CARACTERÍSTICAS MICROESTRUTURAIS, MODOS DE FALHA E PROPRIEDADES MECÂNICAS DE AÇOS TWIP SOLDADOS POR SOLDAGEM A PONTO POR RESISTÊNCIA

MICROSTRUCTURAL FEATURES, FAILURE MODES AND MECHANICAL PROPERTIES OF RESISTANCE SPOT WELDED TWIP STEELS

DOI

10.5151/1516-392X-31691

Downloads

Baixar Artigo 261 Downloads

Resumo

Chapas de aço TWIP980 foram soldadas por soldagem a ponto por resistência com diferentes parâmetros de processo. A microestrutura pós-soldagem foi caracterizada e as propriedades mecânicas das juntas soldadas foram avaliadas. Para cada condição de processo, os modos de falha foram identificados e correlacionados com as propriedades mecânicas. Não foram identificadas regiões de segregação de manganês, indicando que o material pós-soldado mantém sua microestrutura austenítica, o que foi confirmado por difractogramas de raios-x e micrografias ópticas. Mapas de microindentação mostraram uma distribuição heterogênea de propriedades mecânicas ao longo da junta soldada. Além disto, a região mais macia localiza-se na zona de fusão da solda, favorecendo modos de falha frágeis, o que foi identificado através de ensaios mecânicos de tração-cisalhamento. No entanto, ajustes de parâmetros de processo mostraram-se eficazes para promover outros modos de falhas, inclusive falha dúctil, o que foi confirmado através de micrografias eletrônicas. Os resultados também mostraram que a resistência mecânica e a capacidade de absorção de energia das juntas estão diretamente relacionados com os parâmetros de processo e modos de falha.

 

TWIP980 steel sheets were welded by resistance spot welding with different welding parameters. The as-welded microstructure was characterized and the mechanical properties of the weld spots were assessed. For each welding condition, the failure modes were identified and correlated with the mechanical properties. No considerable Mn segregation was identified, indicating that the material remains essentially austenitic in the as-welded condition, which was confirmed by XRD patterns and optical micrographs. The fusion zone hardness is lower than that of heat affected zone and base metal, as evidenced by microindentation maps, which facilitates interfacial failure mode during tensile-shear tests. However, adjustments in the process parameters were shown to be effective in promoting more favorable failure modes, which was confirmed by scanning electron micrographs. The results also showed that the tensile-shear strength and energy absorption capability are directly correlated to the failure modes and the welding process parameters.

Palavras-chave

Aço TWIP; AHSS; Soldagem a ponto por resistência; modos de falhas

TWIP steel; AHSS: resistance spot welding; failure modes