Título

CARACTERIZAÇÃO DE UM AÇO LEAN DUPLEX POR TÉCNICAS ANALÍTICAS

LEAN DUPLEX STEEL CHARACTERIZATION BY ANALYTICAL METHODS

DOI

10.5151/1516-392X-26254

Downloads

Baixar Artigo 651 Downloads

Resumo

Neste trabalho, amostras de aço Lean Duplex UNS S32304 foram submetidas à temperatura de 800°C em um forno acoplado a um difratômetro de raios-x durante intervalos de tempo de 30, 60 e 90 minutos. Com o objetivo de analisar em tempo real a transformação das fases constituintes, foram realizadas várias varreduras insitu durante os diferentes tempos de permanência em 800°C deste material. Assim, observou-se a formação da fase sigma neste aço, tanto nos contornos de grão da ferrita como nas interfaces ferrita/austenita. Os valores de fase sigma obtidos para cada tempo de exposição foram calculados através do método de Rietveld sobre cada difratograma obtido e variaram de 11% a 17%. Notou-se que a fase sigma exibiu crescimento contínuo até 60 minutos e variação após este período. Todavia, observou-se que a formação de fase sigma a 800°C ocorre de forma significativa neste material após 30 minutos de aquecimento, o que pode comprometer as propriedades do mesmo.

 

In this work, samples from a Lean Duplex Steel UNS S32304 were subjected to a temperature of 800°C for different intervals of time, being 30min, 60min and 90 min. All samples were allocated inside a small high temperature furnace attached to an xray diffractor. The goal of the work was to analyze the phase transformations occurring in those samples in real time. Formation of sigma phase was observed both in the ferrite grain boundaries as in the ferrite/austenite interface. The amount of sigma phase formed was measured by quantitative phase analysis using the Rietveld method and result values ranged from 11% to 17 % in volume. It was also noticed that the sigma phase exhibit a continuous growth up to 60 minutes, become stable for a few minutes to then grow again. In any case, it was observed that sigma phase formed significantly in the material after 30 minutes soaking, which can lead to a decrease in the material properties.

Palavras-chave

Aço lean duplex, Difração de raios-x in-situ, Microestrutura, Fase sigma

Lean duplex steel, In-situ x-ray diffraction, Microstructure, Sigma phase