DESEMPENHO MECÂNICO E ENCRUAMENTO DO AÇO INOXIDÁVEL LEAN DUPLEX 2304 SUBMETIDO À LAMINAÇÃO A FRIO E RECOZIMENTOS ISÓCRONOS EM BAIXA TEMPERATURA

MECHANICAL BEHAVIOR AND WORK HARDENING OF 2304 A LEAN DUPLEX STAINLESS STEEL SUBJECTED TO COLD ROLLING AND ISOCHRONOUS ANNEALING AT LOW TEMPERATURE

Autoria

Santos, Dagoberto Brandao; Aguiar, Isabela Viegas; Leucas, Bruna Castro Barsand de; Abreu, Thaís Braga de

DOI

10.5151/2594-5327-34313

Downloads

Baixar Artigo 14 Downloads

Resumo

OS AÇOS INOXIDÁVEIS DUPLEX (AID) POSSUEM UMA MICROESTRUTURA BIFÁSICA, COMPOSTA POR FERRITA E AUSTENITA. ESTA MICROESTRUTURA CONFERE AOS AID RESISTÊNCIA MECÂNICA E À CORROSÃO E, POR ISSO, SÃO UTILIZADOS NA INDÚSTRIA PETROQUÍMICA, DE PAPEL E CELULOSE, ÓLEO E GÁS, NAVAL E NUCLEAR. NESSE TRABALHO, O AID LEAN FOI LAMINADO A FRIO ATÉ UMA REDUÇÃO DE 60% DE ESPESSURA E PASSOU POR RECOZIMENTOS DURANTE 30 MIN EM QUATRO TEMPERATURAS: 600, 700, 800 E 900°C. A ANÁLISE MICROESTRUTURAL ENVOLVEU A MICROSCOPIA ELETRÔNICA DE VARREDURA E DIFRAÇÃO DE RAIOS-X. A ANÁLISE DO COMPORTAMENTO MECÂNICO ENVOLVEU ENSAIOS DE TRAÇÃO E DUREZA VICKERS. AS MICROGRAFIAS EVIDENCIARAM A FORMAÇÃO DE MARTENSITA INDUZIDA POR DEFORMAÇÃO (SIM) NOS GRÃOS DE AUSTENITA. AO LONGO DO RECOZIMENTO OBSERVOU-SE O AUMENTO DA PROPORÇÃO DE AUSTENITA EM RELAÇÃO A AMOSTRA LAMINADA A FRIO. A LAMINAÇÃO A FRIO PROVOCOU AUMENTO NAS PROPRIEDADES MECÂNICAS DO MATERIAL E O RECOZIMENTO REDUZIU PROGRESSIVAMENTE TAIS PROPRIEDADES. AS CURVAS DE ENCRUAMENTO REVELARAM ESTÁGIOS BEM DEFINIDOS ENVOLVIDOS NO PROCESSO DE DEFORMAÇÃO PLÁSTICA DO AÇO.

 

DUPLEX STAINLESS STEELS (DSS) HAVE A MICROSTRUCTURE COMPOSED OF FERRITE AND AUSTENITE PHASES. THIS MICROSTRUCTURE PROVIDES TO A DSS MECHANICAL AND CORROSION RESISTANCE AND, THEREFORE, THEY ARE USED IN THE PETROCHEMICAL, PULP AND PAPER, OIL AND GAS, NAVAL AND NUCLEAR INDUSTRIES. DSS 2304 IS A LEAN DUPLEX STAINLESS STEELS (LDSS), BECAUSE IT HAS LOW NICKEL AND MOLYBDENUM AND HIGH NITROGEN AND MANGANESE CONTENTS. THE PRESENT WORK EVALUATED THE MECHANICAL PROPERTIES A 2304 LDSS. THE STEEL WAS COLD-ROLLED TO A 60% REDUCTION AND ANNEALED FOR 30 MIN AT FOUR TEMPERATURES: 600, 700, 800 AND 900°C. THE MICROSTRUCTURAL ANALYSIS WAS CARRIED OUT WITH SCANNING ELECTRON MICROSCOPY (SEM), AND X-RAY DIFFRACTION. THE ANALYSIS OF MECHANICAL PROPERTIES WAS PERFORMED BY TENSILE AND VICKERS HARDNESS TESTS. THE MICROGRAPHS SHOWED WAVYLINES INSIDE THE OF THE  PHASE, ASSOCIATED WITH THE STRAIN-INDUCED MARTENSITE (DIM) FORMATION. COLD ROLLING CAUSED AN INCREASE IN THE MECHANICAL PROPERTIES OF THE MATERIAL AND ANNEALING PROGRESSIVELY RECOVERED THESE PROPERTIES AS THE TEMPERATURE INCREASED. THE WORK HARDENING RATE CURVES REVEALED WELL-DEFINED STAGES INVOLVED IN THE STEEL HARDENING PROCESS, LINKED TO THE DIFFERENT MECHANISMS OF PLASTIC DEFORMATION OF THE AUSTENITE AND FERRITE

Palavras-chave

Aço inoxidável lean duplex; Recozimento; Laminação a frio; Encruamento

Lean duplex stainless steel; Annealing; Cold Rolling; Work hardening