Título

CARACTERIZAÇÃO MICROGRÁFICA DE PRÓTESES DENTAIS DE ALUMINA INFILTRADA COM VIDRO DE LANTÂNIO E SUA CORRELAÇÃO COM A RESISTÊNCIA FLEXURAL POR TRÊS PONTOS

MICROGRAPHIC CHARACTERIZATION OF LANTHANUM GLASS INFILTRATED ALUMINA DENTAL PROSTHESIS AND ITS CORRELATION TO THE THREE- POINT FLEXURAL STRENGTH

DOI

10.5151/2594-5327-0102

Downloads

Baixar Artigo 84 Downloads

Resumo

Estudou-se a infiltração (em diferentes condições) do vidro de lantânio em alumina parcialmente sinterizada e a sua relação com a resistência flexural. As barras de In-Ceram Alumina, fraturadas em flexão por 3 pontos, foram lixadas, polidas e caracterizadas por microscopias ótica e eletrônica de varredura (MEV). Foram usadas 10 amostras para cada condição operacional. Resultados: (a) A MEV confirma que os núcleos de barras In-Ceram Alumina (sinterizados a 1120oC durante 2h) infiltrados a 1100oC durante 6h contém menos vidro de lantânio do que aqueles das barras infiltradas durante 6h a 1110oC; (b) A micrografia ótica confirma que os núcleos de barras In-Ceram Alumina (sinterizada a 1120oC durante 2h) infiltrada durante 6h (ou 2h) nas temperatruras de 1100oC, 1100oC, 1120oC e 1130oC não se diferem notavelmente; (c) A MEV mostra que a microestrutura interna de barras In-Ceram Alumina infiltradas com vidro de lantânio a 1120oC e 1130oC é complexa.

 

It was studied the infiltration of partially sintered alumina (under different conditions) by lanthanum alumino-silicate glass and its relation to the three-point flexural strength. The In- Ceram alumina bars, fractured by flexural test, were ground by sand-paper, polished, and characterized by optical and scanning electron microscopy (SEM). It was used 10 samples for each operational condition. Results: a) The SEM confirmed that the core of the In-Ceram® alumina bars (sintered at 1120oC for 2h) infiltrated at 1100oC during 6h contain less lanthanum glass than that of alumina bar infiltrated by glass at 1110oC for 6h; (b) The optical micrography confirmed that the cores of the In-Ceram®Alumina bars (sintered at 1120oC for 2h) infiltrated during 6h (or 2h) at temperatures of 1100oC, 1100oC, 1120oC and 1130oC do not differe significantly each other; (c) The SEM showed that the internal microstructure of the In-Ceram® Alumina bars infiltrated with lanthanum glass at 1120oC and 1130oC is complex.

Palavras-chave

Cerâmica dental; Alumina infiltrada com vidro; Análise ceramográfica; Resistência flexural por três pontos.

Dental ceramics; Glass-infiltrated alumina; Ceramographic analysis; Three-point flexural strength.

Como citar

Pinto, Vinicius Bemfica Barreira; Silva, Patrícia Tasca Galdino da; Silva, Raquel Costa da; Ogasawara, Tsuneharu. CARACTERIZAÇÃO MICROGRÁFICA DE PRÓTESES DENTAIS DE ALUMINA INFILTRADA COM VIDRO DE LANTÂNIO E SUA CORRELAÇÃO COM A RESISTÊNCIA FLEXURAL POR TRÊS PONTOS , p. 912-920. In: 62º Congresso anual da ABM, Vitória, 2007.