COMPORTAMENTO TRIBOLÓGICO DE REVESTIMENTOS DEPOSITADOS POR ASPERSÃO TÉRMICA (HVOF) COMO ALTERNATIVA AO CROMO ELETRODEPOSITADO

TRIBOLOGICAL BEHAVIOR OF THERMAL COATINGS SPRAYED BY HVOF AS ALTERNATIVE TO CHROMIUM ELECTROPLATED

DOI

10.5151/1516-392X-24400

Downloads

Baixar Artigo 562 Downloads

Resumo

A utilização de revestimentos a base de cromo eletrolítico traz prejuízos ao meio ambiente, uma vez que durante o processo são liberados íons de cromo hexavalente e estes são extremamente tóxicos à natureza e ao homem. No entanto, existem outras tecnologias que vem sendo estudadas como alternativas ao processo tradicional de cromagem. A aspersão térmica por oxi-combustível de alta velocidade (HVOF) é a técnica que tem apresentado os melhores resultados sob as óticas de qualidade de revestimento, porosidade, resistência ao desgaste, propriedades mecânicas e adesivas. Neste trabalho foi realizado um estudo comparativo da eficácia da técnica de HVOF em termos de adesão, resistência ao desgaste e coeficiente de atrito. Como substrato foi utilizado o aço SAE 4140; o revestimento utilizado na aspersão por HVOF foi o WC-Co-Cr em comparação como o cromo eletroliticamente depositado, todos com a mesma espessura de camada. A avaliação tribológica foi realizada através de ensaios de desgaste por deslizamento do tipo pino sobre disco e a resistência adesiva por meio de ensaio de adesão.

 

The use of coatings based in electrolytic chromium deposition causes damages to the environment, since during the process, hexavalent chromium ions are released and these are extremely toxic to nature and man. However, other technologies have been studied as alternatives to the traditional chromium electroplating process. The thermal spray high velocity oxy-fuel (HVOF) is a technique that has shown the best results considering coating quality, porosity, wear resistance, mechanical and adhesive properties. In this paper, a comparative study of HVOF efficacy was realized in terms of adhesion, wear resistance and friction coefficient. The substrate used was the SAE 4140; the spray coating WC-Co-Cr was applied by HVOF and compared with chromium electroplated, all coatings had the same layer thicknesses. The tribological evaluation was performed by sliding wear testing type pin on disc and the bond strength by adhesion test.

Palavras-chave

Aspersão térmica; HVOF; Desgaste; Adesão

Thermal spray coatings; HVOF; Wear; Adhesion

Como citar

Matheus Machado de Souza; Filipi Flor Teixeira; César Edil da Costa; Júlio César Giubilei Milan. COMPORTAMENTO TRIBOLÓGICO DE REVESTIMENTOS DEPOSITADOS POR ASPERSÃO TÉRMICA (HVOF) COMO ALTERNATIVA AO CROMO ELETRODEPOSITADO , p. 6510-6521. In: 69° Congresso Anual da ABM - Internacional, São Paulo - Brasil, 2014.