AZULEJO PRODUZIDO COM LODO DE ESTAÇÃO DE TRATAMENTO DE ESGOTO (ETE) MUNICIPAL

WALL TILE PRODUCED WITH A MUNICIPAL SEWAGE TREATMENT PLANT (STP) SLUDGE

Autoria

AREIAS, ISABELA OLIVEIRA RANGEL; MACIEL, FELIPE SARDINHA; HOLANDA, JOSÉ NILSON FRANÇA DE

AREIAS, ISABELA OLIVEIRA RANGEL

Eu sou esse autor

MACIEL, FELIPE SARDINHA

Eu sou esse autor

HOLANDA, JOSÉ NILSON FRANÇA DE

Eu sou esse autor

DOI

10.5151/2594-5327-41455

Downloads

Resumo

ESTE TRABALHO TEVE COMO OBJETIVO AVALIAR O USO DE LODO DE ESTAçãO DE TRATAMENTO DE ESGOTO (ETE) COMO MATéRIA-PRIMA ALTERNATIVA NA PRODUçãO DE AZULEJO. AS MATéRIAS-PRIMAS UTILIZADAS FORAM ARGILA VERMELHA, QUARTZO, CALCáRIO CALCíTICO E LODO DE ETE. QUATRO FORMULAçõES FORAM PREPARADAS: 0, 5, 10 E 15 % EM MASSA DE LODO DE ETE EM SUBSTITUIçãO AO MATERIAL CALCáRIO. A ANáLISE QUíMICA ELEMENTAR DAS MATéRIAS-PRIMAS FOI DETERMINADA PELA TéCNICA DE FLUORESCêNCIA DE RAIOS X. A PERDA AO FOGO FOI TAMBéM DETERMINADA. AS PEçAS FORAM PRENSADAS E QUEIMADAS A 1160 ºC USANDO UM CICLO DE QUEIMA RáPIDA. AS PEçAS DE AZULEJO FORAM TESTADAS PARA DETERMINAR SUAS PROPRIEDADES TECNOLóGICAS (RETRAçãO LINEAR, ABSORçãO DE áGUA E TENSãO DE RUPTURA à FLEXãO). OS RESULTADOS EXPERIMENTAIS INDICARAM QUE AS PROPRIEDADES TECNOLóGICAS FORAM INFLUENCIADAS PELA INCORPORAçãO DO LODO DE ETE. OS RESULTADOS TAMBéM MOSTRARAM QUE AS PEçAS DE AZULEJO APRESENTARAM VALORES DE ABSORçãO DE áGUA NA FAIXA DE 18,66-19,65 %. ASSIM, O LODO DE ETE PODE SUBSTITUIR INTEGRALMENTE O MATERIAL CALCáRIO NATURAL (ATé 15 % EM MASSA) NA PRODUçãO DE PLACA CERâMICA PARA REVESTIMENTO DO TIPO AZULEJO (REVESTIMENTO POROSO - GRUPO BIII - ABSORçãO DE ÁGUA > 10 %; NORMA ABNT NBR ISO 13006:2020). POR FIM, O USO DE LODO DE ETE NA PRODUçãO DE AZULEJOS PODE SER UMA SOLUçãO TéCNICA PARA A ELIMINAçãO DESTE RESíDUO SóLIDO POLUENTE, ALéM DE CONTRIBUIR PARA O DESENVOLVIMENTO SUSTENTáVEL.

THIS WORK AIMED TO EVALUATE THE USE OF STP SLUDGE AS AN ALTERNATIVE RAW MATERIAL IN TILE PRODUCTION. THE RAW MATERIALS USED WERE RED CLAY, QUARTZ, CALCITIC CALCAREOUS AND STP SLUDGE. FOUR FORMULATIONS WERE PREPARED: 0, 5, 10 AND 15% BY WEIGHT OF STP SLUDGE REPLACING CALCAREOUS MATERIAL. THE ELEMENTARY CHEMICAL ANALYSIS OF THE RAW MATERIALS WAS DETERMINED BY THE X-RAY FLUORESCENCE TECHNIQUE. THE LOSS ON IGNITION (LOI) WAS ALSO DETERMINED. THE PIECES WERE PRESSED AND FIRED AT 1160 ºC IN A RAPID FIRING CYCLE. THE PIECES OF RED WALL TILE WERE TESTED TO DETERMINE THEIR TECHNOLOGICAL PROPERTIES (LINEAR SHRINKAGE, WATER ABSORPTION, AND FLEXURAL BREAKING STRENGTH). THE EXPERIMENTAL RESULTS INDICATED THAT THE TECHNOLOGICAL PROPERTIES WERE INFLUENCED BY THE INCORPORATION OF STP SLUDGE. THE RESULTS ALSO SHOWED THAT THE RED WALL TILE PIECES PRESENTED WATER ABSORPTION VALUES IN THE RANGE OF 18.66-19.65%. THUS, STP SLUDGE CAN FULLY REPLACE NATURAL CALCAREOUS MATERIAL (UP TO 15% WT.%) IN THE PRODUCTION OF CERAMIC SLABS FOR RED WALL TILE-TYPE COVERINGS (POROUS COATING - BIII GROUP - WATER ABSORPTION > 10%; ABNT NBR ISO 13006: 2020 STANDARD). FINALLY, THE USE OF STP SLUDGE ON THE PRODUCTION OF RED WALL TILES COULD BE A TECHNICAL SOLUTION FOR ELIMINATING THESE POLLUTING SOLID WASTE, IN ADDITION TO CONTRIBUTING TO SUSTAINABLE DEVELOPMENT.