CONSIDERAÇÕES PARA A SOLDAGEM DOS AÇOS INOXIDÁVEIS AUSTENÍTICOS AISI 310 E ER 316

CONSIDERATIONS FOR THE WELDABILITY OF TYPES AISI 310 AND ER 316 AUSTENITIC STAINLESS STEEL

Autoria

Garcia, Julianna Magalhães; Casanova, Andréy de Moraes Barcelos; Brandão, Luiz Paulo Mendonça

Garcia, Julianna Magalhães

Eu sou esse autor

Casanova, Andréy de Moraes Barcelos

Eu sou esse autor

Brandão, Luiz Paulo Mendonça

Eu sou esse autor

DOI

10.5151/2594-5327-34354

Downloads

Resumo

CONSIDERAÇÕES E ANÁLISES SOBRE PRECIPITAÇÃO ASSOCIADAS COM ALTERAÇÕES MICROESTRUTURAIS DE UM AÇO AUSTENÍTICO AISI310 SOLDADO PELO PROCESSO TIG COM ELETRODO REVESTIDO - ER 316 FORAM REALIZADAS. INOVANDO PELA UTILIZAÇÃO DE UMA SOLDA MENOS NOBRE DE ER 316, EM SUBSTITUIÇÃO À SOLDA DE BASE NÍQUEL - NI, INCONEL 625, AMPLAMENTE USADA E ESTUDA PARA A SOLDAGEM DO AÇO AISI 310, PORÉM MAIS CARA. PARA O ESTUDO FORAM REALIZADOS ENSAIOS DE MICRODUREZA, FERRITOSCOPIA E MEV NAS AMOSTRAS APÓS A SOLDAGEM. PELA MICRODUREZA, O MATERIAL DE SOLDA APRESENTOU VALORES MAIORES QUE OS DO MATERIAL BASE, COM O FERRITOSCÓPIO INDICANDO UM PERCENTUAL DE FERRITA MAGNÉTICA MAIOR NO MATERIAL DE SOLDA. PARA INVESTIGAR ESSAS MUDANÇAS, MICROGRAFIAS OBTIDAS POR MEV, FORAM ANALISADAS. SUGERE-SE A PRESENÇA DE CARBONETO DE CROMO, UM PRECIPITADO SENSITIZANTE E FASE SIGMA, NO MATERIAL BASE E DE SOLDA PELAS MICROGRAFIAS. PRINCIPALMENTE SE APLICARMOS ESSE COMPONENTE SOLDADO EM ALTAS TEMPERATURAS, ESSA PRECIPITAÇÃO SERIA UM FRAGILIZANTE DO MATERIAL E LIMITANTE DA SUA VIDA ÚTIL, TRAZENDO ASSIM, UMA IMPORTANTE DISCUSSÃO PARA ESSE MATERIAL, AMPLAMENTE UTILIZADO EM USINAS TERMOELÉTRICAS.

CONSIDERATIONS AND ANALYSIS ON PRECIPITATION ASSOCIATED WITH MICROSTRUCTURAL CHANGES OF AN AISI310 AUSTENITIC STEEL WELDED WITH TIG ER 316 WERE CARRIED OUT. INNOVATING BY EMPLOYING A LESS NOBLE WELD OF ER 316, REPLACING THE NI-BASED WELD, INCONEL 625, WIDELY USED AND STUDIED FOR WELDING AISI 310, BUT ALSO MORE EXPENSIVE. FOR THE STUDY, MICROHARDNESS, FERRITOSCOPE AND SEM TESTS WERE PERFORMED ON THE SAMPLES AFTER WELDING. DUE TO THE MICRO-HARDNESS, THE WELD MATERIAL SHOWED HIGHER VALUES THAN THOSE OF THE BASE MATERIAL, WITH THE FERRITOSCOPE INDICATING A HIGHER PERCENTAGE OF MAGNETIC FERRITE IN THE WELD MATERIAL. TO INVESTIGATE THESE CHANGES, MICROSCOPIES BY SEM WERE ANALYZED. THE PRESENCE OF CHROMIUM CARBIDE, A SENSITIZING PRECIPITATE AND SIGMA PHASE, IS SUGGESTED IN THE BASE AND WELD MATERIAL BY MICROGRAPHS. ESPECIALLY IF WE APPLY THIS WELDED COMPONENT AT HIGH TEMPERATURES, THIS PRECIPITATION WOULD BE A WEAKENING OF THE MATERIAL AND LIMIT ITS USEFUL LIFE, THUS BRINGING AN IMPORTANT DISCUSSION FOR THIS MATERIAL, WIDELY USED IN THERMOELECTRIC.

Palavras-chave

Aços austeníticos; Ferritoscópio; Precipitação; Transformação de fase

Austenitic steels; Ferritoscope; Precipitation; Phase transformation