Título

AVALIAÇÃO DO FILME DE TIN EM FERRAMENTAS DE AÇO AISI 1045 PARA O PROCESSO DE SOLDAGEM POR ATRITO (FSW).

EVALUATION OF THE TIN FILM IN AISI 1045 STEEL TOOL FOR THE FRICTION STIR WELDING PROCESS, FSW

Autoria

Aguilera, Leticia; Oliveira, Paulo Rodrigues; Teodoro, Bruno Neves Targino; Silva, Alexandre Mello de Paulo; Silveira, José Luís Lopes da; Campos, José Brant de

DOI

10.5151/2594-5327-34630

Downloads

Baixar Artigo 9 Downloads

Resumo

A BUSCA POR PROPRIEDADES ESPECÍFICAS EM PEÇAS E FERRAMENTAS DE GRANDES ESFORÇOS MECÂNICOS PARA AS MAIS DIVERSAS APLICAÇÕES TEM GERADO AVANÇOS NAS TÉCNICAS DE DEPOSIÇÃO DE MATERIAIS EM FILMES PARA INCREMENTO DO TEMPO DE VIDA DA FERRAMENTA E SUAS PROPRIEDADES MECÂNICAS NA SUPERFÍCIE. DESTA FORMA, INÚMEROS PROCESSOS FORAM CRIADOS E DIVERSAS TÉCNICAS QUE VISAM A CARACTERIZAÇÃO DAS SUPERFÍCIES DE TRABALHO SÃO EMPREGADAS PARA A AVALIÇÃO DOS REVESTIMENTOS. O OBJETIVO DO TRABALHO CONSISTIU NA CARACTERIZAÇÃO ESTRUTURAL E AVALIAÇÃO DA SUPERFÍCIE DE AMOSTRAS DE UMA FERRAMENTA DE AÇO AISI 1045 COM SUPERFÍCIE LIMPA EM BANHO ULTRASSÔNICO, JATEADA COM ESFERAS DE VIDRO E NITRETADAS, COM DEPOSIÇÃO DE FILME DE TIN POR MAGNETRON SPUTTERING. A RUGOSIDADE SUPERFICIAL TAMBÉM FOI AVERIGUADA E OBSERVOU-SE QUE HOUVE DIMINUIÇÃO APÓS OS PROCESSOS DE NITRETAÇÃO E DEPOSIÇÃO DO FILME. A MICRODUREZA VICKER APRESENTOU VALORES MÉDIOS SUPERIORES PARA AS AMOSTRAS COM O FILME DE TIN (1050 HV) COMPARADAS ÀS AMOSTRAS SEM O REVESTIMENTO (250 HV). PELA DIFRAÇÃO DE RAIOS X E REFINAMENTO POR RIETVELD VERIFICOU-SE A PRESENÇA DE FASES CONTAMINANTES NO REVESTIMENTO ALÉM DO FILME DE TIN. A REFLEXÃO DE BAIXO ÂNGULO INDICOU A ESPESSURA DO REVESTIMENTO DE 576 NM.

 

THE SEARCH FOR SPECIFIC PROPERTIES IN PARTS AND TOOLS OF GREAT MECHANICAL EFFORTS FOR THE MOST DIVERSE APPLICATIONS HAS GENERATED ADVANCES IN THE TECHNIQUES OF DEPOSITION OF MATERIALS IN FILMS TO INCREASE THE TOOL'S LIFETIME AND ITS MECHANICAL PROPERTIES ON THE SURFACE. IN THIS WAY, INNUMERABLE PROCESSES WERE CREATED AND SEVERAL TECHNIQUES THAT AIM AT THE CHARACTERIZATION OF THE WORK SURFACES ARE USED FOR THE EVALUATION OF THE COATINGS. THE OBJECTIVE OF THE WORK CONSISTED IN THE STRUCTURAL CHARACTERIZATION AND EVALUATION OF THE SURFACE OF SAMPLES OF AN AISI 1045 STEEL TOOL WITH A CLEAN SURFACE IN AN ULTRASONIC BATH, BLASTED WITH GLASS AND NITRIDED SPHERES, WITH DEPOSITION OF TIN FILM BY MAGNETRON SPUTTERING. THE SURFACE ROUGHNESS WAS ALSO INVESTIGATED AND IT WAS OBSERVED THAT THERE WAS A DECREASE AFTER THE PROCESSES OF NITRIDING AND DEPOSITION OF THE FILM. THE VICKER MICROHARDNESS SHOWED HIGHER AVERAGE VALUES FOR THE SAMPLES WITH THE TIN FILM (1050 HV) COMPARED TO THE SAMPLES WITHOUT THE COATING (250 HV). BY X-RAY DIFFRACTION AND RIETVELD REFINEMENT, THE PRESENCE OF CONTAMINATING PHASES IN THE COATING WAS VERIFIED IN ADDITION TO THE TIN FILM. THE LOW ANGLE REFLECTION INDICATED THE COATING THICKNESS OF 576 NM.

Palavras-chave

Magnetron Sputtering; Difração de Raios – X; Filme de TiN; Ferramenta de Soldagem

Magnetron Sputtering; X-Ray Diffraction; TiN Film; Welding Tool