Título

CARACTERIZAÇÃO MORFOLÓGICA DA FIBRA DE TURURI PARA AVALIAR SEU POTENCIAL USO COMO REFORÇO DE MATRIZ POLIMÉRICA

MORPHOLOGICAL CHARACTERIZATION OF TURURI FIBER TO EVALUATE ITS POTENTIAL USE AS REINFORCEMENT IN POLYMERIC MATRIX COMPOSITE

Autoria

Santos, Avener Gleidson Andrade; Matos, Taiana de Sousa; Nascimento, Damares da Cruz Barbosa; Monteiro, Sérgio Neves; Silva, Alisson Clay Rios da; Candido, Verônica Scarpini

DOI

10.5151/2594-5327-34973

Downloads

Baixar Artigo 42 Downloads

Resumo

A BUSCA POR NOVOS MATERIAIS COM PROPRIEDADES EQUIVALENTES ÀS SINTÉTICAS, ALAVANCOU A PESQUISA E O DESENVOLVIMENTO DE NOVOS MATERIAIS. VISANDO O ALTO DESEMPENHO E SUSTENTABILIDADE, AS FIBRAS DA REGIÃO AMAZÔNICA VÊM SE DESTACANDO NO CAMPO DAS PESQUISAS. NESSE SENTIDO, A BUSCA POR NOVOS MATERIAIS COM CARACTERÍSTICAS RENOVÁVEIS FAZ-SE NECESSÁRIA, BUSCANDO EM PRIMEIRO LUGAR O BAIXO CUSTO AGREGADO À ELEVADA RESISTÊNCIA. ESSE TRABALHO OBJETIVA CARACTERIZAR A MORFOLOGIA DO TECIDO FIBROSO DE TURURI E DETERMINAR A MASSA ESPECÍFICA PARA POSSÍVEL APLICAÇÃO COMO REFORÇO EM COMPÓSITOS DE MATRIZ POLIMÉRICA. A FIBRA DE TURURI, POR APRESENTAR-SE NA FORMA DE TECIDO FIBROSO, DESPERTA ELEVADO INTERESSE NO CAMPO DAS PESQUISAS. APESAR DE SER POUCO EXPLORADO NA LITERATURA, O TECIDO É AMPLAMENTE UTILIZADO EM ATIVIDADES RÚSTICAS, COMO RECOBRIMENTO DE RESIDÊNCIAS E CONFECÇÃO DE ARTESANATOS E CESTOS. O TECIDO FIBROSO FOI OBTIDO NO MERCADO DO VER-O-PESO, BELÉM – PARÁ. O TECIDO FOI LAVADO EM ÁGUA CORRENTE E SABÃO NEUTRO, EM SEGUIDA FOI ENCAMINHADO PARA SECAGEM EM ESTUFA À 60 ºC POR 90 MINUTOS. O TECIDO FOI CARACTERIZADO EM MICROSCÓPIO ÓPTICO (MO) E MICROSCÓPIO ELETRÔNICO DE VARREDURA (MEV). E, TAMBÉM, FOI REALIZADA A DETERMINAÇÃO DA MASSA ESPECIFICA DO TECIDO EM ETANOL. OS RESULTADOS OBTIDOS INDICAM QUE O TECIDO FIBROSO TEM ELEVADO POTENCIAL PARA SER UTILIZADO COMO REFORÇO EM COMPÓSITO DE MATRIZ POLIMÉRICA, POR CONTA DA SUA BAIXA MASSA ESPECIFICA E O ELEVADO GRAU DE ENTRELAÇAMENTO OBSERVADO NA MEV E NA MO

 

THE SEARCH FOR NEW MATERIALS WITH PROPERTIES EQUIVALENT TO SYNTHETIC ONES, LEVERAGED THE RESEARCH AND DEVELOPMENT OF NEW MATERIALS. AIMING AT HIGH PERFORMANCE AND SUSTAINABILITY, FIBERS FROM THE AMAZON REGION HAVE BEEN STANDING OUT IN THE FIELD OF RESEARCH. IN THIS SENSE, THE SEARCH FOR NEW MATERIALS WITH RENEWABLE CHARACTERISTICS IS NECESSARY, SEEKING IN THE FIRST PLACE THE ADDED COST TO THE HIGH RESISTANCE. THIS WORK AIMS TO CHARACTERIZE THE MORPHOLOGY OF THE FIBROUS TISSUE OF TURURI AND DETERMINE A SPECIFIC MASS FOR POSSIBLE APPLICATION OF REINFORCEMENT IN POLYMER MATRIX COMPOSITES. THE TURURI FIBER, AS IT PRESENTS ITSELF IN THE FORM OF FIBROUS TISSUE, AROUSES INTEREST IN THE FIELD OF RESEARCH. OF BEING AN EXPLORER IN THE LITERATURE, THE FABRIC, DESPITE BEING LITTLE USED IN ACTIVITIES, SUCH AS COVERING HOUSES AND MAKING HANDICRAFTS AND BASKETS. THE FIBROUS TISSUE WAS PURCHASED AT THE VER-O-PESO MARKET, BELéM - PARá. THE TISSUE WAS WASHED IN RUNNING AND NEUTRAL WATER, THEN SENT TO DRYING IN AN OVEN AT 0 ºC FOR 1. THE TISSUE WAS EMINENTLY OPTICAL AESTHETIC (MO) AND ELECTRONIC MECHANISM (MEV). ALSO, THE DETERMINATION OF THE SPECIFIC MASS OF THE ETHANOL TISSUE WAS PERFORMED. THE RESULTS OBTAINED INDICATE THAT THE FIBROUS TISSUE HAS THE POTENTIAL TO BE USED AS A REINFORCEMENT IN A POLYMER MATRIX COMPOSITE, DUE TO THE LOW MASS AND THE HIGH DEGREE OF ENTANGLEMENT OBSERVED IN SEM AND OM

Palavras-chave

Tecido fibroso, Compósitos, poliméricos, Amazônia, Tururi

Fibrous tissue, Composites, Polymers, Amazon, Tururi