Título

COMPORTAMENTO EM TRAÇÃO E ASPECTO FRACTOGRÁFICO DO COMPÓSITO HÍBRIDO COM FIBRAS DE SISAL E PARTICULADO DE MARUPÁ

BEHAVIOR IN TENSION AND ASPECT FRACTOGRAPHY OF HYBRID COMPOSITE WITH SISAL FIBERS AND MARUPÁ PARTICULATE

Autoria

Nascimento, Damares da Cruz Barbosa; Ribeiro, Maurício Maia; Fujiyama, Roberto Tetsuo; Rodrigues, Jean da Silva; Silva, Alisson Clay Rios da; Monteiro, Sérgio Neves; Candido, Verônica Scarpini

DOI

10.5151/2594-5327-34980

Downloads

Baixar Artigo 7 Downloads

Resumo

OS MATERIAIS COMPÓSITOS APRESENTAM GRANDE INTERESSES NAS DEMAIS ÁREAS DAS CIÊNCIAS, DEVIDO AO VASTO CAMPO DE APLICABILIDADE E TRABALHABILIDADE. NESSE SENTIDO, AS FIBRAS NATURAIS E RESÍDUOS INDUSTRIAIS SÃO MATÉRIAS PRIMAS COM BOM DESEMPENHO PARA PRODUÇÃO DE UM MATERIAL COMPÓSITO. ASSIM, OBJETIVO DESTE ESTUDO É AVALIAR O COMPORTAMENTO MECÂNICO E MORFOLÓGICO, APÓS O ENSAIO TRAÇÃO DE ACORDO COM A NORMA ASTM D638, DE UM COMPÓSITO HÍBRIDO DE 25/25% DE FIBRA DE SISAL 15 MM E PARTICULADO DE MARUPÁ EM MATRIZ POLIÉSTER, COM AGENTE DE CURA DE 0,33%. POSTERIORMENTE, CARACTERIZAR AS MATÉRIAS PRIMAS POR MICROSCOPIA ELETRÔNICA DE VARREDURA E CARACTERIZAR MORFOLOGICAMENTE O COMPÓSITO HÍBRIDO APÓS O ENSAIO DE TRAÇÃO. OS RESULTADOS PARA MORFOLOGIA DA FIBRA DE SISAL INDICARAM UMA GEOMETRIA REGULAR, COM AUSÊNCIAS DE CAMADAS. JÁ O PARTICULADO DE MARUPÁ, DESTACOU UMA MORFOLOGIA MAIS IRREGULAR, HETEROGÊNEA. OS RESULTADOS PARA O COMPÓSITO HIBRIDO DESTACOU A RESISTÊNCIA A TRAÇÃO DE 25,70 MPA, CERCA DE 30% DE REDUÇÃO COMPARADO A MATRIZ PURA DE 36,74 MPA. O ASPECTO FRACTOGRÁFICO REVELOU A PRESENÇA DE PULL OUT, ARRANCHAMENTO DA FIBRA E PRESENÇA DE PARTÍCULAS DA MADEIRA. POR FIM, O COMPÓSITO OBTEVE BOM RENDIMENTO EM RELAÇÃO AOS DEMAIS COMPÓSITOS ESTUDADOS, PODENDO APRESENTAR–SE COMO UM MATERIAL DE BOM DESEMPENHO.

 

COMPOSITE MATERIALS ARE OF GREAT INTEREST IN OTHER AREAS OF SCIENCE, DUE TO THE VAST FIELD OF APPLICABILITY AND WORKABILITY. IN THIS SENSE, NATURAL FIBERS AND INDUSTRIAL WASTE ARE RAW MATERIALS WITH GOOD PERFORMANCE FOR THE PRODUCTION OF A COMPOSITE MATERIAL. THUS, THE OBJECTIVE OF THIS STUDY IS TO EVALUATE THE MECHANICAL AND MORPHOLOGICAL BEHAVIOR, AFTER THE TENSILE TEST ACCORDING TO ASTM D638, OF A HYBRID COMPOSITE OF 25/25% OF 15 MM SISAL FIBER AND MARUPá PARTICULATE IN POLYESTER MATRIX, WITH CURE RATE OF 0.33%. SUBSEQUENTLY, CHARACTERIZE THE RAW MATERIALS BY SCANNING ELECTRON MICROSCOPY AND MORPHOLOGICALLY CHARACTERIZE THE HYBRID COMPOSITE AFTER THE TENSILE TEST. THE RESULTS FOR SISAL FIBER MORPHOLOGY INDICATED A REGULAR GEOMETRY, WITH ABSENCE OF LAYERS. THE MARUPá PARTICULATE, ON THE OTHER HAND, HIGHLIGHTED A MORE IRREGULAR, HETEROGENEOUS MORPHOLOGY. THE RESULTS FOR THE HYBRID COMPOSITE HIGHLIGHTED THE TENSILE STRENGTH OF 25.70 MPA, ABOUT 30% REDUCTION COMPARED TO THE PURE MATRIX OF 50.24 MPA. THE FRACTOGRAPHIC APPEARANCE REVEALED THE PRESENCE OF PULL OUT, FIBER SCRATCHING AND THE PRESENCE OF WOOD PARTICLES. FINALLY, THE COMPOSITE OBTAINED GOOD PERFORMANCE IN RELATION TO THE OTHER COMPOSITES STUDIED, BEING ABLE TO PRESENT ITSELF AS A MATERIAL WITH GOOD PERFORMANCE.

Palavras-chave

Fibras de Sisal; Compósitos; Resíduo de Marupá; Caracterização

BEHAVIOR IN TENSION AND ASPECT FRACTOGRAPHY OF HYBRID COMPOSITE WITH SISAL FIBERS AND MARUPÁ PARTICU