CARACTERIZAÇÃO MORFOLÓGICA DE COMPÓSITOS DE MATRIZ POLIMÉRICA REFORÇADA COM FIBRAS DE AÇAÍ E CURAUÁ: MORPHOLOGICAL CHARACTERIZATION OF POLYMER MATRIX COMPOSITES REINFORCED WITH AÇAÍ AND CURAUÁ FIBERS

EM MATERIAIS COMPóSITOS, A UTILIZAçãO DE FIBRAS LIGNOCELULóSICAS COMO REFORçO é UMA ALTERNATIVA SUSTENTáVEL, DE BAIXO CUSTO E COM PROPRIEDADES MECâNICAS SIGNIFICATIVAS EM RELAçãO AS FIBRAS SINTéTICAS. O OBJETIVO DESSE ESTUDO FOI DESENVOLVER MATERIAIS COMPóSITOS ATRAVéS DO MéTODO MANUAL DE FABRICAçãO, COM MATRIZ POLIéSTER ORTOFTáLICA EMPREGANDO REFORçO DE FIBRAS LIGNOCELULóSICAS DE AçAí, CURAUá E HíBRIDO PARA REALIZAR ANáLISES MORFOLóGICAS DAS SUPERFíCIES DE FRATURAS. OS VALORES DE FRAçãO MáSSICA UTILIZADAS NOS COMPóSITOS FORAM DE 50% DE FIBRA, PARA 50% DE RESINA E 1% DE CATALISADOR, E PARA O COMPóSITO HíBRIDO FORAM 25% DE FIBRA DE AçAí E 25% DE FIBRA DE CURAUá PARA 50% DE RESINA POLIéSTER. PARA ISSO, FOI REALIZADO ENSAIO DE DENSIDADE DAS FIBRAS, ANáLISE MORFOLóGICA DA SUPERFíCIE DE FRATURA DOS COMPóSITOS ATRAVéS DE ANáLISES MICROSCóPICAS DOS CORPOS-DE-PROVA, POR MEIO DE MICROSCOPIA ÓPTICA (MO) E MICROSCOPIA ELETRôNICA DE VARREDURA (MEV). AS ANáLISES MOSTRARAM QUE OS COMPóSITOS APRESENTARAM UMA BOA ADESãO INTERFACIAL FIBRA/MATRIZ, OBSERVADAS PELO ROMPIMENTO DAS FIBRAS E PRESENçA DE POUCAS BOLHAS, ASSIM DEMONSTRANDO POTENCIAL PARA UM COMPORTAMENTO MECâNICO SATISFATóRIO, SENDO APTOS PARA REALIZAçãO DE ENSAIOS MECâNICOS E APLICAçõES FUTURAS.

IN COMPOSITE MATERIALS, THE USE OF LIGNOCELLULOSIC FIBERS AS REINFORCEMENT IS A SUSTAINABLE, LOW-COST ALTERNATIVE WITH SIGNIFICANT MECHANICAL PROPERTIES COMPARED TO SYNTHETIC FIBERS. THE OBJECTIVE OF THIS STUDY WAS TO DEVELOP COMPOSITE MATERIALS THROUGH THE MANUAL MANUFACTURING METHOD, WITH AN ORTHOPHTHALIC POLYESTER MATRIX USING REINFORCEMENT FROM AçAí, CURAUá AND HYBRID LIGNOCELLULOSIC FIBERS TO PERFORM MORPHOLOGICAL ANALYZES OF FRACTURE SURFACES. THE MASS FRACTION VALUES USED IN THE COMPOSITES WERE 50% FIBER, 50% RESIN AND 1% CATALYST, AND FOR THE HYBRID COMPOSITE THEY WERE 25% AçAí FIBER AND 25% CURAUá FIBER TO 50% RESIN. POLYESTER. TO THIS END, FIBER DENSITY TESTING AND MORPHOLOGICAL ANALYSIS OF THE FRACTURE SURFACE OF THE COMPOSITES WERE CARRIED OUT THROUGH MICROSCOPIC ANALYSIS OF THE SPECIMENS, USING OPTICAL MICROSCOPY (OM) AND SCANNING ELECTRON MICROSCOPY (SEM). THE ANALYZES SHOWED THAT THE COMPOSITES PRESENTED GOOD FIBER/MATRIX INTERFACIAL ADHESION, OBSERVED BY THE RUPTURE OF THE FIBERS AND THE PRESENCE OF FEW BUBBLES, THUS DEMONSTRATING THE POTENTIAL FOR SATISFACTORY MECHANICAL BEHAVIOR, BEING SUITABLE FOR CARRYING OUT MECHANICAL TESTS AND FUTURE APPLICATIONS.

Palavras-chave

Fibras de açaí; poliéster ortoftálico; análise morfológica.

Açaí fibers; orthophthalic polyester; morphological analysis.

Como citar

COELHO, DAYSE NATALIA MATOS; FERREIRA, PAULO ANDERSON ARANGA; FRANÇA, GIOVANA ZAGALO DE; SANTANA, RAYANNE OLIVEIRA LEÃO; CANDIDO, VERÔNICA SCARPINI; SILVA, ALISSON CLAY RIOS DA. CARACTERIZAÇÃO MORFOLÓGICA DE COMPÓSITOS DE MATRIZ POLIMÉRICA REFORÇADA COM FIBRAS DE AÇAÍ E CURAUÁ , p. 2256-2265. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-41179