COMPÓSITOS DE PIAÇAVA COM RESINA NATURAL PARA FABRICAÇÃO DE REVESTIMENTO DE ALTO DESEMPENHO

PIAÇAVA COMPOSITES WITH NATURAL RESIN FOR THE PRODUCTION OF HIGH PERFORMANCE COATINGS

Autoria

Carvalho, Juliana Peixoto Rufino Gazem de; Ribeiro, Amanda Mendes; Lopes, Felipe Perisse Duarte; Simonassi, Noan Tonini; Carvalho, Eduardo Atem de; Vieira, Carlos Maurício Fontes

DOI

10.5151/2594-5327-34179

Downloads

Baixar Artigo 8 Downloads

Resumo

OS REVESTIMENTOS DE ALTO DESEMPENHO (RAD) SÃO PISOS QUE PROTEGEM SUBSTRATOS EM DIVERSOS TIPOS DE INDÚSTRIAS BRASILEIRAS. SUA UTILIZAÇÃO FAZ-SE NECESSÁRIA DEVIDO AOS DIVERSOS BENEFÍCIOS COMO RAPIDEZ DE APLICAÇÃO, ALTO DESEMPENHO MECÂNICO E AUSÊNCIA DE JUNTAS DE DILATAÇÃO. PORÉM, A NORMA BRASILEIRA FAZ MENÇÃO À FABRICAÇÃO COM RESINAS EPOXÍDICAS, DE ORIGEM SINTÉTICA, E AGREGADOS MINERAIS. LOGO, ESTE TRABALHO VISOU O ESTUDO DO DESEMPENHO MECÂNICO DESTE MATERIAL UTILIZANDO UMA RESINA POLIURETANA VEGETAL E, COMO AGREGADO, FIBRA DE PIAÇAVA MOÍDA NO MOINHO DE FACAS. A FIBRA UTILIZADA FOI OBTIDA COMO UM SUBPRODUTO INDUSTRIAL DE UMA FÁBRICA DE VASSOURAS LOCALIZADA EM CAMPOS DOS GOYTACAZES-RJ. A METODOLOGIA DA PESQUISA CONSISTIU, INICIALMENTE, NA DETERMINAÇÃO DA DENSIDADE DAS FIBRAS COLETADAS, COMO RESÍDUO, ATRAVÉS DA TÉCNICA DE PICNOMETRIA. BEM COMO A ANÁLISE MORFOLÓGICA POR MICROSCOPIA ELETRÔNICA DE VARREDURA (MEV). POSTERIORMENTE, FORAM REALIZADOS OS ENSAIOS DE ABSORÇÃO DE ÁGUA APÓS FERVURA, RESISTÊNCIA À COMPRESSÃO E ANÁLISE DA FRATURA ATRAVÉS DE MEV. OS RESULTADOS MOSTRARAM A EFICÁCIA DA UTILIZAÇÃO DE 20% DE FIBRA QUE POSSIBILITA A APLICAÇÃO DESTA COMPOSIÇÃO PARA A FORMULAÇÃO E UTILIZAÇÃO EM RAD.

 

HIGH PERFORMANCE COATINGS (HPC) ARE FLOORS THAT PROTECT SUBSTRATES IN SEVERAL TYPES OF BRAZILIAN INDUSTRIES. ITS USE IS NECESSARY DUE TO SEVERAL BENEFITS SUCH AS SPEED OF APPLICATION, HIGH MECHANICAL PERFORMANCE AND ABSENCE OF EXPANSION JOINTS. HOWEVER, THE BRAZILIAN STANDARD MENTIONS MANUFACTURING WITH EPOXY RESINS, OF SYNTHETIC ORIGIN, AND MINERAL AGGREGATES. THEREFORE, THIS WORK AIMED TO STUDY THE MECHANICAL PERFORMANCE OF THIS MATERIAL USING A VEGETABLE POLYURETHANE RESIN AND, AS AN AGGREGATE, PIASSAVA FIBER GROUND IN THE KNIFE MILL. THE FIBER USED WAS OBTAINED AS AN INDUSTRIAL BY-PRODUCT OF A BROOM FACTORY LOCATED IN CAMPOS DOS GOYTACAZES-RJ. THE RESEARCH METHODOLOGY CONSISTED, INITIALLY, IN THE DETERMINATION OF THE DENSITY OF THE FIBERS COLLECTED AS WASTE THROUGH THE PYCNOMETRY TECHNIQUE, AS WELL AS THE MORPHOLOGICAL ANALYSIS THROUGH SCANNING ELECTRON MICROSCOPY (SEM). SUBSEQUENTLY, WATER ABSORPTION TESTS WERE CARRIED OUT AFTER BOILING, COMPRESSIVE STRENGTH AND FRACTURE ANALYSIS USING SEM. THE RESULTS SHOWED THE EFFICIENCY OF USING 20% FIBER THAT MAKES IT POSSIBLE TO APPLY THIS COMPOSITION FOR FORMULATION AND USE IN RAD.

Palavras-chave

Poliuretano Vegetal; Óleo de Mamona; Piaçava; Materiais Compósitos; Fibras Naturais; Compósitos Ecoa

Castor Oil Polyurethane; Piassava; Composite Materials; Natural Fibers; Eco-friendly Composites.