DESENVOLVIMENTO DE AÇO BAIXO CARBONO EM ACIARIA ELÉTRICA PARA PRODUÇÃO DE ARAMES GALVANIZADOS

DEVELOPMENT OF LOW CARBON STEEL IN AN ELECTRIC STEEL SHOP FOR GALVANIZED WIRE PRODUCTION

Autoria

Nicolodi, Anderson; Ilha, Ricardo; Forte, Sabrina Karnopp; Bielefeldt, Wagner Viana; Vilela, Antônio Cezar Faria

DOI

10.5151/2594-5327-34426

Downloads

Baixar Artigo 8 Downloads

Resumo

O OBJETIVO DESTE ESTUDO FOI VIABILIZAR A PRODUÇÃO DE UM AÇO BAIXO CARBONO EM ACIARIA ELÉTRICA PARA FABRICAÇÃO DE ARAMES GALVANIZADOS. FORAM PRODUZIDOS SEIS AÇOS BASEADOS NO AÇO SAE 1005: UM AÇO EM ACIARIA A OXIGÊNIO DE USINA INTEGRADA, UM AÇO EM ACIARIA A OXIGÊNIO DE USINA INTEGRADA COM ADIÇÃO DE BORO, UM AÇO EM ACIARIA ELÉTRICA E TRÊS AÇOS COM DIFERENTES NÍVEIS DE ADIÇÃO DE BORO EM ACIARIA ELÉTRICA. ESTES AÇOS FORAM EMPREGADOS NA PRODUÇÃO DE ARAMES GALVANIZADOS BWG 12. A CARACTERIZAÇÃO DOS AÇOS E ARAMES GALVANIZADOS VISOU DETERMINAR COMPOSIÇÃO QUÍMICA, RESISTÊNCIA MECÂNICA (ENSAIO DE TRAÇÃO) E COMPORTAMENTO FRENTE AO ENVELHECIMENTO ESTÁTICO. OS RESULTADOS OBTIDOS INDICAM QUE A ADIÇÃO DE BORO NA PRODUÇÃO DE AÇO EM ACIARIA ELÉTRICA PERMITE REDUZIR CONSIDERAVELMENTE O LIMITE DE RESISTÊNCIA A TRAÇÃO E AUMENTAR O ALONGAMENTO DE ARAMES GALVANIZADOS, TORNANDO-OS SIMILARES AOS PRODUZIDOS EM USINAS INTEGRADAS. ESTAS OBSERVAÇÕES SÃO MAXIMIZADAS PARA O AÇO COM TEOR DE BORO INTERMEDIÁRIO ESTUDADO. NAS CONDIÇÕES EM QUE O ESTUDO FOI REALIZADO, OBSERVOU-SE QUE A PRODUÇÃO DE UM AÇO BAIXO CARBONO EM ACIARIA ELÉTRICA PARA FABRICAÇÃO DE ARAMES GALVANIZADOS PODE SER REALIZADA COM ADIÇÕES ADEQUADAS DE BORO NA COMPOSIÇÃO DOS AÇOS.

 

THIS STUDY AIMED TO MAKE FEASIBLE THE PRODUCTION OF A LOW CARBON STEEL IN AN ELECTRIC STEEL SHOP FOR GALVANIZED WIRE MANUFACTURING. SIX STEELS WERE PRODUCED BASED ON THE SAE 1005 STANDARD: ONE STEEL PRODUCED AT AN INTEGRATED STEEL MILL EQUIPPED WITH A BASIC OXYGEN FURNACE, ONE STEEL WITH BORON ADDITION PRODUCED AT AN INTEGRATED STEEL MILL EQUIPPED WITH A BASIC OXYGEN FURNACE, ONE STEEL PRODUCED AT AN ELECTRICAL STEEL SHOP, AND THREE STEELS WITH DIFFERENT LEVELS OF BORON ADDITION PRODUCED AT AN ELECTRICAL STEEL SHOP. THESE STEELS WERE USED FOR PRODUCTION OF GALVANIZED WIRES BWG 12. THE CHARACTERIZATION OF THE STEELS AND GALVANIZED WIRES AIMED TO DETERMINE CHEMICAL COMPOSITION, MECHANICAL STRENGTH (TENSILE TEST) AND STRAIN AGEING BEHAVIOR. THE RESULTS OBTAINED INDICATE THAT THE ADDITION OF BORON IN THE PRODUCTION OF STEEL IN AN ELECTRIC MELT SHOP CONSIDERABLY REDUCES THE ULTIMATE TENSILE STRENGTH AND INCREASES THE ELONGATION OF GALVANIZED WIRES, MAKING THEM SIMILAR TO THOSE PRODUCED IN INTEGRATED STEEL MILLS. THESE OBSERVATIONS ARE EVEN CLEARER FOR THE STEEL WITH INTERMEDIATE BORON CONTENT. UNDER THE CONDITIONS IN WHICH THIS STUDY WAS CARRIED OUT, IT WAS OBSERVED THAT THE PRODUCTION OF LOW CARBON STEEL IN AN ELECTRIC STEEL SHOP FOR THE MANUFACTURE OF GALVANIZED WIRES COULD BE CARRIED OUT WITH APPROPRIATE ADDITIONS OF BORON IN THE STEEL COMPOSITION.

Palavras-chave

Aço baixo carbono; Boro; Arame galvanizado; Aciaria elétrica

Low carbon steel; Boron; Galvanized wire; Electric steel shop