COMPÓSITOS DE RESINA POLIÉSTER INCORPORADA COM FIBRA DE SISAL – PROPRIEDADES MECÂNICAS E CARACTERISTICAS DE FRATURA

SISAL FIBER INCORPORATED POLYESTER MATRIX COMPOSITES – MECHANICAL PROPERTIES AND FRACTURE CHARACTERISTICS

Autoria

Inácio, Wellington Pereira; Monteiro, Sergio Neves; Lopes, Felipe Perissé Duarte

DOI

10.5151/2594-5327-14768

Downloads

Baixar Artigo 65 Downloads

Resumo

O comportamento mecânico de compósitos poliméricos reforçados com fibras alinhadas de sisal ainda não foi havia sido estudado para a matriz poliéster. O objetivo deste trabalho foi investigar as propriedades mecânicas e as características da fratura de compósitos com matriz poliéster incorporada com até 35% de fibras de sisal. Fibras de sisal, comercialmente obtidas, foram colocadas de maneira alinhada, ao longo de um molde utilizado para a fabricação de compósitos juntamente com resina poliéster ortoftálica misturada ao endurecedor metil-etil-cetona. Após cura a 25°C por um dia, corpos de prova de flexão foram ensaiados até a ruptura. A superfície de fratura foi analisada por microscopia eletrônica de varredura. Obteve- se um aumento na resistência à flexão dos compósitos até a fração incorporada de 15% em volume de fibras de sisal. A partir deste ponto, a resistência apresentou uma queda contínua. Este efeito de reforço nos compósitos pôde ser interpretado através da observação do processo de interação fibra/matriz durante a propagação das trincas na fratura.

 

The mechanical behavior of polymeric composites reinforced with sisal fibers has not yet been studied for polyester matrix. The objective of this work was to investigate the mechanical properties and fracture characteristics of polyester matrix composites incorporated with up to 35% in volume of sisal fibers. Sisal fibers, commercially available, were aligned in a mold used for the manufacture of composite with ortophtalic polyester resin mixed with methyl-ethyl-ketone hardener. After curing at 25°C for one day, bend specimens were tested until rupture. The fracture surface was examined by scanning electron microscopy. An increase in the flexural resistance of composites with up to 15% of sisal fibers was obtained. With greater amounts of sisal fiber, a continuous decrease was found for the composite strength. This effect of strengthening in the composites was interpreted through the observation of the fiber/matrix interaction during cracks propagation in the fracture.

Palavras-chave

Fibra de sisal; Compósito polimérico; Ensaio de flexão; Características da fratura.

Sisal fiber; Polymer composites; Bending test; Fracture characteristics.