Título

CARACTERIZAÇÃO MORFOLÓGICA DA ESCÓRIA DE ALTO FORNO COMO MATÉRIA-PRIMA PARA MATERIAIS ÁLCALI ATIVADOS

MORPHOLOGICAL CHARACTERIZATION OF BLAST FURNACE SLAG AS RAW MATERIAL FOR ALKALI ACTIVATED MATERIALS

Autoria

NASCIMENTO, DAMARES DA CRUZ BARBOSA; SANTANA, RAYANNE OLIVEIRA LEÃO; FERREIRA, PAULO ANDERSON ARANHA; SILVA, ALISSON CLAY RIOS DA; CANDIDO, VERÔNICA SCARPINI

NASCIMENTO, DAMARES DA CRUZ BARBOSA

Eu sou esse autor

SANTANA, RAYANNE OLIVEIRA LEÃO

Eu sou esse autor

FERREIRA, PAULO ANDERSON ARANHA

Eu sou esse autor

SILVA, ALISSON CLAY RIOS DA

Eu sou esse autor

CANDIDO, VERÔNICA SCARPINI

Eu sou esse autor

DOI

10.5151/2594-5327-41287

Downloads

Resumo

O DESENVOLVIMENTO DE NOVOS MATERIAIS QUE UTILIZEM MATéRIAS-PRIMAS ORIUNDAS DE RESíDUOS INDUSTRIAIS, TORNAM-SE PLEITEáVEIS PARA DIVERSAS APLICAçõES. A ESCóRIA DE ALTO FORNO é UM RESíDUO ADVINDO DO PROCESSAMENTO SIDERúRGICO DO FERRO GUSA. ESSE INSUMO POSSUI CARACTERíSTICAS E PROPRIEDADES DESEJáVEIS PARA SEREM UTILIZADOS COMO MATéRIA-PRIMA EM MATERIAL áLCALI-ATIVADO. DESSA FORMA, OBJETIVA-SE ESTUDAR AS CARACTERíSTICAS MORFOLóGICAS E MINERALóGICAS DA ESCóRIA DE ALTO FORNO DE ACIARIA. PARA ISSO, REALIZOU-SE TéCNICA DE EMBUTIMENTO A QUENTE, DIFRAçãO DE RAIOS X (DRX), MICROSCOPIA óPTICA (MO) E MICROSCOPIA ELETRôNICA DE VARREDURA (MEV). POR DRX FOI POSSíVEL OBSERVAR FASES CORRESPONDENTES COMO CALCITA, QUARTZO E HEMATITA. O ASPECTO MORFOLóGICO REVELOU POSSíVEIS REGIõES CARACTERíSTICAS DE CáLCIO, óXIDO DE FERRO E PONTOS LUMINESCENTES DE QUARTZO. O MEV APRESENTOU MICROESTRUTURAS IRREGULARES COM FORMATOS E FORMAS DIFERENTES, ALéM DE REGIõES RUGOSAS E LISAS. ESSAS CARACTERíSTICAS TORNAM A ESCóRIA DE ALTO FORNO UMA MATéRIA-PRIMA COM ELEVADO POTENCIAL PARA APLICAçãO EM MATERIAIS áLCALI-ATIVADOS.

THE DEVELOPMENT OF NEW MATERIALS THAT USE RAW MATERIALS FROM INDUSTRIAL WASTE IS DESIRABLE FOR SEVERAL APPLICATIONS. BLAST FURNACE SLAG IS A RESIDUE FROM THE STEELMAKING PROCESSING OF PIG IRON. THIS INPUT HAS DESIRABLE CHARACTERISTICS AND PROPERTIES TO BE USED AS A RAW MATERIAL IN ALKALI-ACTIVATED MATERIAL. THUS, THE OBJECTIVE IS TO STUDY THE MORPHOLOGICAL AND MINERALOGICAL CHARACTERISTICS OF BLAST FURNACE SLAG FROM STEEL MILLS. FOR THIS PURPOSE, HOT EMBEDDING TECHNIQUES, X-RAY DIFFRACTION (XRD), OPTICAL MICROSCOPY (OM) AND SCANNING ELECTRON MICROSCOPY (SEM) WERE PERFORMED. BY XRD, IT WAS POSSIBLE TO OBSERVE CORRESPONDING PHASES SUCH AS CALCITE, QUARTZ AND HEMATITE. THE MORPHOLOGICAL ASPECT REVEALED POSSIBLE CHARACTERISTIC REGIONS OF CALCIUM, IRON OXIDE AND LUMINESCENT QUARTZ POINTS. THE SEM SHOWED IRREGULAR MICROSTRUCTURES WITH DIFFERENT SHAPES AND FORMS, AS WELL AS ROUGH AND SMOOTH REGIONS. THESE CHARACTERISTICS MAKE BLAST FURNACE SLAG A RAW MATERIAL WITH HIGH POTENTIAL FOR APPLICATION IN ALKALI-ACTIVATED MATERIALS.

Palavras-chave

Escória de alto forno; Microscopia; Caracterização; Geopolímero

Blast furnace slag; Microscopy; Characterization; Geopolymer.