CARACTERIZAÇÃO MICROESTRUTURAL DE LIGAS TI-6AL-4V SINTERIZADAS COM LASER

MICROSTRUCTURAL CHARACTERIZATION OF TITANIUM ALLOY TI-6AL-4V PRODUCED BY SELECTIVE LASER SINTERING

Autoria

Rufino, Clarisse da Costa; Mathias, Iasmin Camargo; Monteiro, Ana Carolina Accioly; Elias, Carlos Nelson

DOI

10.5151/2594-5327-34556

Downloads

Baixar Artigo 10 Downloads

Resumo

AS LIGAS DE TITÂNIO POSSUEM CARACTERÍSTICAS QUE AS TORNAM MUITO ATRATIVAS PARA DIVERSAS APLICAÇÕES, COMO ALTA RESISTÊNCIA MECÂNICA, BAIXA DENSIDADE E EXCELENTE RESISTÊNCIA À CORROSÃO. O OBJETIVO DESTE ESTUDO É CARACTERIZAR A LIGA TI-6AL-4V PRODUZIDA POR PROCESSO DE SINTERIZAÇÃO SELETIVA A LASER (SLS), ANALISAR A MICROESTRUTURA E AVALIAR SUAS PROPRIEDADES MECÂNICAS. PARA ATINGIR TAIS OBJETIVOS, FORAM FEITAS ANÁLISES DAS AMOSTRAS COM MICROSCÓPIO ÓPTICO (MO), MICROSCÓPIO ELETRÔNICO DE VARREDURA (MEV), ENSAIO DE MICRODUREZA E DIFRAÇÃO DE RAIOS-X (DRX). OS RESULTADOS OBTIDOS POR MO E MEV MOSTRARAM UMA MORFOLOGIA CARACTERÍSTICA DA FASE MARTENSÍTICA ACICULAR, E A ANÁLISE COM DRX CONFIRMOU A PRESENÇA COMPLETA DE FASE ΑLFA’. A TRANSFORMAÇÃO MARTENSÍTICA ΒETA → ΑLFA’ FOI COMPLETA, E NÃO HOUVE A FORMAÇÃO DA FASE ΑLFA PREVISTA NO EQUILÍBRIO. CONCLUIU-SE QUE COM O EMPREGO DO PROCESSO DE SLS DA LIGA DE TI-6AL-4V É POSSÍVEL PRODUZIR AMOSTRAS QUE CONSERVAM PROPRIEDADES MECÂNICAS SEMELHANTES ÀQUELAS PRODUZIDAS POR MÉTODOS CONVENCIONAIS DE CONFORMAÇÃO MECÂNICA E USINAGEM.

 

TITANIUM ALLOYS HAVE CHARACTERISTICS WHICH MAKE THEM VERY ATTRACTIVE FOR DIFFERENT APPLICATIONS, SUCH AS HIGH MECHANICAL RESISTANCE, LOW DENSITY AND EXCELLENT CORROSION RESISTANCE. THE AIM OF THIS STUDY IS TO CHARACTERIZE THE TI-6AL-4V ALLOY PROTOTYPED BY SELECTIVE LASER SINTERING (SLS), ANALYZE ITS MICROSTRUCTURE AND EVALUATE ITS MECHANICAL PROPERTIES. TO ACHIEVE THESE OBJECTIVES, SAMPLES WERE ANALYZED USING AN OPTICAL MICROSCOPE (OM), SCANNING ELECTRON MICROSCOPE (SEM), MICROHARDNESS TESTING AND X-RAY DIFFRACTION (XRD). THE RESULTS OBTAINED BY OM AND SEM SHOWED A CHARACTERISTIC MORPHOLOGY OF ACICULAR MARTENSITE PHASE, AND THE ANALYSIS BY XRD CONFIRMED THE COMPLETE PRESENCE OF αLFA’ PHASE. THE MARTENSITIC TRANSFORMATION βETA → αLFA’ WAS COMPLETE, AND THERE WAS NO FORMATION OF THE αLFA PHASE PREDICTED IN THE EQUILIBRIUM. IT WAS CONCLUDED THAT USING SLS PROCESS OF THE TI-6AL-4V ALLOY CAN PRODUCE SAMPLES WITH MECHANICAL PROPERTIES SIMILAR TO THOSE PRODUCED BY CONVENTIONAL METHODS OF MECHANICAL CONFORMATION AND MACHINING.

Palavras-chave

Ligas de titânio; SLS; Caracterização microestrutural; Morfologia.

Titanium alloys; SLS; Microstructural characterization; Morphology.