Título

COMPORTAMENTO TÉRMICO DE NANOCOMPÓSITOS DE POLIETILENO DE ALTA DENSIDADE REFORÇADOS COM TECIDOS DE JUTA E ARAMIDA, E NANOPLAQUETAS DE GRAFITE

CHARACTERIZATION OF HYBRID JUTE AND ARAMID REINFORCING GRAPHITE NANOPLATELETS IN HIGH-DENSITY POLYETHYLENE NANOCOMPOSITES

Autoria

OLIVEIRA, LIVIA VIANA AGUIAR DE; COSTA, ULISSES OLIVEIRA; MONTEIRO, SERGIO NEVES

OLIVEIRA, LIVIA VIANA AGUIAR DE

Eu sou esse autor

COSTA, ULISSES OLIVEIRA

Eu sou esse autor

MONTEIRO, SERGIO NEVES

Eu sou esse autor

DOI

10.5151/2594-4711-41009

Downloads

Resumo

AS FIBRAS NATURAIS LIGNOCELULóSICAS SãO AMPLAMENTE UTILIZADAS PARA FABRICAçãO DE ARTEFATOS ARTESANAIS. NO ENTANTO, COM BASE NAS SUAS INúMERAS VANTAGENS E POTENCIAIS DE APLICAçõES ESSAS TêM GANHADO CADA VEZ MAIS NOTORIEDADE EM SE TRATANDO DE COMPóSITOS PARA APLICAçõES DE ENGENHARIA. ESTE ESTUDO INVESTIGA O DESENVOLVIMENTO DE NANOCOMPóSITOS HíBRIDOS, QUE EMPREGAM UMA MATRIZ DE POLIETILENO DE ALTA DENSIDADE MODIFICADA COM NANOPLAQUETAS DE GRAFITE E REFORçADA POR TECIDOS DE ARAMIDA E JUTA. A ANáLISE BASEADA NOS RESULTADOS DE CALORIMETRIA DIFERENCIAL DE VARREDURA (DSC) E ANáLISE DINâMICO-MECâNICA (DMA) REVELA QUE AS NANOPLAQUETAS DE GRAFITE DESEMPENHAM UM PAPEL CRUCIAL NA MODIFICAçãO DAS TEMPERATURAS DE CRISTALIZAçãO E TRANSIçãO VíTREA (TC E TG), INFLUENCIANDO O COMPORTAMENTO MECâNICO DINâMICO. ESPECIFICAMENTE, ESSAS NANOPLAQUETAS AUMENTAM A RIGIDEZ VISCOELáSTICA, ELEVAM O MóDULO DE ARMAZENAMENTO (E’) EM MAIS DE 30% E REDUZEM O VALOR DE TANδ.

HYBRID NANOCOMPOSITES HAVE EMERGED AS A PROMISING SOLUTION FOR ENGINEERING APPLICATIONS ASSOCIATED WITH COST AND WEIGHT REDUCTION, AIMING TO ENHANCE PERFORMANCE IN HIGH-TECH AREAS. THIS STUDY DELVES INTO THE DEVELOPMENT OF HYBRID NANOCOMPOSITES FEATURING A HIGH-DENSITY POLYETHYLENE MATRIX MODIFIED WITH GRAPHITE NANOPLATELETS AND REINFORCED BY ARAMID AND JUTE FABRICS. BASED ON THE RESULTS OF DIFFERENTIAL SCANNING CALORIMETRY (DSC) AS WELL AS DYNAMIC MECHANICAL ANALYSIS (DMA), GRAPHITE NANOPLATELETS PLAY AN IMPORTANT ROLE IN MODIFYING THE CRYSTALLIZATION AND GLASS TRANSITION TEMPERATURES (TC AND TG) AND INFLUENCING DYNAMIC MECHANICAL BEHAVIOR. SPECIFICALLY, THEY INCREASE VISCOELASTIC STIFFNESS, RAISE THE STORAGE MODULUS (E’) BY MORE THAN 30%, AND REDUCE THE TANδ VALUE.

Palavras-chave

Juta; Aramida; Nanoplacas de grafite; Polietileno de alta densidade; Nanocompósito híbrido

Jute; Aramid; Graphite nanoplatelet; High-density polyethylene; Hybrid nanocomposite.