COMPORTAMENTO EM TRAÇÃO E ASPECTO FRACTOGRÁFICO DO COMPÓSTO HIBRIDO COM FIBRAS DE JUTA E PARTICULADO DE MARUPÁ

BEHAVIOR IN TRACTION AND FRACTOGRAPHIC APPEARANCE OF THE HYBRID COMPOUND WITH JUTE FIBERS AND MARUPÁ POWER

Autoria

Nascimento, Damares da Cruz Barbosa; Ribeiro, Maurício Maia; Fujiyama, Roberto Tetsuo; Rodrigues, Jean da Silva; Silva, Alisson Clay Rios da; Monteiro, Sérgio Neves; Candido, Verônica Scarpini

DOI

10.5151/2594-5327-34986

Downloads

Baixar Artigo 5 Downloads

Resumo

OS COMPÓSITOS SÃO MATERIAIS IMPORTANTES PARA O DESENVOLVIMENTO DE NOVOS PRODUTOS PARA DETERMINADAS APLICAÇÕES. ESSES MATERIAIS SÃO COMPOSTOS POR FASES/MICROCONSTITUINTE, QUE DETERMINAM AS PROPRIEDADES E CARACTERÍSTICAS DO PRODUTO FINAL. A FIBRA NATURAL DE JUTA POSSUI BOAS PROPRIEDADES MECÂNICAS, RESISTÊNCIA E É UM REFORÇO RENOVÁVEL, BIODEGRADÁVEL E ECONOMICAMENTE VIÁVEL. JÁ OS RESÍDUOS DE MADEIRA, POR SUA VEZ, CONSTITUEM UM BOM REFORÇO A MATRIZ, ADERINDO-SE DE FORMA EXPONENCIAL. DIANTE DISTO, OBJETIVO DESTE ESTUDO É AVALIAR AS PROPRIEDADES DE TRAÇÃO DE UM COMPÓSITO HÍBRIDO DE 25/25% DE FIBRA NATURAL DE JUTA E RESÍDUOS DE MADEIRA DE MARUPÁ, EM MATRIZ POLIÉSTER METIL – ETIL – CETONA DE 0,33% (V/V). POSTERIORMENTE, O COMPÓSITO HIBRIDO FOI SUBMETIDO A ENSAIO DE TRAÇÃO, SEGUNDO A NORMA ASTM D638, E ANÁLISE FRACTOGRÁFICA POR MICROSCOPIA ELETRÔNICA DE VARREDURA. COM ISSO, OS RESULTADOS MOSTRARAM QUE O COMPÓSITO APRESENTOU UMA RESISTÊNCIA A TRAÇÃO MÉDIA IGUAL A 25,13 MPA, COM APENAS 31,54% DE REDUÇÃO QUANDO COMPARA A RESISTÊNCIA DA MATRIZ PURA. O ASPECTO FRACTROGRÁFICO MOSTROU A PRESENÇA DE POROSIDADE NO MATERIAL E PULL OUT. SENDO ASSIM, EM FUNÇÃO DAS CARACTERÍSTICAS CITADAS, O COMPÓSITO HÍBRIDO APRESENTOU UM BOM DESEMPENHO, COMPARADO A MATRIZ PURA.

 

COMPOSITES ARE IMPORTANT MATERIALS FOR THE DEVELOPMENT OF NEW PRODUCTS FOR CERTAIN APPLICATIONS. THESE MATERIALS ARE COMPOSED OF PHASES/MICROCONSTITUENT, WHICH DETERMINE THE PROPERTIES AND CHARACTERISTICS OF THE FINAL PRODUCT. NATURAL JUTE FIBER HAS GOOD MECHANICAL PROPERTIES, STRENGTH AND IS A RENEWABLE, BIODEGRADABLE AND ECONOMICALLY VIABLE REINFORCEMENT. ON THE OTHER HAND, WOOD RESIDUES, IN TURN, CONSTITUTE A GOOD REINFORCEMENT TO THE MATRIX, ADHERING EXPONENTIALLY. THEREFORE, THE OBJECTIVE OF THIS STUDY IS TO EVALUATE THE TENSILE PROPERTIES OF A HYBRID COMPOSITE OF 25/25% OF NATURAL JUTE FIBER AND MARUPá WOOD RESIDUES, IN A POLYESTER MATRIX METHYL - ETHYL - KETONE OF 0.33% (V/V ). SUBSEQUENTLY, THE HYBRID COMPOSITE WAS SUBJECTED TO TENSILE TESTING, ACCORDING TO ASTM D638, AND FRACTOGRAPHIC ANALYSIS BY SCANNING ELECTRON MICROSCOPY. THUS, THE RESULTS SHOWED THAT THE COMPOSITE PRESENTED AN AVERAGE TENSILE STRENGTH EQUAL TO 25.13 MPA, WITH ONLY 31.54% REDUCTION WHEN COMPARING THE STRENGTH OF THE PURE MATRIX. THE FRACTROGRAPHIC ASPECT SHOWED THE PRESENCE OF POROSITY IN THE MATERIAL AND PULL OUT. THUS, IN FUNCTION OF THE MENTIONED CHARACTERISTICS, THE HYBRID COMPOSITE PRESENTED A GOOD PERFORMANCE, COMPARED TO THE PURE MATRIX.

Palavras-chave

Compósitos; Fibras de Juta; Resíduo de Marupá; Ensaio de Tração.

Composites; Jute fibers; Marupá residue; Tensile Test.