AVALIAÇÃO MECÂNICA DOS COMPÓSITOS REFORÇADOS POR FIBRAS DE GUARUMÃ FOCADA EM APLICAÇÃO BALÍSTICA

MECHANICAL EVALUATION OF COMPOSITES REINFORCED BY GUARUMAN FIBERS FOCUSED ON BALLISTIC APPLICATION

Autoria

Reis, Raphael Henrique Morais

DOI

10.5151/2594-5327-34391

Downloads

Baixar Artigo 8 Downloads

Resumo

SISTEMAS DE BLINDAGEM MULTICAMADA (SBM) SÃO COMPOSTOS POR PATILHAS CERÂMICAS NA CAMADA FRONTAL, COMPÓSITOS NA CAMADA INTERMEDIÁRIA E TECIDOS SINTÉTICOS COMO A ARAMIDA EM SUA CAMADA FINAL. OS MATÉRIAS UTILIZADOS NA CAMADA INTERMEDIÁRIA DEVEM POSSUI PROPRIEDADES ESPECÍFICAS FAVORÁVEIS A SEU USO EM BLINDAGENS, TANTO EM COMPORTAMENTO DINÂMICO QUANTO SEMI ESTÁTICO. DESDE MODO, COMPÓSITOS REFORÇADOS COM FIBRAS NATURAIS LIGNOCELULOSICAS (FNL), CADA VEZ MAIS, PROVAM POSSUIR PROPRIEDADES VANTAJOSAS EM TAIS APLICAÇÕES DE PROTEÇÃO CORPORAL. RECENTEMENTE, A FIBRA AMAZÔNICA DE GUARUMÃ CONSTATOU-SE SENDO UMA DAS FNLS COM MENOR DENSIDADE. PORTANTO, O PRESENTE TRABALHO DEDICOU-SE A AVALIAR AS PROPRIEDADES MECÂNICAS DO COMPÓSITO EPÓXI-GUARUMÃ ATRAVÉS DOS ENSAIOS DE TRAÇÃO E IMPACTO IZOD SOBRE AS FRAÇÕES VOLUMÉTRICAS DE 10, 20 E 30% DE FIBRA. OS RESULTADOS COMPROVARAM ESTATISTICAMENTE QUE A FRAÇÃO VOLUMÉTRICA DE FIBRA ESTÁ DIRETAMENTE RELACIONADA A SUA PROPRIEDADES SENDO OS COMPÓSITOS REFORÇADOS COM 30% OS MAIS INDICADOS AS APLICAÇÕES EM SBM.

 

MULTILAYER ARMOUR SYSTEMS (MAS) ARE COMPOSED OF CERAMIC TABS ON THE FRONT LAYER, COMPOSITES ON THE MIDDLE LAYER AND SYNTHETIC FABRICS LIKE ARAMID IN ITS FINAL LAYER. THE MATERIALS USED IN THE INTERMEDIATE LAYER MUST HAVE SPECIFIC PROPERTIES FAVORABLE TO THEIR USE IN SHIELDING, BOTH IN DYNAMIC AND SEMI-STATIC BEHAVIOR. THEREFORE, COMPOSITES REINFORCED WITH NATURAL LIGNOCELLULOSIC FIBERS (FNL), INCREASINGLY, PROVE TO HAVE ADVANTAGEOUS PROPERTIES IN SUCH BODY PROTECTION APPLICATIONS. RECENTLY, THE GUARUMã AMAZON FIBER WAS FOUND TO BE ONE OF THE FNLS WITH THE LOWEST DENSITY. THEREFORE, THE PRESENT WORK WAS DEDICATED TO EVALUATE THE MECHANICAL PROPERTIES OF THE EPOXY-GUARUMã COMPOSITE THROUGH THE IZOD TENSILE AND IMPACT TESTS ON THE VOLUMETRIC FRACTIONS OF 10, 20 AND 30% OF FIBER. THE RESULTS PROVED STATISTICALLY THAT THE VOLUMETRIC FRACTION OF FIBER IS DIRECTLY RELATED TO ITS PROPERTIES, WITH COMPOSITES REINFORCED WITH 30% THE MOST SUITABLE APPLICATIONS IN MAS.

Palavras-chave

Blindagem balística, Avaliação Mecânica, Compósitos Reforçados com Fibras Naturais

Ballistic Shielding, Mechanical Evaluation, Composites Reinforced with Natural Fibers.