Título

AVALIAÇÃO MICROESTRUTURAL, MECÂNICA E ELÉTRICA DO AÇO AISI 310 SUBMETIDO A LAMINAÇÃO A FRIO E SOLUBILIZAÇÃO

MICROSTRUCTURAL, MECHANICAL AND ELECTRICAL EVALUATION OF AISI 310 STEEL SUBMITTED TO COLD ROLLING AND SOLUBILIZATION

Autoria

Garcia, Julianna Magalhães; Carvalho, Iana Costa; Pires, Wellington Mattos; Casanova, Andréy de Moraes Barcelos; Monteiro, Ana Carolina Accioly; Brandao, Luiz Paulo

DOI

10.5151/2594-5327-34658

Downloads

Baixar Artigo 5 Downloads

Resumo

NESSE ESTUDO, FOI REALIZADA A AVALIAÇÃO MICROESTRUTURAL DO AÇO AISI 310 LAMINADO A FRIO E RECOZIDO A 1050 °C POR 90 MIN. A EVOLUÇÃO MICROESTRUTURAL FOI ESTUDADA ATRAVÉS DE ENSAIOS DE DIFRAÇÃO DE RAIOS X, MICROSCOPIA ELETRÔNICA DE VARREDURA, MICRODUREZA VICKERS E MEDIDAS DE CONDUTIVIDADE DO MATERIAL. FOI VERIFICADO QUE O MATERIAL LAMINADO A FRIO APRESENTAVA PRECIPITAÇÃO DE CARBONETOS E MACLAS, SENDO QUE O PROCESSO DE RECOZIMENTO CONSEGUIU SOLUBILIZAR MUITOS PRECIPITADOS, AUMENTANDO O TAMANHO DE GRÃO EM CERCA DE 113%. OS DIFRATOGRAMAS NÃO POSSUÍRAM SENSIBILIDADE PARA DISTINGUIR OUTRA FASE, QUE NÃO SEJA A MATRIZ AUSTENÍTICA. SENDO QUE A MICRODUREZA DEMONSTROU UMA TENDÊNCIA DE DECRESCIMENTO COM O RECOZIMENTO, O QUE CORROBORA COM A IDEIA DE AUMENTO DO TAMANHO DE GRÃO E DIMINUIÇÃO DOS PRECIPITADOS. AS MEDIDAS DE CONDUTIVIDADE POR SUA VEZ, CONSEGUIRAM TER A SENSIBILIDADE PARA DETECTAR TANTO O TAMANHO DE GRÃO QUANTO A PRECIPITAÇÃO COM AFERIÇÕES DIRETAS IN LOCO, AS QUAIS NÃO FORAM DETECTÁVEIS NO ENSAIO DE DRX. MOSTRANDO UMA POTENCIALIDADE DA TÉCNICA DE CONDUTIVIDADE COMO FORMA DE AVALIÇÃO MICROESTRUTURAL DO MATERIAL.

 

IN THIS STUDY, THE MICROSTRUCTURAL EVALUATION OF AISI 310 STEEL AFTER COLD-ROLLING AND ANNEALING AT 1050 ° C FOR 90 MIN WAS CARRIED OUT. THE MICROSTRUCTURAL EVOLUTION WAS INVESTIGATED THROUGH X-RAY DIFFRACTION TESTS, SCANNING ELECTRON MICROSCOPY, VICKERS MICROHARDNESS AND ELECTRICAL CONDUCTIVITY MEASUREMENTS. IT WAS VERIFIED THAT THE COLD ROLLED MATERIAL HAD PRECIPITATION OF CARBIDES AND TWINS. WHILE THE ANNEALING PROCESS DECREASED THE OCCURRENCE OF PRECIPITATES AND ALSO INCREASED THE GRAIN SIZE BY ABOUT 113%. DIFFRACTOGRAMS DID NOT HAD THE SENSIBILITY TO DISTINGUISH ANOTHER PHASE, OTHER THAN THE AUSTENITIC MATRIX. MICROHARDNESS SHOWED A DECREASING TREND WITH ANNEALING, WHICH CORROBORATES THE OBSERVATION OF INCREASING THE GRAIN SIZE AND DECREASING THE PRECIPITATES. THE ELECTRICAL CONDUCTIVITY MEASUREMENTS, IN TURN, MANAGED TO HAVE THE SENSITIVITY TO DETECT BOTH GRAIN SIZE CHANGES AND PRECIPITATION WITH DIRECT MEASUREMENTS IN LOCO, WHICH WERE NOT DETECTABLE IN THE XRD TESTS. SHOWING A POTENTIALITY OF THE CONDUCTIVITY TECHNIQUE AS A WAY TO EVALUATE THE MICROSTRUCTURE OF THE MATERIAL.

Palavras-chave

Laminação a frio; Solubilização; DRX; Condutividade.

Cold-rolling; Solubilization; XRD; Conductivity