COMPÓSITOS POLIMÉRICOS REFORÇADOS COM FIBRAS MOÍDAS DE COCO PARA APLICAÇÃO EM REVESTIMENTO PARA PISO

POLYMERIC COMPOSITES REINFORCED WITH GROUND COCONUT FIBERS FOR APPLICATION IN FLOOR COATING

Autoria

Carvalho, Juliana Peixoto Rufino Gazem de; Azevedo, Jessika Rogério de; Lopes, Felipe Perisse Duarte; Simonassi, Noan Tonini; Vieira, Carlos Maurício Fontes

DOI

10.5151/2594-5327-34195

Downloads

Baixar Artigo 85 Downloads

Resumo

O OBJETIVO DESTE TRABALHO É IDENTIFICAR A INFLUÊNCIA DA FIBRA DE COCO E DO USO DE RESINA POLIURETANA DERIVADA DE ÓLEO DE MAMONA (PUOM) NAS PROPRIEDADES MECÂNICAS DE COMPÓSITOS DESTINADOS À APLICAÇÃO COMO REVESTIMENTO DE ALTO DESEMPENHO (RAD). ALÉM DISSO, PARALELAMENTE, BUSCOU-SE ANALISAR A MESMA FIBRA EM MATRIZ EPÓXI. INICIALMENTE, FOI DETERMINADA A DENSIDADE DA FIBRA PELO MÉTODO DE ARQUIMEDES. EM SEGUIDA, FORAM CONFECCIONADOS CORPOS DE PROVA DE 0%, 5%, 10% E 15% EM FIBRA COM MATRIZES DE PUOM E EPÓXI. AS AMOSTRAS FORAM FEITAS DE ACORDO COM A NORMA NBR14050, QUE ESPECIFICA REQUISITOS PARA O RAD. POSTERIORMENTE, FORAM REALIZADOS TESTES DE RESISTÊNCIA À COMPRESSÃO E ABSORÇÃO DE ÁGUA NOS COMPÓSITOS. POR FIM, AS SUPERFÍCIES DE FRATURA FORAM ANALISADAS UTILIZANDO O MICROSCÓPIO ELETRÔNICO DE VARREDURA (MEV). COMO RESULTADO OBTEVE-SE QUE OS COMPÓSITOS FORMULADOS COM PUOM E OS DE MATRIZ EPÓXI COM FIBRA NÃO ATINGIRAM O REQUISITO MÍNIMO DE 45MPA. ESTE DESEMPENHO FOI ATRIBUÍDO À UTILIZAÇÃO DE MATRIZ ABERTA (SEM PRESSÃO) E AUSÊNCIA DE TRATAMENTO PRÉVIO NA FIBRA, FATORES QUE PREJUDICARAM A ADESÃO INTERFACIAL.

 

THE OBJECTIVE OF THIS WORK IS TO IDENTIFY THE INFLUENCE OF COCONUT FIBER AND THE USE OF CASTOR OIL-DERIVED POLYURETHANE RESIN (PUOM) ON THE MECHANICAL PROPERTIES OF COMPOSITES FOR HIGH PERFORMANCE COATING (HPC). IN ADDITION, IN PARALLEL, THE SAME FIBER WAS ANALYZED IN AN EPOXY MATRIX. INITIALLY, THE FIBER DENSITY WAS DETERMINED USING THE ARCHIMEDES METHOD. THEN, 0%, 5%, 10% AND 15% SPECIMENS WERE MADE OF FIBER WITH PUOM AND EPOXY MATRICES. THE SAMPLES WERE MADE IN ACCORDANCE WITH THE NBR14050 STANDARD, WHICH SPECIFIES REQUIREMENTS FOR THE HPC. SUBSEQUENTLY, COMPRESSIVE STRENGTH AND WATER ABSORPTION TESTS WERE PERFORMED ON THE COMPOSITES. FINALLY, THE FRACTURE SURFACES WERE ANALYZED USING THE SCANNING ELECTRON MICROSCOPE (SEM). AS A RESULT, IT WAS FOUND THAT COMPOSITES FORMULATED WITH PUOM AND THOSE WITH EPOXY MATRIX WITH FIBER DID NOT MEET THE MINIMUM REQUIREMENT OF 45MPA. THIS PERFORMANCE WAS ATTRIBUTED TO THE USE OF AN OPEN MATRIX (WITHOUT PRESSURE) AND THE ABSENCE OF PREVIOUS TREATMENT IN THE FIBER, FACTORS THAT IMPAIRED INTERFACIAL ADHESION.

Palavras-chave

Fibra de coco; Resina de Poliuretano; Fibra natural; Materiais compósitos.

Coconut fiber; Polyurethane resin; Natural fiber; Composite materials