COMPÓSITO DE FIBRA DE SISAL ALINHADO 0° UNIDIRECIONAL: COMPARAÇÃO DA TENSÃO MÁXIMA EXPERIMENTAL E TEÓRICA

COMPOSITE SISAL FIBER ALIGNED 0° UNIDIRECTIONAL: COMPARISON OF EXPERIMENTAL AND MAXIMUM STRESS TEÓRICA

Autoria

Carvalho, Michel José Caldas; Fujiyama, Roberto Tetsuo

Carvalho, Michel José Caldas

Eu sou esse autor

Fujiyama, Roberto Tetsuo

Eu sou esse autor

DOI

10.5151/2594-5327-20934

Downloads

Resumo

As fibras naturais como sisal, juta, curauá possuem comprimentos que possibilitam a confecção de corpos de prova alinhados. As fibras de sisal variam de 700 mm a 1.100 mm tornando possível a fabricação de compósitos contínua e alinhada. Esse trabalho busca avaliar a resistência mecânica de um laminado compósito de fibra natural de sisal alinhado 0° unidirecional, fazendo uma comparação na tensão obtida com dados experimentais através da máquina de ensaio universal EMIC com os dados teóricos aplicando a regra da mistura. A metodologia para a confecção das placas usou pouco maquinário ou tecnologia, sendo usado lâminas de vidro e fitas dupla-face para que as fibras mantivessem o alinhamento e fosse possível a fabricação dos mesmos. Os resultados foram satisfatórios e dentro do esperado para esse tipo de orientação e fibra, obtendo uma tensão máxima de 66,91 MPa. Os dados experimentais normalmente diferem dos teóricos e uma das propostas desse trabalho é avaliar as possíveis possibilidades de fatores que influenciam para esta diferenciação.

Natural fibers as sisal, jute, curauá have lengths that allow the preparation of specimens aligned. The sisal fiber presents length that varies 700 mm to 1.100 mm making possible the construction of composites with a length that fit the specific dimensions set out in standards such as ASTM D3039M. This study sought to determine the strength of a composite fiber of natural sisal 0° aligned unidirectional laminates, with a comparison stress obtained from experimental data by a universal testing machine EMIC theoretical data with the applying the mixture rule. The methodology used for the manufacture of these laminates was rudimentary, which fits into the proposed use of no machinery or technology in obtaining these composite materials, at the time was used glass slides and double-sided tape to keep the fiber alignment and it was possible to manufacture them. The results were satisfactory and as expected for this type of fiber orientation and, obtaining a maximum stress of 66.91 MPa. The experimental data usually differ from the theoretical and the proposal of this paper is to evaluate the potential possibilities of influencing factors for this differentiation.

Palavras-chave

Fibras naturais; Ensaio de tração; Sisal; Regra das misturas.

Natural fibers; Tensile test; Sisal; Rule of mixtures.