CARACTERIZAÇÃO METALOGRÁFICA E MECÂNICA DE TUBO DE AÇO API 5L X70 SOLDADO COM MULTIPASSES PELO PROCESSO SMAW EM CONDIÇÕES ESPECÍFICAS DE ENERGIA

METALOGRAPHIC AND MECHANICAL CARACTERIZATION OF PIPE LINE API 5L X70 WELDED WITH MULTIPASS SMAW WELDING PROCESS IN SPECIFIC CONDITIONS OF HEAT INPUT

Autoria

Chilque, Angel Rafael Arce; Souzar, Camila Rita de; Martins, Wanderson Antônio

DOI

10.5151/1516-392X-26467

Downloads

Baixar Artigo 649 Downloads

Resumo

O presente trabalho trata do estudo micrográfico e mecânico de junta soldada a multipassesde tubo de aço API 5L X70, pelo processo manual com eletrodorevestido (SMAW) para os passes de raiz, enchimento e acabamento na posição vertical 3G. Em acordo com API 1104, o consumível escolhido foi eletrodo revestido básico E 9018 – M, a fim de atender a parâmetros de soldabilidade e permitir a comparação dos resultados com trabalhos anteriores. Foram realizados ensaios macrográficos e micrográficos qualitativos da junta soldada e do metal de base, bem como a medição da microdureza Vickers (HV) ao longo da junta e medição do tamanho de grão da região de superaquecimento. Ensaios mecânicos de dobramento, tração e impacto também foram realizados. Os resultados dos ensaios Charpy foram correlacionados com a estrutura metalúrgica, tamanho de grão e microconstituintes presentes na junta soldada.

 

This work deals with the micrographic study and mechanical splice welded steel pipe API 5L X70 multipass, the manual process with coated electrodes (SMAW) for root passes, filling and finishing in 3G upright. In accordance with API 1104, the chosen consumable electrode was coated basic E 9018 - M, in order to meet the weldability of parameters and comparison of results with previous work. Macrographics tests were conducted and qualitative micrographs of the weld and the base metal as well as the measurement of Vickers hardness (HV) across the weld, measuring the grain size of the superheat region. Mechanical bending tests, tensile and impact were also conducted. The results of Charpy tests were correlated with the metallurgical structure, grain size and microconstituents present in the welded joint.

Palavras-chave

Aço API 5L X70, Gasodutos, Resistência ao impacto, Metalurgia da soldagem

API 5 L X70 steel, Pipelines, Impact test, Welding metallurgy