A ATUAçãO DOS MECANISMOS RESTAURATIVOS DURANTE DEFORMAçãO A QUENTE é DE FUNDAMENTAL IMPORTâNCIA PARA AS PROPRIEDADES DA AUSTENITA DEFORMADA, QUE IMPACTARá DIRETAMENTE NA RESISTêNCIA à DEFORMAçãO AO LONGO DOS PASSES SUBSEQUENTES DA LAMINAçãO A QUENTE E NA MICROESTRUTURA FINAL OBTIDA, CONSEQUENTEMENTE NAS PROPRIEDADES MECâNICAS. NESTE ESTUDO A INFLUêNCIA DESSES MECANISMOS FOI ESTUDADA EM ENSAIOS DE DEFORMAçãO DE DUPLO PASSE AVALIANDO-SE O COMPORTAMENTO DAS CURVAS TENSãO-DEFORMAçãO OBTIDAS E MEDINDO-SE O AMACIAMENTO GERADO ENTRE OS PASSES. O AçO ESTUDO FOI O 27MNCRB5 COM E SEM ADIçãO DE NIóBIO. FORAM UTILIZADAS TEMPERATURAS DE DEFORMAçãO DE 800 °C A 1050 °C E INTERVALOS ENTRE PASSES DE 1 S E 3 S A UMA TAXA DE DEFORMAçãO DE 20 S-1. FORAM OBTIDAS IMAGENS VIA MICROSCóPIO óTICO E MEV PARA CARACTERIZAçãO DA MICROESTRUTURA. FOI ENCONTRADO QUE O AMACIAMENTO é PARCIAL PARA TEMPERATURAS ATé 1000° C PARA OS INTERVALOS DE 1S ATé 900 °C PARA OS INTERVALOS DE 3S E INDICANDO RECRISTALIZAçãO PARCIAL DOS GRãOS. AMACIAMENTOS SUPERIORES A 100% FORAM ENCONTRADOS PARA INTERVALOS DE 3 S E TEMPERATURAS SUPERIORES A 1000 °C INDICANDO POSSíVEL CRESCIMENTO DE GRãO E FORMAçãO DE GRãOS METADINâMICAMENTE FORMADOS. AS TEMPERATURAS DE NãO RECRISTALIZAçãO OBTIDAS POR FóRMULAS EMPíRICAS E POR OUTROS ENSAIOS DE DUPLO PASSE NãO FORAM COMPATíVEIS COM O COMPORTAMENTO DESTE ENSAIO DEVIDO à TAXA DE DEFORMAçãO E àS DEFORMAçõES MAIS ELEVADAS. O NIóBIO NãO DEMONSTROU EFETIVIDADE APARENTE NOS ENSAIOS UMA VEZ QUE ESTE FOI ENCONTRADO ASSOCIADO A PRECIPITADOS GROSSEIROS DE TIN.
THE ROLE OF RESTORATION MECHANISMS DURING HOT DEFORMATION IS FUNDAMENTALLY IMPORTANT FOR THE PROPERTIES OF DEFORMED AUSTENITE, DIRECTLY IMPACTING DEFORMATION RESISTANCE DURING SUBSEQUENT HOT ROLLING PASSES AND THE FINAL MICROSTRUCTURE, THUS INFLUENCING THE MECHANICAL PROPERTIES. IN THIS STUDY, THE INFLUENCE OF THESE MECHANISMS WAS EXAMINED IN DOUBLE-HIT PLANE STRAIN COMPRESSION TESTS BY EVALUATING THE BEHAVIOR OF THE OBTAINED STRESS-STRAIN CURVES AND MEASURING THE SOFTENING GENERATED BETWEEN THE PASSES. THE STUDIED STEEL WAS 27MNCRB5 WITH AND WITHOUT NIOBIUM ADDITION. DEFORMATION TEMPERATURES RANGED FROM 800 °C TO 1050 °C, WITH INTERVALS BETWEEN PASSES OF 1 S AND 3 S AT A STRAIN RATE OF 20 S-1. MICROSTRUCTURAL CHARACTERIZATION WAS PERFORMED USING OPTICAL MICROSCOPY AND SEM. IT WAS FOUND THAT SOFTENING IS PARTIAL FOR TEMPERATURES UP TO 1000°C FOR 1 S INTERVALS AND UP TO 900°C FOR 3 S INTERVALS, INDICATING PARTIAL RECRYSTALLIZATION OF THE GRAINS. SOFTENINGS GREATER THAN 100% WERE FOUND FOR 3 S INTERVALS AT TEMPERATURES STARTING AT 1000°C, INDICATING POSSIBLE GRAIN GROWTH AND THE OCCURRENCE OF METADYNAMICALLY FORMED GRAINS. THE NON-RECRYSTALLIZATION TEMPERATURES OBTAINED FROM EMPIRICAL FORMULAS AND OTHER DOUBLE-HIT TESTS WERE NOT COMPATIBLE WITH THE BEHAVIOR OF THIS TEST DUE TO THE HIGHER STRAIN RATE AND DEFORMATIONS. NIOBIUM WAS ASSOCIATED WITH COARSE TIN PRECIPITATES AND SHOWED NO NOTICEABLE EFFECTIVENESS AS DISLOCATION PINNING AGENT.
Palavras-chave
Mecanismos restaurativos; ensaio duplo passe; 27MnCrB5; adição de nióbio
Restoration mechanisms; Double-hit deformation; 27MnCrB5; Niobium addition
Como citar
DIAS, TARCÍSIO FERREIRA;
FERNANDES, JOELMA KRUGEL BRITES;
MACHADO, MARCELO LUCAS PEREIRA;
MURAD, BRUNO BASTOS DA SILVA;
FERREIRA, FERNANDO GENEROSO NEIVA;
DIAS, TARCÍSIO FERREIIRA;
DIAS, TARCÍSIO FERREIIRA.
COMPORTAMENTO DA DEFORMAçãO A QUENTE DO AçO 27MNCRB5 SOB TESTE DE DEFORMAçãO PLANA DE DUPLO PASSE
,
p. 467-482.
In: 59º Seminário de Laminação, Conformação de Metais e Produtos,
São Paulo, Brasil,
2024.
ISSN: 2594-5297
, DOI 10.5151/2594-5297-41086