A UTILIZAÇÃO DE FIBRAS NATURAIS EM COMPÓSITOS É UMA ALTERNATIVA MAIS LEVE E ECONÔMICA DO QUE A APLICAÇÃO DE FIBRAS DE VIDRO. DESSA FORMA, ESTE TRABALHO BUSCA COMPARAR A RESISTÊNCIA A TRAÇÃO DE COMPÓSITOS EPOXÍDICOS REFORÇADOS COM TECIDOS DE JUTA COM COMPÓSITOS COM TECIDO DE FIBRA DE VIDRO, BEM COMO, COM O MATERIAL DA MATRIZ, A RESINA EPÓXI. A RESINA UTILIZADA FOI UM SISTEMA DGEBA/TETA E O ENSAIO FOI REALIZADO CONFORME A ASTM 3039, A UMA TAXA DE 2MM/MIN. A SIGNIFICÂNCIA ESTATÍSTICA ENTRE COMPÓSITOS PRODUZIDOS E A RESINA EPÓXI PURA AVALIADA POR MEIO DA ANÁLISE POR VARIÂNCIA (ANOVA) E TESTE DE TUKEY. OS RESULTADOS INDICARAM QUE OS COMPÓSITOS DE TECIDO DE VIDRO OBTIVERAM UM ACRÉSCIMO DE RESISTÊNCIA A TRAÇÃO E MÓDULO DE TENACIDADE. ENTRETANTO, OS COMPÓSITOS REFORÇADOS COM JUTA APRESENTARAM UM COMPORTAMENTO PRÓXIMO AO EPÓXI, NÃO POSSUINDO NENHUMA DIFERENÇA ESTATISTICAMENTE RELEVANTE.
THE USE OF NATURAL FIBERS IN COMPOSITES IS A LIGHTER AND MORE ECONOMICAL ALTERNATIVE TO THE APPLICATION OF GLASS FIBERS. THUS, THIS WORK SEEKS TO COMPARE THE TENSILE STRENGTH OF EPOXY COMPOSITES REINFORCED WITH JUTE FABRICS WITH FIBERGLASS COMPOSITES, AS WELL AS THE MATRIX MATERIAL, EPOXY RESIN. THE RESIN USED WAS A DGEBA/TETA SYSTEM AND THE TEST WAS PERFORMED ACCORDING TO ASTM 3039, AT A RATE OF 2MM/MIN. THE STATISTICAL SIGNIFICANCE BETWEEN COMPOSITES PRODUCED AND PURE EPOXY RESIN WAS EVALUATED THROUGHT ANALYSIS BY VARIANCE (ANOVA) AND TUKEY'S TEST. THE RESULTS INDICATED THAT THE GLASS FABRIC COMPOSITES OBTAINED AN INCREASE IN TENSILE STRENGTH AND TENACITY MODULUS. HOWEVER, COMPOSITES REINFORCED WITH JUTE HAD A SIMILAR BEHAVIOR TO EPOXY, WITH NO STATISTICALLY RELEVANT DIFFERENCE.
Palavras-chave
Compósitos; Epóxi; Fibra de Juta; Fibra de Vidro
Composites; Epoxy; Jute fiber; Fiberglass
Como citar
Moreira, Mariane Oliveira;
Velasco, David Coverdale Rangel;
Alves, Gustavo Maciel Rodrigues;
Lopes, Felipe Perissé Duarte;
Simonassi, Noan Tonini;
Monteiro, Sergio Neves;
Vieira, Carlos Maurício Fontes;
Loiola, Rômulo Leite.
COMPARAÇÃO DA RESISTÊNCIA A TRAÇÃO DE COMPÓSITOS EPOXÍDICOS REFORÇADOS COM TECIDO DE JUTA E COM TECIDO DE VIDRO
,
p. 2887-2897.
In: 75° Congresso Anual da ABM,
São Paulo,
2022.
ISSN: 2594-5327
, DOI 10.5151/2594-5327-34702