COLAGEM DE JUNTA DE MADEIRA COM ADESIVO EPÓXI

ADHESIVENESS WOOD-WOOD WITH EPOXY

Autoria

Cardoso, Ruth Pereira; Neto, Bernardo Borges Pompeu; Fujiyama, Roberto Tetsuo

Cardoso, Ruth Pereira

Eu sou esse autor

Neto, Bernardo Borges Pompeu

Eu sou esse autor

Fujiyama, Roberto Tetsuo

Eu sou esse autor

DOI

10.5151/2594-5327-15234

Downloads

Resumo

Este trabalho tem como, objetivo confeccionar, testar e comparar juntas coladas de topo, biselada e encaixada de espécies de madeira de diferentes densidades. A metodologia de fabricação das juntas, foi estabelecida nos procedimentos descritos na norma brasileira NBR 7190 de 1997 Realizou-se ensaio de caracterização da madeira, para confirmação de suas espécies. Depois de estabelecida à dimensão das juntas confeccionaram-se os corpos de prova utilizando as madeiras Angelim- pedra, Jatobá e Tauari, adquirida em depósito de madeira na cidade de Ananindeua- Pa, e o adesivo Compound Adesivo de base epóxi. Após a colagem das juntas realizou-se ensaio de tração a fim de determinar à resistência. Quanto à caracterização do adesivo, verificou-se através do ensaio de tração, que tem boa resistência mecânica. Os resultados mostram que, quanto maiores forem às áreas de colagem das juntas, mais eficiente ficam as emendas. De acordo com os resultados, observou-se que a madeira Jatobá combinou muito bem com este tipo de adesivo. Com relação às juntas coladas, a junta biselada mostrou-se mais eficiente, pois obteve a maior tensão de ruptura em relação à junta de topo e encaixada para os três tipos de madeira. Os valores médios da resistência à tração paralela às fibras, determinado nos corpos de prova das juntas colada biselada de Jatobá apresentou equivalência à resistência ao cisalhamento da madeira sólida, que de acordo com a norma NBR 7190 de 1997, indica boa qualidade da adesão.

This work has the objective of making, to test and to compare the glued joints of butt, scarf and (finger) telescope with three species of wood of different densities. The methodology of production of the joint, it was established in the procedures described in the Brazilian norm NBR 7190 of 1997. Rehearsal of characterization of the wood it was accomplished, for confirmation of your species. After established the dimension of the joints was made the bodies of proof using wood Angelim-pedra, Jatobá and Tauari, acquired in wood deposit in the city of Ananindeua-Pa, and the adhesive Compound Adesivo of epoxy base. After collages of the joints it was accomplished traction rehearsal to determining the resistance. With relationship to the characterization of the adhesive, it was verified through the traction rehearsal that has good mechanical resistance. The results present as larger collage area of the joints, more efficient are the joints. In agreement with the results, is observed that the wood Jatobá combined very well with this adhesive type. With relationship to the glued joints, the scarf joint it was shown more efficient because obtained the largest rupture tension in relation to the glued butt joints and telescope for the three wood types. The medium values of the resistance to the parallel traction to the fibers, determining in the bodies of proof of the glued joints of scarf of Jatobá it presented equivalence to the resistance to the shearing of the solid wood, that in agreement with the norm NBR 7190 of 1997, it indicates good quality of the adhesion.

Palavras-chave

Madeira; Adesivo; Juntas coladas.

Wood; Adhesive; Glued joints.