Título

CARACTERIZAÇÃO DO ROLO DA DESEMPENADEIRA DE CHAPAS DE AÇO

CHARACTERIZATION OF STEEL SHEET STRAIGHTENER ROLLER

Autoria

Mudesto, Bruno Fernandes; Rocha, Fernanda Mitke M. L. R. H.; Souza, Juan Carlos Sacramento de; Ximenes, Daniel Alexandre da Costa; Fernandes, Vinícius Santiago

DOI

10.5151/2594-5327-34957

Downloads

Baixar Artigo 12 Downloads

Resumo

ENTENDER AS PROPRIEDADES DO ROLO DA DESEMPENADEIRA DE CHAPAS DE AÇO, É DE SUMA IMPORTÂNCIA PARA O ENTENDIMENTO DO TIPO DE MATERIAL QUE COMPÕE ESTE ITEM, BEM COMO POSSUIR RECURSOS PARA ESPECIFICAR SUA COMPRA EM CASO DE QUEBRA OU NECESSIDADE DE TROCA. A APLICAÇÃO DOS MÉTODOS DE CARACTERIZAÇÃO, ATRAVÉS DAS ANÁLISES LABORATORIAIS, É O QUE EXPRIME AS PROPRIEDADES APRESENTADAS PELO MATERIAL ANALISADO. FOI A PARTIR DAS ANÁLISES LABORATORIAIS QUE FORAM OBTIDAS INFORMAÇÕES DE COMPOSIÇÃO QUÍMICA, MICRODUREZA E IDENTIFICAÇÃO DA MICROESTRUTURA CONSTITUINTE DO ROLO. EM POSSE DOS RESULTADOS OBTIDOS, FORAM REALIZADAS PESQUISAS BIBLIOGRÁFICAS, CONSULTANDO AS NORMAS REGULAMENTADORAS PARA FABRICAÇÃO E ESPECIFICAÇÃO DE AÇOS, A FIM DE IDENTIFICAR SE OS DADOS APRESENTADOS PELO COMPONENTE ESTUDADO SE ENQUADRAVAM DENTRO DE ALGUMA DESSAS ESPECIFICAÇÕES NORMATIZADAS. COMPARANDO OS VALORES OBTIDOS COM OS VALORES APRESENTADOS NA ESPECIFICAÇÃO DO AÇO 51CRV4, FOI POSSÍVEL CONCLUIR QUE TODAS AS CARACTERÍSTICAS APRESENTADAS SE ENQUADRAVAM DENTRO DOS LIMITES ESTABELECIDOS PELAS NORMAS, LEVANDO ASSIM AO ENTENDIMENTO QUE O METAL BASE UTILIZADO PARA A FABRICAÇÃO DO ROLO ESTUDADO PODE SER CARACTERIZADO COMO UM AÇO 51CRV4.

 

REALIZE THE PROPERTIES OF THE STEEL SHEET STRAIGHTENER ROLLER IS OF UTMOST IMPORTANCE TO UNDERSTAND WICH KIND OF MATERIAL THAT MAKES UP THIS ITEM, AS WELL AS HAVING RESOURCES TO SPECIFY ITS PURCHASE IN CASE OF BREAKAGE OR NEED OF REPLACEMENT. THE APPLICATION OF CHARACTERIZATION METHODS, THROUGH LABORATORY ANALYSIS, IS WHAT EXPRESSES THE PROPERTIES PRESENTED BY THE ANALYZED MATERIAL. IT WAS BY LABORATORY ANALYSES THAT INFORMATION ABOUT CHEMICAL COMPOSITION, MICROHARDNESS AND IDENTIFICATION OF THE ROLL'S CONSTITUENT MICROSTRUCTURE WERE OBTAINED. IN POSSESSION OF THE RESULTS OBTAINED, BIBLIOGRAPHIC RESEARCH WAS CARRIED OUT, CONSULTING THE REGULATORY STANDARDS FOR STEEL MANUFACTURING AND SPECIFICATION, IN ORDER TO IDENTIFY WHETHER THE DATA PRESENTED BY THE STUDIED COMPONENT FIT WITHIN ANY OF THESE STANDARDIZED SPECIFICATIONS. COMPARING THE VALUES OBTAINED WITH THE VALUES PRESENTED IN THE 51CRV4 STEEL SPECIFICATION, IT WAS POSSIBLE TO CONCLUDE THAT ALL THE CHARACTERISTICS PRESENTED FIT WITHIN THE LIMITS ESTABLISHED BY THE STANDARDS, THUS LEADING TO THE UNDERSTANDING THAT THE BASE METAL USED TO MANUFACTURE THE ROLL STUDIED CAN BE CHARACTERIZED AS A 51CRV4.

Palavras-chave

Rolo; Caracterização; Análises Laboratoriais; 51CrV4.

Roll; Characterization; Laboratory Analysis; 51CrV4.