AVALIAÇÃO MECÂNICA E FRACTOGRÁFICA DE COMPÓSITOS DE FIBRAS DE SISAL E PÓ DE QUARUBA

MECHANICAL AND FRACTOGRAPHIC EVALUATION OF COMPOSITES OF SISAL FIBERS AND QUARUBA POWD

Autoria

Nascimento, Damares da Cruz Barbosa; Ribeiro, Maurício Maia; Ferreira, Paulo Anderson Aranha; Monteiro, Sérgio Neves; Silva, Alisson Clay Rios da; Candido, Verônica Scarpini; Matos, Taiana de Sousa

DOI

10.5151/2594-5327-34995

Downloads

Baixar Artigo 9 Downloads

Resumo

OS MATERIAIS COMPÓSITOS TÊM ADQUIRIDO DESTAQUE DEVIDO ASSOCIAR EXCELENTES CARACTERÍSTICAS TECNOLÓGICAS E AMBIENTAIS. NESSE SENTIDO, DESTACA-SE O DESENVOLVIMENTO DE COMPÓSITOS DE MATRIZ POLIMÉRICA, PODENDO DESTACAR A APLICAÇÃO DE RESÍDUOS EM COMPÓSITOS. O DESENVOLVIMENTO DE COMPÓSITOS SURGE COMO ALTERNATIVA DE DESTINAÇÃO FINAL AMBIENTALMENTE CORRETA TAMBÉM DE DIFERENTES RESÍDUOS. ASSIM O OBJETIVO DESSE TRABALHO CONSISTE NA PRODUÇÃO DE MATERIAIS COMPÓSITOS DE MATRIZ POLIÉSTER INSATURADA, COM AGENTE DE CURA PERÓXIDO DE METIL-ETIL-CETONA (MEK), NA PRESENÇA DE RESÍDUO DE MADEIRA DE QUARUBA E FIBRA DE SISAL CORTADA MANUALMENTE. O RESÍDUO DE MADEIRA E A FIBRA FORAM DISPOSTOS ALEATORIAMENTE NA MATRIZ POLIÉSTER E O PROCESSO DE FABRICAÇÃO FOI POR MOLDAGEM MANUAL E SEM PRESSÃO. A PROPRIEDADE MECÂNICA AVALIADA FOI ATRAVÉS DE ENSAIO DE TRAÇÃO DE ACORDO COM NORMA ASTM D 638:2010. APÓS O ENSAIO DE TRAÇÃO, FOI REALIZADA MICROSCOPIA ELETRÔNICA DE VARREDURA (MEV) VISANDO A ANÁLISE DA SUPERFÍCIE DE FRATURA DE MODO A ESTABELECER RELAÇÃO ENTRE OS ASPECTOS DA FRATURA COM AS PROPRIEDADES MECÂNICAS. OS RESULTADOS DEMONSTRARAM QUE A METODOLOGIA APLICADA COMO SATISFATÓRIA PRINCIPALMENTE EM FUNÇÃO DE REVELAR DADOS INOVADORES SOBRE ESTE COMPÓSITO A PRESENÇA DE FIBRAS DE SISAL É ACOMPANHADA DE VAZIOS DEVIDO PRESENÇA DE PULL OUT.

 

COMPOSITE MATERIALS HAVE GAINED PROMINENCE DUE TO THEIR ASSOCIATION WITH EXCELLENT TECHNOLOGICAL AND ENVIRONMENTAL CHARACTERISTICS. IN THIS SENSE, THE DEVELOPMENT OF POLYMERIC MATRIX COMPOSITES STANDS OUT, HIGHLIGHTING THE APPLICATION OF WASTE IN COMPOSITES. THE DEVELOPMENT OF COMPOSITES EMERGES AS AN ALTERNATIVE FOR THE ENVIRONMENTALLY CORRECT FINAL DISPOSAL OF DIFFERENT WASTES AS WELL. THUS, THE OBJECTIVE OF THIS WORK IS THE PRODUCTION OF COMPOSITE MATERIALS WITH AN UNSATURATED POLYESTER MATRIX, WITH A METHYL ETHYL KETONE PEROXIDE (MEK) CURING AGENT, IN THE PRESENCE OF QUARUBA WOOD RESIDUE AND MANUALLY CUT SISAL FIBER. THE WOOD RESIDUE AND FIBER WERE RANDOMLY DISPOSED IN THE POLYESTER MATRIX AND THE MANUFACTURING PROCESS WAS BY MANUAL MOLDING AND WITHOUT PRESSURE. THE MECHANICAL PROPERTY EVALUATED WAS THROUGH A TENSILE TEST IN ACCORDANCE WITH ASTM D 638:2010 STANDARD. AFTER THE TENSILE TEST, SCANNING ELECTRON MICROSCOPY (SEM) WAS PERFORMED AIMING TO ANALYZE THE FRACTURE SURFACE IN ORDER TO ESTABLISH A RELATIONSHIP BETWEEN THE ASPECTS OF THE FRACTURE WITH THE MECHANICAL PROPERTIES. THE RESULTS SHOWED THAT THE METHODOLOGY APPLIED AS SATISFACTORY, MAINLY DUE TO REVEALING INNOVATIVE DATA ABOUT THIS COMPOSITE, THE PRESENCE OF SISAL FIBERS IS ACCOMPANIED BY VOIDS DUE TO THE PRESENCE OF PULL OUT.

Palavras-chave

Resíduo; Microscopia; Tração; Sustentabilidade

Residue; Microscopy; Traction; Sustainability