COMPORTAMENTO DE MICROSEGREGAÇÃO DE C, MN, SI, P, S, TI E NIÓBIO EM REGIÕES DENDRÍTICAS E INTERDENDRÍTICAS DE ACORDO COM A PRÁTICA DE RESFRIAMENTO PARA LINGOTAMENTO CONTÍNUO DE  PLACAS: MICROSEGREGATION BEHAVIOUR OF C, MN, SI, P, S, TI AND NIOBIUM IN DENDRITIC AND INTERDENDRITIC REGIONS ACCORDING TO THE COOLING PRACTICE FOR SLAB CONTINUOUS CASTER

ESTE TRABALHO TEM COMO OBJETIVO DETERMINAR A INFLUêNCIA DOS PARâMETROS DE SOLIDIFICAçãO/RESFRIAMENTO NA MICROSEGREGAçãO DE PLACAS DE AçO HSLA+NB EM DIFERENTES POSIçõES. A MICROSEGREGAçãO é VISTA COMO UMA DAS FONTES MAIS IMPORTANTES DE VARIABILIDADE NAS PROPRIEDADES METALúRGICAS, ESPECIALMENTE TENACIDADE, E MEDIDAS QUE BUSCAM REDUZIR O BANDEAMENTO MICROESTRUTURAL E A PRECIPITAçãO PREFERENCIAL RESULTARãO EM MAIOR HOMOGENEIDADE MICROESTRUTURAL E MENOR VARIABILIDADE DE PROPRIEDADES. AS AMOSTRAS FORAM RETIRADAS EM POSIçõES AO LONGO DA LARGURA (CENTRO E -294MM EM RELAçãO AO CENTRO) E ESPESSURA DA PLACA (12,50, 37,50, 102,50 E 125,00MM). MICROANáLISE POR SONDA ELETRôNICA (EPMA), POR ESPECTROSCOPIA DE DISPERSãO DE COMPRIMENTO DE ONDA DE RAIOS-X (WDS), FOI REALIZADA PARA CARACTERIZAR QUANTITATIVAMENTE A MICROSEGREGAçãO DE DIVERSOS ELEMENTOS (C, MN, SI, P, S, NB E TI) NAS áREAS DENDRíTICAS E INTERDENDRíTICAS. FORAM REALIZADAS MEDIçõES SDAS (ESPAçAMENTO DO BRAçO DENDRíTICO SECUNDáRIO), QUE PERMITIRAM CALCULAR A TAXA DE RESFRIAMENTO, UTILIZANDO EQUAçõES PUBLICADAS, EM CADA POSIçãO. ESTE TRABALHO PERMITIU COMPREENDER DETALHADAMENTE O COMPORTAMENTO DOS DIFERENTES ELEMENTOS QUíMICOS EM DIFERENTES POSIçõES NUMA PLACA LINGOTADA, BEM COMO DETERMINAR A INFLUêNCIA DA TAXA DE RESFRIAMENTO NESTE COMPORTAMENTO. ESTE CONHECIMENTO PODE SER A BASE PARA OTIMIZAçõES DE PROCESSOS QUE VISAM REDUZIR A MICROSEGREGAçãO EM PRODUTOS ONDE A HOMOGENEIDADE MICROESTRUTURAL é UM FATOR CRíTICO DE QUALIDADE DO PRODUTO.

THIS WORK AIMS TO DETERMINE THE INFLUENCE OF SOLIDIFICATION/COOLING PARAMETERS ON THE MICROSEGREGATION OF HSLA+NB STEEL SLABS AT DIFFERENT POSITIONS. MICROSEGREGATION IS SEEN AS ONE OF THE MOST IMPORTANT SOURCES FOR VARIABILITY IN METALLURGICAL PROPERTIES, ESPECIALLY TOUGHNESS, AND MEASURES THAT SEEK TO REDUCE THE MICROSTRUCTURAL BANDING AND PREFERENTIAL PRECIPITATION WILL RESULT IN GREATER MICROSTRUCTURAL HOMOGENEITY AND LOWER PROPERTIES VARIABILITY. THE SAMPLES WERE TAKEN AT POSITIONS ALONG THE WIDTH (CENTER AND -294MM IN RELATION TO THE CENTER) AND THICKNESS OF THE SLAB (12.50, 37.50, 102.50 AND 125.00MM). ELECTRON PROBE MICROANALYSIS (EPMA) BY WAVELENGTH-DISPERSIVE X-RAY SPECTROSCOPY (WDS) WAS PERFORMED TO QUANTITATIVELY CHARACTERIZE THE MICROSEGREGATION OF SEVERAL ELEMENTS (C, MN, SI, P, S, NB AND TI) IN THE DENDRITIC AND IN INTERDENDRITIC AREAS. SDAS (SECONDARY DENDRITE ARM SPACING) MEASUREMENTS WERE CARRIED OUT, WHICH ALLOWED TO CALCULATE THE COOLING RATE, USING PUBLISHED EQUATIONS, IN EACH POSITION. THIS WORK ALLOWED TO UNDERSTAND IN DETAIL THE BEHAVIOR OF THE DIFFERENT CHEMICAL ELEMENTS IN DIFFERENT POSITIONS IN A CAST SLAB, AS WELL AS TO DETERMINE THE INFLUENCE OF THE COOLING RATE ON THIS BEHAVIOR. THIS KNOWLEDGE CAN BE THE BASIS FOR PROCESS OPTIMIZATIONS AIMED AT REDUCING MICROSEGREGATION IN PRODUCTS WHERE MICROSTRUCTURAL HOMOGENEITY IS A CRITICAL PRODUCT QUALITY FACTOR.

Palavras-chave

MICROSEGREGAÇÃO; EPMA; SDAS; arbl

Microsegregation; EPMA; SDAS; HSLA.

Como citar

OLIVEIRA, ALISSON PAULO DE; MELO, GILBERSON MENDONÇA STORCK DE; TENAGLIA, NICOLAS; MOOR, EMMANUEL DE; URANGA, PELLO. COMPORTAMENTO DE MICROSEGREGAÇÃO DE C, MN, SI, P, S, TI E NIÓBIO EM REGIÕES DENDRÍTICAS E INTERDENDRÍTICAS DE ACORDO COM A PRÁTICA DE RESFRIAMENTO PARA LINGOTAMENTO CONTÍNUO DE PLACAS , p. 166-178. In: 53º Seminário de Aciaria, Fundição e Metalurgia de Não-Ferrosos, São Paulo, Brasil, 2024.
ISSN: 2594-5300 , DOI 10.5151/2594-5300-40650