DESENVOLVIMENTO DE AÇO AHSS DE TERCEIRA GERAÇÃO DE 1000 MPA DE LIMITE DE RESISTêNCIA EM ESCALA DE LABORATÓRIO NA USIMINAS

DEVELOPMENT OF A 1000 MPA THIRD GENERATION AHSS IN LABORATORY SCALE AT USIMINAS

Autoria

COSTA, FERNANDO DE SOUZA; RODRIGUES, PAULO JOSÉ DUARTE; JUNIOR, GUILHERME BRITO MENEGAZ

COSTA, FERNANDO DE SOUZA

Eu sou esse autor

RODRIGUES, PAULO JOSÉ DUARTE

Eu sou esse autor

JUNIOR, GUILHERME BRITO MENEGAZ

Eu sou esse autor

DOI

10.5151/2594-5327-40522

Downloads

Resumo

DESDE A DéCADA DE 1990, A USIMINAS ESTUDA AçOS AVANçADOS DE ALTA RESISTêNCIA (AHSS). AO LONGO DO TEMPO, ESTA FAMíLIA DE AçOS, QUE INCLUI EM SUA “PRIMEIRA GERAçãO” PRODUTOS COMO AçO DUAL PHASE (DP), PLASTICIDADE INDUZIDA POR TRANSFORMAçãO (TRIP), AçO MULTICONSTITUíDO (CP) E MARTENSíTICO (MART), TORNOU-SE UMA REALIDADE CONSOLIDADA NA INDúSTRIA AUTOMOTIVA. NOS úLTIMOS ANOS, PORéM, O FOCO TEM SIDO NO DESENVOLVIMENTO DE NOVOS AHSS, CHAMADOS DE “AHSS DE TERCEIRA GERAçãO”, QUE PROMETE INCLUIR MATERIAIS COM MICROESTRUTURAS AINDA MAIS COMPLEXAS, COMBINANDO FASES DE ALTA RESISTêNCIA MECâNICA, COMO FERRITA DE GRANULAçãO ULTRAFINA, MARTENSITA OU BAINITA E QUANTIDADES SIGNIFICATIVAS DE UM CONSTITUINTE COM BOA DUCTILIDADE (POR EXEMPLO, AUSTENITA). ESTE TRABALHO APRESENTA OS PRINCIPAIS RESULTADOS DO DESENVOLVIMENTO EM ESCALA DE LABORATóRIO DE UM AHSS DE TERCEIRA GERAçãO, COM GRAU DE RESISTêNCIA 1000 MPA, COM EFEITO TRIP, NA USIMINAS. PARA TANTO, FORAM REALIZADOS DIVERSOS CICLOS TéRMICOS EM UMA MáQUINA GLEEBLE E EM UM DILATôMETRO. O MATERIAL OBTIDO APRESENTOU BOA HOMOGENEIDADE MICROESTRUTURAL, ALTA DUCTILIDADE FACE AO SEU GRAU DE RESISTêNCIA MECâNICA, ALIADO A BOM POTENCIAL DE ABSORçãO DE ENERGIA.

SINCE THE 1990S, USIMINAS HAS BEEN STUDYING ADVANCED HIGH STRENGTH STEEL (AHSS). OVER TIME, THIS FAMILY OF STEELS, WHICH INCLUDES IN ITS “FIRST GENERATION” PRODUCTS SUCH AS DUAL PHASE (DP), TRANSFORMATION INDUCED PLASTICITY (TRIP), MULTI-CONSTITUTED COMPLEX PHASE (CP) AND MARTENSITIC (MART), HAS BECOME A CONSOLIDATED REALITY IN THE AUTOMOTIVE INDUSTRY. IN RECENT YEARS, HOWEVER, THE FOCUS HAS BEEN ON THE DEVELOPMENT OF NEW AHSS, CALLED “THIRD GENERATION AHSS”, WHICH PROMISES TO INCLUDE MATERIALS WITH EVEN MORE COMPLEX MICROSTRUCTURES, COMBINING PHASES OF HIGH MECHANICAL STRENGTH, SUCH AS ULTRAFINE GRAINED FERRITE, MARTENSITE OR BAINITE, AND SIGNIFICANT AMOUNTS OF A CONSTITUENT WITH GOOD DUCTILITY (E.G., AUSTENITE). THIS WORK PRESENTS THE MAIN RESULTS OF THE DEVELOPMENT IN LABORATORY SCALE OF A THIRD GENERATION AHSS OF THE 1000 MPA STRENGTH GRADE, WITH TRIP EFFECT, AT USIMINAS. FOR THIS PURPOSE, SEVERAL THERMAL CYCLES WERE PERFORMED IN A GLEEBLE MACHINE AND IN A DILATOMETER. THE MATERIAL OBTAINED SHOWED GOOD MICROSTRUCTURAL HOMOGENEITY, HIGH DUCTILITY IN VIEW OF ITS MECHANICAL STRENGTH GRADE, COMBINED WITH GOOD POTENTIAL FOR ENERGY ABSORPTION.

Palavras-chave

AHSS de Terceira Geração; Efeito TRIP; Aplicação automotiva

Third Generation AHSS; TRIP effect; Automotive application.