AVALIAÇÃO MECÂNICA DE TRAÇÃO DE COMPÓSITO POLIMÉRICO REFORÇADO COM FIBRAS SISAL DE 15MM DE COMPRIMENTO

MECHANICAL EVALUATION OF TENSION OF POLYMERIC COMPOSITE REINFORCED WITH 15MM LENGHT SISAL FIBERS

Autoria

Ferreira, Paulo Anderson Aranha; Ribeiro, Maurício Maia; Nascimento, Damares da Cruz Barbosa; Matos, Taiana de Sousa; Monteiro, Sérgio Neves; Silva, Alisson Clay Rios da; Candido, Verônica Scarpini

DOI

10.5151/2594-5327-34978

Downloads

Baixar Artigo 7 Downloads

Resumo

A ALTA DEMANDA DE RECURSOS E ENERGIA PARA A PRODUÇÃO DE FIBRAS SINTÉTICAS APLICADAS NA FABRICAÇÃO DE MATERIAIS COMPÓSITOS, CORROBORAM UM PROCESSO NOCIVO AO CENÁRIO AMBIENTAL DE HOJE. O USO DE FIBRAS VEGETAIS VÊM SENDO OBJETO DE ESTUDO PARA SUBSTITUIR AS FIBRAS SINTÉTICAS, EM RAZÃO DO SEU CARÁTER SUSTENTÁVEL E MECANICAMENTE SIMILAR ÀS FIBRAS CONVENCIONAIS. A FIBRA DE SISAL (AGAVE SISALANA), POSSUI PROPRIEDADES MECÂNICAS MODERADAS, BOA TRABALHABILIDADE E FÁCIL CULTIVO. NO PRESENTE TRABALHO, FOI AVALIADO OS ASPECTOS MECÂNICOS DE RESISTÊNCIA A TRAÇÃO E ANÁLISE DA FRATURA DO COMPÓSITO POLIMÉRICO REFORÇADO COM AS FIBRAS CURTAS DE SISAL, SEPARADOS EM QUATRO FRAÇÕES MÁSSICAS DE FIBRA, 25%, 50%, 75% E 100%. FORAM UTILIZADOS NESSE ESTUDO, A RESINA POLIÉSTER INSTAURADA PRÉ-ACELERADA, O AGENTE DE CURA E FIBRAS DE SISAL CORTADAS MANUALMENTE NO COMPRIMENTO DE 15 MM. A CONFECÇÃO DOS COMPÓSITOS FOI FEITA EM MOLDES DE SILICONE DE CORPO DE PROVA DE ENSAIO DE TRAÇÃO. APÓS O PROCESSO DE CURA, OS CORPOS DE PROVA FORAM SUBMETIDOS AO ENSAIO DE TRAÇÃO, E LOGO APÓS, ANALISADOS A FRATURA NO MICROSCÓPIO ELETRÔNICO DE VARREDURA (MEV). FORAM CONSTATADOS, ATRAVÉS DA AVALIAÇÃO, QUE A PROPORÇÃO DE FIBRA DE 25% POSSUI A MAIOR RESISTÊNCIA A TRAÇÃO, COMPARADOS AS OUTRAS FRAÇÕES. JÁ A ANÁLISE FRACTOGRÁFICA, REVELOU UMA ADESÃO INTERFACIAL FRACA ENTRE A FIBRA E A MATRIZ.

 

THE HIGH DEMAND FOR RESOURCES AND ENERGY FOR THE PRODUCTION OF SYNTHETIC FIBERS APPLIED IN THE MANUFACTURE OF COMPOSITE MATERIALS, CORROBORATES A PROCESS HARMFUL TO TODAY'S ENVIRONMENTAL SCENARIO. THE USE OF PLANT FIBERS HAS BEEN THE OBJECT OF STUDY TO REPLACE SYNTHETIC FIBERS, DUE TO THEIR SUSTAINABLE CHARACTER AND MECHANICALLY SIMILAR TO CONVENTIONAL FIBERS. SISAL FIBER (AGAVE SISALANA) HAS MODERATE MECHANICAL PROPERTIES, GOOD WORKABILITY AND EASY CULTIVATION. IN THE PRESENT WORK, THE MECHANICAL ASPECTS OF TENSILE STRENGTH AND FRACTURE ANALYSIS OF THE POLYMER COMPOSITE REINFORCED WITH SHORT SISAL FIBERS WERE EVALUATED, SEPARATED INTO FOUR FIBER MASS FRACTIONS, 25%, 50%, 75% AND 100%. IN THIS STUDY, PRE-ACCELERATED INSTALLED POLYESTER RESIN, THE CURING AGENT AND MANUALLY CUT SISAL FIBERS TO A LENGTH OF 15 MM WERE USED. THE MAKING OF THE COMPOSITES WERE MADE IN SILICONE MOLDS OF TEST SPECIMENS IN A TENSILE TEST. AFTER THE CURING PROCESS, THE SPECIMENS WERE SUBMITTED TO THE TENSILE TEST, AND SOON AFTER, THE FRACTURE WAS ANALYZED IN THE SCANNING ELECTRON MICROSCOPE (SEM). IT WAS FOUND, THROUGH THE EVALUATION, THAT THE PROPORTION OF FIBER OF 25% HAS THE HIGHEST TENSILE STRENGTH, COMPARED TO THE OTHER FRACTIONS. THE FRACTOGRAPHIC ANALYSIS, ON THE OTHER HAND, REVEALED A WEAK INTERFACIAL ADHESION BETWEEN THE FIBER AND THE MATRIX.

Palavras-chave

fibras vegetais; compósitos; tração.

vegetables fibers; composites; tensile.