Título

COMPARAÇÃO DA DUREZA VICKERS SOBRE A ADIÇÃO SUPERFICIAL ATRAVÉS DO TRATAMENTO TERMOQUÍMICO DE PB E SN NAS AMOSTRAS DE LIGAS DE CU-AL

COMPARATIVE STUDY OF VICKERS HARDNESS ON SURFACE ADDITION BY MEANS THE THERMOCHEMICAL TREATMENT OF PB AND SN IN SAMPLES OF CU-AL ALLOYS

Autoria

Neuba, Lucas de Mendonça; Oliveira, Pablo Henrique Ataide; Almeida, Rangel de Paula; Oliveir, Alexsandro de; Junio, Raí Felipe Pereira; Palmeira, Alexandre Alvarenga; Monteiro, Sergio Neves

DOI

10.5151/2594-5327-34452

Downloads

Baixar Artigo 15 Downloads

Resumo

OS METAIS BABBITT CONSISTEM EM UMA MICROESTRUTURA COM UMA JUNÇÃO DE UMA MATRIZ DÚCTIL COM PARTICULADOS INTERMETÁLICOS DUROS (SN-SB OU CU6SN). GRANDE PARTE DOS NOVOS MATERIAIS UTILIZADOS EM ROLAMENTOS SÃO BASEADOS NESSAS LIGAS BABBITT. O PRESENTE TRABALHO BUSCA ESTUDAR A SUBSTITUIÇÃO E COMPARAR ANEIS DE VEDAÇÕES DE BRONZE ALUMINIO (CUAL) COM ADIÇÃO SUPERCIAL DE ESTANHO (SN), POR UM ANEL DE BRONZE ALUMINIO COM ADIÇÃO SUPERFICIAL DE CHUMBO (CUAL +PB), UTILIZADOS EM UMA BOMBA DE DESLOCAMENTO POSITIVO. FORAM UTILIZADAS AMOSTRAS DE SAE-68D COM DIMENSÕES DE 2,5 X 2,5 X 1,0 CM, AS QUAIS FORAM SUBMETIDAS A PROCESSOS DE TRATAMENTO TERMOQUÍMICO, BASEANDO-SE EM DIFERENTES PERÍODOS DE TEMPO, 3, 4 E 5 HORAS. DURANTE ESSE PROCESSO OCORRE A DIFUSÃO DO ELEMENTO QUÍMICO PB PARA A SUPERFÍCIE DAS AMOSTRAS E NÃO PARA O CENTRO DA MESMA. A DUREZA POR MICROIDENTAÇÃO FOI REALIZADA CONFORME A NORMA ASTM E92 SEGUIDO-SE DE UMA COMPARAÇÃO ENTRE OS RESULTADOS OBTIDOS PARA A LIGA EM ESTUDO (CUAL + PB) E A LIGA DE BRONZE ALUMINIO COM ESTANHO SUPERCIAL (CUAL + SN).

 

A BABBITT METAL MICROSTRUCTURE CONSIST OF A SOFT MATRIX AND HARD INTERMETALLIC PARTICLES OF SN-SB E CU6SN. MOST OF THE NEW BEARING MATERIALS ARE BASED ON BABBITT METAL ALLOYS. THE PRESENT WORK AIMS TO STUDY THE POSSIBILITY OF SUBSTITUTING A SEALING RING OF CUAL BRONZE COATED WITH TIN (SN) FOR A SEALING RING OF CUAL COATED WITH SUPERFICIAL LEAD (PB) ON A FUNCTIONAL POSITIVE DISPLACEMENT PUMP. SAMPLES OF SAE-68D WITH DIMENSIONS OF 2.5 X 2.5 X 1,0 CM WERE USED AS SAMPLES. THESE SAMPLES WERE SUBJECTED TO A THERMOCHEMICAL TREATMENT PROCESS, BASED ON DIFFERENT PERIODS RANGING FROM 3, 4, AND 5 HOURS. DURING THESE PERIODS A DIFFUSION OF THE CHEMICAL ELEMENT PB OCCURRED ON THE SURFACE OF THE SPECIMENS. A HARDNESS HAVE BEEN DONE FOLLOWING THE PROCEDURES OF ASTM E92, AFTER THAT A COMPARISON BETWEEN THE DIFFERENT GROUPS WAS ANALYZED. BESIDES THE RESULTS WERE COMPARED TO THE PREVIOUS OPERATING SEALING RING OF CUAL BRONZE COATED WITH SUPERFICIAL SN.

Palavras-chave

Babbitt;Tratamento termoquimico; Dureza Vickers; Bronze aluminio.

Babbitt; Thermochemical treatment; Vickers hardness; Bronze.