COMPORTAMENTO EM TRAÇÃO E ASPECTO FRACTOGRÁFICO DE MATRIZ POLIÉSTER COM PÓ DE AEROSIL

BEHAVIOR IN TENSION AND FRACTOGRAPHIC ASPECT OF POLYESTER MATRIX WITH AEROSIL POWDER

Autoria

Leite, Olívia Lopes; Ribeiro, Maurício Maia; Ferreira, Paulo Anderson Aranha; Matos, Taiana de Sousa; Monteiro, Sérgio Neves; Rios, Alisson Clay; Candido, Veronica Scarpini

DOI

10.5151/2594-5327-34948

Downloads

Baixar Artigo 9 Downloads

Resumo

A ADIÇÃO DE PARTICULADOS INORGÂNICOS COMO REFORÇO EM MATERIAIS COMPÓSITOS DE MATRIZ POLIMÉRICA TEM SIDO MOTIVO DE GRANDE INTERESSE TECNOLÓGICO, POIS CONDUZ A MELHORIAS NAS PROPRIEDADES E NO DESEMPENHO DOS MATERIAIS JÁ EXISTENTES, ALÉM DA POSSIBILIDADE DE REDUÇÃO DE IMPACTO AMBIENTAL E DE CUSTOS PARA A INDÚSTRIA. NESTE CONTEXTO, ESTE TRABALHO APRESENTA A CARACTERIZAÇÃO DO PÓ DE AEROSIL (MASSA ESPECÍFICA, TEOR DE UMIDADE E CARACTERIZAÇÃO MORFOLÓGICA) E O ESTUDO DO COMPORTAMENTO MECÂNICO EM TRAÇÃO CONFORME ASTM D 638:2010, DE COMPÓSITOS POLIMÉRICOS DE MATRIZ POLIÉSTER REFORÇADOS COM 0, 25 E 50% DE PÓ DE AEROSIL, BEM COMO AVALIAÇÃO DA SUPERFÍCIE FRATURA APÓS ENSAIO. EM RELAÇÃO À MORFOLOGIA, O PÓ DE AEROSIL MOSTROU-SE HOMOGÊNEO. APESAR DA POROSIDADE APRESENTADA PELOS COMPÓSITOS A MEDIDA EM QUE SE AUMENTOU A PROPORÇÃO DE AEROSIL NA MATRIZ, OS VALORES OBTIDOS APÓS O ENSAIO DE TRAÇÃO DEMONSTRARAM QUE PARA TAIS PORCENTAGENS O PÓ DE AEROSIL PODE SER UTILIZADO COMO REFORÇO EM MATRIZ POLIÉSTER MELHORANDO SIGNIFICATIVAMENTE AS PROPRIEDADES EM TRAÇÃO DO MATERIAL.

 

THE ADDITION OF INORGANIC PARTICULATES AS REINFORCEMENT IN POLYMER MATRIX COMPOSITE MATERIALS HAS BEEN A MATTER OF GREAT TECHNOLOGICAL INTEREST, AS IT LEADS TO IMPROVEMENTS IN THE PROPERTIES AND PERFORMANCE OF EXISTING MATERIALS, IN ADDITION TO THE POSSIBILITY OF REDUCING ENVIRONMENTAL IMPACT AND COSTS FOR THE INDUSTRY. IN THIS CONTEXT, THIS WORK PRESENTS THE CHARACTERIZATION OF AEROSIL POWDER (SPECIFIC MASS, MOISTURE CONTENT AND MORPHOLOGICAL CHARACTERIZATION) AND THE STUDY OF THE MECHANICAL BEHAVIOR IN TENSION ACCORDING TO ASTM D 638:2010, OF POLYMERIC COMPOSITES OF POLYESTER MATRIX REINFORCED WITH 0, 25 AND 50% AEROSIL POWDER, AS WELL AS EVALUATION OF THE FRACTURE SURFACE AFTER TESTING. REGARDING MORPHOLOGY, THE AEROSIL POWDER WAS HOMOGENEOUS. DESPITE THE POROSITY PRESENTED BY THE COMPOSITES AS THE PROPORTION OF AEROSIL IN THE MATRIX INCREASED, THE VALUES OBTAINED AFTER THE TENSILE TEST SHOWED THAT FOR SUCH PERCENTAGES THE AEROSIL POWDER CAN BE USED AS A REINFORCEMENT IN POLYESTER MATRIX, SIGNIFICANTLY IMPROVING THE TENSILE PROPERTIES OF MATERIAL

Palavras-chave

Materiais compósitos; Pó de aerosil; Matriz poliéster; Comportamento Mecânico.

Composite materials; aerosil powder; Polyester matrix; Mechanical Behavior.