI 10.5151/2594-4711-41389