AVALIAÇÃO MICROESTRUTURAL DAS LIGAS DE ALTA ENTROPIA AL(CO)CRFENITI SUBMETIDAS À TRATAMENTO TÉRMICO DE HOMOGENEIZAÇÃO

MICROSTRUCTURAL EVALUATION OF HIGH ENTROPY ALLOYS AL(CO)CRFENITI SUBMITTED TO THE HOMOGENEIZATION HEAT TREATMENT

Autoria

Krepke, Wagner Antonio Loreiro Lima; Carvalho, Iana Costa; Esteves, Paulo Davi Borges; Teixeira, Rodolfo da Silva; Sousa, Talita Gama de; Garcia, Julianna Magalhães; Paula, Andersan dos Santos

DOI

10.5151/2594-5327-34690

Downloads

Baixar Artigo 29 Downloads

Resumo

AS LIGAS DE ALTA ENTROPIA (LAE) EM ESTUDO FORAM ALCOCRFENITI E ALCRFENITI FORAM SUBMETIDAS A UM TRATAMENTO TÉRMICO A 950 ºC POR 24 HORAS, COM RESFRIAMENTO EM ÁGUA, PARA OBSERVAR AS MODIFICAÇÕES MICROESTRUTURAIS RESULTANTES E CRITICAR O AVANÇO NA HOMOGENEIZAÇÃO DA ESTRUTURA INICIALMENTE FUNDIDA, E ENTÃO, A AVALIAR A EVOLUÇÃO MICROESTRUTURAL. ESTAS ANÁLISES FORAM FEITAS COM AUXÍLIO DA MICROSCOPIA ÓPTICA (MO) E MICROSCOPIA ELETRÔNICA DE VARREDURA (MEV) (EM CONJUNTO COM OS DETECTORES DE ELÉTRONS SECUNDÁRIOS (SE) E RETROESPALHADOS (BSE)). AS LAE MOSTRARAM ASPECTO MICROESTRUTURAL DENDRÍTICO COM MORFOLOGIA DE FORMATO EM FLORES EM AMBAS AS LIGAS, A FORMAÇÃO DE GRÃOS DENDRÍTICOS MAIS REFINADOS DEU-SE NA LIGA SEM ADIÇÃO DE CO. A MICROESTRUTURA RESULTANTE DO TRATAMENTO TÉRMICO ADOTADO RESULTOU EM TRINCAS PARA AMBAS AS LIGAS, MAIS INTENSAS NA LIGA COM CO, E NÃO PROMOVEU MODIFICAÇÕES MICROESTRUTURAIS SIGNIFICATIVA, OU SEJA, MANTEVE-SE A MORFOLOGIA FUNDIDA, PORÉM NA LIGA COM CO APARENTA TER OCORRIDO UM CRESCIMENTO NO TAMANHO DE GRÃO DENDRÍTICO E O DECRÉSCIMO NO ESPAÇAMENTO INTERDENDRÍTICO, OBSERVA-SE O COMPORTAMENTO INVERSO NA LIGA SEM CO - DESTACANDO TAMBÉM NESTA UM ASPECTO MAIS MARCANTE DAS RAMIFICAÇÕES DOS BRAÇOS DENDRÍTICOS.

 

THE HIGH ENTROPY ALLOYS (HEA) UNDER STUDY ALCOCRFENITI AND ALCRFENITI SUBJECTED TO A HEAT TREATMENT AT 950 ºC FOR 24 HOURS, WITH COOLING IN WATER, TO OBSERVE HOW MICROSTRUCTURAL AND TO CRITICIZE THE HOMOGENIZATION OF WERE SUBJECTED TO THE FORMATION OF FUNDS, AND THEN, AN ASSESSMENT OF MICROSTRUCTURAL EVOLUTION. THESE ANALYZES WERE MADE WITH THE AID OF OPTICAL MICROSCOPY (OM) AND SCANNING ELECTRON MICROSCOPY (SEM) (TOGETHER WITH SECONDARY ELECTRON DETECTORS (SE) AND BACKSCATTERED (BSE)). THE HEAS SHOWN DENDRITIC MICROSTRUCTURAL ASPECT WITH FLOWER-SHAPED MORPHOLOGY IN BOTH ALLOYS, THE FORMATION OF MORE REFINED DENDRITIC GRAINS IN THE ALLOY WITHOUT CO ADDITION. THE MICROSTRUCTURE RESULTING FROM THE HEAT TREATMENT ADOPTED RESULTED IN CRACKS FOR BOTH ALLOYS, MORE INTENSE IN THE ALLOY WITH CO, AND DID NOT PROMOTE SIGNIFICANT MICROSTRUCTURAL MODIFICATIONS, THAT IS, THE CASTING MORPHOLOGY WAS MAINTAINED, HOWEVER IN THE ALLOY WITH CO IT APPEARS THAT THERE WAS AN INCREASE IN THE DENDRITIC GRAIN SIZE AND A DECREASE IN THE INTERDENDRITIC SPACING, NOTES THE INVERSE BEHAVIOR IN THE ALLOY WITHOUT CO - ALSO EMPHASIZING IN THIS ONE A MORE STRIKING ASPECT OF THE RAMIFICATIONS OF THE DENDRITIC ARMS.

Palavras-chave

Ligas de alta entropia; AlCoCrFeNiTi; AlCrFeNiTi; Tratamento Térmico; Microestrutura.

High Entropy Alloys; AlCoCrFeNiTi; AlCrFeNiTi; Heat treatment; Microstructure.