Título

CARACTERIZAÇÃO DA TEXTURA CRISTALOGRÁFICA DO REVESTIMENTO DE FOLHAS DE FLANDRES PRODUZIDOS COM DIFERENTES DENSIDADES DE CORRENTE

CHARACTERIZATION OF THE CRYSTALLOGRAPHIC TEXTURE OF TINPLATES PRODUCED WITH DIFFERENT ELECTRIC CURRENT DENSITIES

Autoria

Oliveira, Alessandro Dias de

Oliveira, Alessandro Dias de

Eu sou esse autor

DOI

10.5151/2594-5327-34915

Downloads

Resumo

FOLHAS DE FLANDRES COM REVESTIMENTO NÃO FUNDIDO (ASPECTO FOSCO) FORAM PRODUZIDAS EM ESCALA LABORATORIAL, NA QUAL FOI UTILIZADO UM ELETRÓLITO INDUSTRIAL A BASE DE ÁCIDO METANOSSULFÔNICO. DIFERENTES DENSIDADES DE CORRENTE ELÉTRICA DE DEPOSIÇÃO (10 A 60 A·DM-2) FORAM UTILIZADAS PARA A OBTENÇÃO DOS CORPOS-DE-PROVA, MANTENDO OS DEMAIS PARÂMETROS DO PROCESSO CONSTANTES. FOI EVIDENCIADO, POR MEIO DA DIFRAÇÃO DE ELÉTRONS RETROESPALHADOS (ELECTRON BACKSCATTERED DIFFRACTION – EBSD) VIA MEV, QUE HOUVE MUDANÇA DA TEXTURA CRISTALOGRÁFICA DO REVESTIMENTO ENTRE AS DENSIDADES 10 E 20 A·DM 2. FOI IDENTIFICADA A PRESENÇA DE UMA TEXTURA PREFERENCIAL ENVOLVENDO AS COMPONENTES (001) E (742) NO REVESTIMENTO ELETRODEPOSITADO SOB A DENSIDADE DE 10 A·DM-2. NAS DENSIDADES DE 20 A 60 A·DM-2 OBSERVOU-SE AS COMPONENTES PREFERENCIAIS (744) E (743). A EVOLUÇÃO DA TEXTURA PREFERENCIAL ENVOLVEU PLANOS QUE POSSUEM VALORES DE DENSIDADE DE EMPACOTAMENTO SEMELHANTES ENTRE SI, OS QUAIS NÃO COMPROMETEM A RESISTÊNCIA À CORROSÃO DO MATERIAL.

THE NON-REFLOW TINPLATES (MATTE ASPECT) WERE PRODUCED IN LABORATORY, IN WHICH AN INDUSTRIAL ELECTROLYTIC BATH WAS USED (METHANE SULFONIC ACID - MSA). DIFFERENT ELECTRIC CURRENT PLATING DENSITIES (10 A 60 A·DM-2) HAVE BEEN USED TO PRODUCE THAT SAMPLE, KEEPING OTHER PROCESS PARAMETERS CONSTANT. THE TEXTURE ANALYSIS SHOWED, BY ELECTRON BACKSCATTERED DIFFRACTION (EBSD) VIA SEM, THAT THERE WAS A CHANGE ON COATING CRYSTALLOGRAPHY TEXTURE BETWEEN DENSITIES 10 AND 20 A·DM-2. THE PRESENCE OF PREFERENTIAL TEXTURE (001) AND (742) HAS BEEN OBSERVED IN ELECTROPLATED COATING PRODUCED UNDER THE DENSITY 10 A·DM 2. IN THE RANGE DENSITIES 20 TO 60 A·DM-2 WERE IDENTIFIED THE COMPONENT (744) AND (743). PREFERENTIAL TEXTURE EVOLUTION INVOLVED PLANES WITH SIMILAR PACKING DENSITY VALUES, WHICH DOES NOT COMPROMISE THE CORROSION RESISTANCE OF THE MATERIAL.

Palavras-chave

Folha de Flandres; Revestimento; Textura; Cristalográfica.

Tinplate; Coating; Texture; Crystallographic