COMPUTATIONAL THERMODYNAMIC SIMULATION OF ADDITIONS TO LOW-CARBON ALUMINUM KILLED (LCAK) STEEL DURING TAPPING FROM THE CONVERTER – INITIAL MODELING STEPS: COMPUTATIONAL THERMODYNAMIC SIMULATION OF ADDITIONS TO LOW-CARBON ALUMINUM KILLED (LCAK) STEEL DURING TAPPING FROM THE CONVERTER – INITIAL MODELING STEPS

O VAZAMENTO DO AçO DO CONVERSOR PARA A PANELA PROMOVE FORTE AGITAçãO. ESTA AGITAçãO é, Há MUITOS ANOS, APROVEITADA DE DIFERENTES FORMAS PARA TORNAR O PROCESSO DE PRODUçãO, NA ACIARIA, MAIS RáPIDO E EFICIENTE E VIABILIZAR A PRODUçãO DE AçOS BEM DESOXIDADOS E DE ELEVADA LIMPEZA INTERNA. NESTE TRABALHO, UM MODELO CINéTICO DO TIPO ACOPLADO A UM SOFTWARE DE TERMODINâMICA COMPUTACIONAL é EMPREGADO PARA AVLAIAR DIVERSAS OPçõES DE ADIçõES, NA PRODUçãO DE AçO DE BAIXO CARBONO PARA ESTAMPAGEM. SãO AVALIADOS OS EFEITOS DA ADIçãO DE DIFERENTES QUANTIDADES DE DESOXIDANTES E FORMADORES DE ESCóRIA SOBRE A EFICIêNCIA DA DESOXIDAçãO E SOBRE A CAPACIDADE DE PRODUZIR UMA ESCóRIA DE PANELA ADEQUADA PARA O PROCESSAMENTO POSTERIOR. SãO AVALIADAS, TAMBéM, DIFERENTES CONDIçõES DE VAZAMENTO. PARA ISTO, DADOS CINéTICOS ANTERIORMENTE OBTIDOS SãO EMPREGADOS, EM CONJUNTO COM UM BANCO DE DADOS TERMODINâMICO ADEQUADO, PARA SIMULAR OS EFEITOS DAS ADIçõES SOBRE AS COMPOSIçõES DE METAL E ESCóRIA NA CHEGADA à PRóXIMA ETAPA DO PROCESSO. ESTES DADOS SERãO UTILIZADOS PARA ORIENTAR UM PROGRAMA EXPERIMENTAL DE AJUSTE DA PRáTICA DE VAZAMENTO COM VISTAS A MáXIMA EFICIêNCIA E GARANTIA DA QUALIDADE DESEJA DO PRODUTO.

TAPPING STEEL FROM CONVERTER TO THE LADLE CAUSES STRONG AGITATION OF THE METAL. FOR MANY YEARS, THIS AGITATION HAS BEEN USED IN DIFFERENT WAYS TO MAKE STEELMAKING FASTER AND MORE EFFICIENT AND TO MAKE POSSIBLE THE PRODUCTION OF WELL DEOXIDIZED, CLEAN STEEL. IN THE PRESENT WORK, A EERZ (EFFECTIVE EQUILIBRIUM REACTION ZONE) COUPLED TO A COMPUTATIONAL THERMODYNAMICS SOFTWARE IS USED TO EVALUATE OPTIONS RELATED TO THE ADDITIONS TO THE HEAT DURING TAPPING WHEN PRODUCING LCAK WITH HIGH FORMABILITY. THE EFFECT OF DIFFERENT AMOUNTS OF DEOXIDIZERS AND OF DIFFERENT AMOUNT OF SLAG FORMERS ON THE DEOXIDATION AND ON THE FORMATION OF A SLAG ADEQUATE FOR THE FURTHER PROCESSING OF THE STEEL. FOR THIS PURPOSE, KINETIC DATA FROM PREVIOUS WORK IS USED, TOGETHER WITH AN ADEQUATE COMPUTATIONAL THERMODYNAMIC DATABASE ARE USED TO SIMULATE THE CHANGES HAPPENING TO METAL AND SLAG DURING TAPPING, AND UNTIL THE HEAT REACHES THE NEXT PROCESSING STEP. THESE DATA WILL BE USED TO GUIDE AN EXPERIMENTAL PROGRAM AIMED AT IMPROVING THE TAPPING PRACTICE WITH THE OBJECTIVE OF OPTIMIZING EFFICIENCY AND MINIMIZING THE NUMBER OF HEATS THAT DEVIATE FROM THE DESIRED QUALITY REQUIREMENTS OF THIS PRODUCT.

Palavras-chave

Termodinâmica, vazamento, Cinética, Desoxidação

Computational thermodynamics, Kinetics, LCAK steel, Deoxidation

Como citar

SALES, JULIA MENDES; FERREIRA, DANYELLE RIOS; BATISTA, RAFAELA PEREIRA; SILVA, ANDRE LUIZ VASCONCELLOS DA COSTA E. COMPUTATIONAL THERMODYNAMIC SIMULATION OF ADDITIONS TO LOW-CARBON ALUMINUM KILLED (LCAK) STEEL DURING TAPPING FROM THE CONVERTER – INITIAL MODELING STEPS , p. 862-870. In: 53º Seminário de Aciaria, Fundição e Metalurgia de Não-Ferrosos, São Paulo, Brasil, 2024.
ISSN: 2594-5300 , DOI 10.5151/2594-5300-41453