Título

COMPORTAMENTO DE ABSORÇÃO DE ENERGIA DE COMPÓSITOS REFORÇADOS COM TECIDO DE FIQUE: EVELHECIMENTO EM ALTA TEMPERATURA

ENERGY ABSORPTION BEHAVIOR OF FIQUE FABRIC REINFORCED COMPOSITES: HIGH TEMPERATURE AGING

Autoria

Oliveira, Michelle Souza; Luz, Fernanda Santos da

Oliveira, Michelle Souza

Eu sou esse autor

Luz, Fernanda Santos da

Eu sou esse autor

DOI

10.5151/2594-5327-34365

Downloads

Resumo

A FIM DE PROTEGER CONTRA O IMPACTO DE UM PROJÉTIL, PROTEÇÕES BALÍSTICAS DEVEM DISSIPAR A ENERGIA CINÉTICA DESSE PROJÉTIL. ATUALMENTE, HÁ UMA GRANDE QUANTIDADE DE MATERIAIS EMPREGADOS NA FABRICAÇÃO DE COLETES BALÍSTICOS. CONTUDO, AINDA NÃO EXISTE UM PROTOCOLO INTERNACIONALMENTE COMUM PARA SUBSTITUIÇÃO DOS COLETES EM USO, UMA VEZ QUE NÃO É COMUM A UTILIZAÇÃO DE TESTES DURANTE O PERÍODO DE USO. TORNA-SE IMPORTANTE ESTUDAR O COMPORTAMENTO SOB DIFERENTES ENVELHECIMENTOS DE MATERIAIS COMPÓSITOS DE MATRIZ POLIMÉRICA REFORÇADOS COM FIBRAS NATURAIS, LEVANTADOS COMO POSSÍVEIS SUBSTITUTOS AS FIBRAS SINTÉTICAS EMPREGADAS. OS COMPÓSITOS EPOXÍDICOS REFORÇADOS COM TECIDO DE FIQUE FORAM EXPOSTOS EM ALTA TEMPERATURA (170°C), EM DIFERENTES TEMPOS 72, 120 E 240 HORAS. AS AMOSTRAS FORAM SUBMETIDAS A TESTES BALÍSTICOS (CLASSE I). OBSERVOU-SE QUE A TEMPERATURA É UM FATOR IMPORTANTE QUE LEVA A MUDANÇAS NAS PROPRIEDADES DOS COMPÓSITOS, BEM COMO DA MATRIZ.

IN ORDER TO PROTECT AGAINST THE IMPACT OF A PROJECTILE, BALLISTIC PROTECTIONS MUST DISSIPATE THE KINETIC ENERGY OF THAT PROJECTILE. CURRENTLY, THERE IS A LARGE AMOUNT OF MATERIALS USED IN THE MANUFACTURE OF BALLISTIC VESTS. HOWEVER, THERE IS STILL NO INTERNATIONALLY COMMON PROTOCOL FOR REPLACING THE VESTS IN USE, SINCE IT IS NOT COMMON TO USE TESTS DURING THE PERIOD OF USE. IT IS IMPORTANT TO STUDY THE BEHAVIOR UNDER DIFFERENT AGING OF COMPOSITE MATERIALS OF POLYMERIC MATRIX REINFORCED WITH NATURAL FIBERS, RAISED AS POSSIBLE SUBSTITUTES FOR THE SYNTHETIC FIBERS USED. THE EPOXY COMPOSITES REINFORCED WITH STONEWARE FABRIC WERE EXPOSED AT HIGH TEMPERATURE (170 ° C), AT DIFFERENT TIMES 72, 120 AND 240 HOURS. THE SAMPLES WERE SUBMITTED TO BALLISTIC TESTS (CLASS I). IT WAS OBSERVED THAT TEMPERATURE IS AN IMPORTANT FACTOR THAT LEADS TO CHANGES IN THE PROPERTIES OF THE COMPOSITES, AS WELL AS THE MATRIX.

Palavras-chave

Envelhecimento; Alta temperatura; Fibras Naturais; Epóxi; Testes balísticos

Aging; High temperature; Natural fibers; Epoxy; Ballistic tests