CARATERIZAÇÃO MICROESTRUTURAL E DA TEXTURA CRISTALOGRÁFICA DA LIGA Al AA1070 DEFORMADO A FRIO VIA ECAP A PARTIR DA ROTA C

MICROSTRUCTURAL CHARACTERIZATION AND OF THE CRYSTALLOGRAPHIC TEXTURE OF THE AL AA1070 ALLOY DEFORMED BY THE COLD ECAP PROCESS FROM ROUTE C

DOI

10.5151/1516-392X-25196

Downloads

Baixar Artigo 305 Downloads

Resumo

O trabalho teve por objetivo produzir uma liga Al AA1070 com microestrutura ultrafina via prensagem por canais equiangulares. O processo empregou a rota C com 2 passes consecutivos a frio e acumulou uma deformação ?2 = 2,38. O material de partida é proveniente de um processo de laminação a quente na qual a microestrutura resultante era composta de grãos grosseiros com tamanho de grão de 14,5 ± 19,1 ?m e dureza de 31,1 ± 1,9 Vickers. Foi realizada a caracterização microestrutural com o auxílio das técnicas de microscopia eletrônica de varredura (MEV) e de difração de elétrons retroespalhados. O comportamento mecânico das amostras foi avaliado por ensaios de dureza Vickers, a fim de se determinar a energia armazenada durante os passes. Os resultados obtidos mostraram que o material de partida apresentou estrutura parcialmente recristalizada, decorrente do processo termomecânico de laminação. A deformação cisalhante severa que ocorre na interseção entre os canais durante o processamento via ECAP permitiu um intenso refinamento de grãos. O tamanho de grão após o 2° passe foi da ordem de 1,6 ± 1,7 µm. A dureza após o 1° passe quase dobrou em relação ao material de partida, mas praticamente se manteve no passe seguinte, sugerindo uma possível estabilidade. Pode-se concluir que ocorreu um considerável refinamento do tamanho de grão em função da elevada fragmentação e rotação da subestrutura após os passes de deformação.

 

The study aimed to produce an alloy with ultrafine Al AA1070 via equiangular channels by pressing microstructure. The process employed to route C with 2 consecutive cold passes and accumulated deformation ?2 = 2.38. The starting material is from a hot rolling process in which the resulting microstructure consisted of coarse grains with grain size of 14.5 ± 19.1 micrometers me hardness of 31.1 ± 1.9 Vickers. Microstructural characterization was performed with the aid of electron microscopy (SEM) and electron backscatter diffraction. The mechanical behavior of the samples was measured by Vickers hardness tests in order to determine the energy stored during the passes. The results showed that the starting material had partially recrystallized structure, resulting from the thermomechanical rolling process. The severe shear deformation that occurs at the intersection between channels during processing via ECAP allowed an intensive grain refinement. The grain size after the 2nd pass was approximately 1.6 ± 1.7 micrometers. The hardness after the 1st pass almost doubled compared to the starting material, but virtually remained the next pass, suggesting a possible stability. It can be concluded that there was a considerable refinement of grain size due to the high fragmentation and rotating the substructure passes after deformation.

Palavras-chave

MEV; ECAP; Al AA 1070; Deformação plástica severa; Caracterização microestrutural e textura cristalográfica

MEV; ECAP; Al AA 1070; Severe plastic deformation; Microstructural characterization and crystallographic texture

Como citar

Gabriel Gonçalves Pessoa de Castro; Rachel dos Santos Mendes; Manuela Fontana; Ana Carolina Ribeiro Duarte; Jefferson Fabrício Cardoso Lins. CARATERIZAÇÃO MICROESTRUTURAL E DA TEXTURA CRISTALOGRÁFICA DA LIGA Al AA1070 DEFORMADO A FRIO VIA ECAP A PARTIR DA ROTA C , p. 9285-9293. In: 69° Congresso Anual da ABM - Internacional, São Paulo - Brasil, 2014.