O OBJETIVO é DESENVOLVER UMA ROCHA ARTIFICIAL USANDO COMO RESíDUO O MáRMORE FRAGMENTADO JUNTO COM UMA RESINA DE EPóXI MOSTRANDO A VIABILIDADE TéCNICA FRENTE àS ROCHAS NATURAIS E USAR A FIBRA NATURAL DE FIQUE PARA REFORçO DESTE MáRMORE COMPARANDO COM A FIBRA DE VIDRO. O MáRMORE ARTIFICIAL FOI PRODUZIDO ATRAVéS DE DUAS COMPOSIçõES SELECIONADAS ATRAVéS DA DETERMINAçãO DA DENSIDADE VIBRADA DAS PARTíCULAS, ADOTOU-SE O MéTODO DE VIBRAçãO, COMPRESSãO E VáCUO, SENDO COMPACTADO A QUENTE A 90ºC DURANTE 20 MIN. AS ROCHAS DAS COMPOSIçõES CP4 E CP8 FORAM PRODUZIDAS INICIALMENTE COM DOIS TEORES DE RESINA, 5 E 10% EM RELAçãO A MASSA DE RESíDUO UTILIZADO, SENDO AS ROCHAS COM 10% SELECIONADAS PARA A ETAPA DE LAMINAçãO DEVIDO A APRESENTAREM MELHORES PROPRIEDADES FíSICAS E MECâNICAS. OS RESULTADOS DE FLEXãO INDICARAM UMA MELHORA NO DESEMPENHO DAS ROCHAS ARTIFICIAIS EM RELAçãO AOS MáRMORES NATURAIS, E OBSERVOU-SE UMA MELHORIA NO DESEMPENHO DAS ROCHAS ARTIFICIAIS QUANDO LAMINADAS COM FIBRA DE FIQUE
THE OBJECTIVE IS TO DEVELOP AN ARTIFICIAL STONE USING FRAGMENTED MARBLE AS WASTE TOGETHER WITH AN EPOXY RESIN SHOWING TECHNICAL VIABILITY COMPARED TO NATURAL STONE AND USING NATURAL FIBER TO REINFORCE THIS MARBLE COMPARED TO FIBERGLASS. THE ARTIFICIAL MARBLE WAS PRODUCED USING TWO COMPOSITIONS SELECTED BY DETERMINING THE VIBRATED DENSITY OF THE PARTICLES, USING THE VIBRATION, COMPRESSION AND VACUUM METHOD, BEING HOT COMPACTED AT 90ºC FOR 20 MIN. THE STONES OF COMPOSITIONS CP4 AND CP8 WERE INITIALLY PRODUCED WITH TWO RESIN LEVELS, 5 AND 10% IN RELATION TO THE MASS OF WASTE USED, WITH STONES WITH 10% SELECTED FOR THE LAMINATION STAGE DUE TO THEIR BETTER PHYSICAL AND MECHANICAL PROPERTIES. BENDING RESULTS INDICATED AN IMPROVEMENT IN THE PERFORMANCE OF ARTIFICIAL STONES IN RELATION TO NATURAL MARBLE, AND AN IMPROVEMENT IN THE PERFORMANCE OF ARTIFICIAL STONES WAS OBSERVED WHEN LAMINATED WITH FIBERGLASS
Palavras-chave
Rocha Artificial; fibra natural; vácuo; Laminação
Artificial Stone; Natural Fiber; Vacuum; Lamination.
Como citar
CAMPOS, MAYARA TITO;
COSTA, ELAINE APARECIDA SANTOS CARVALHO;
MIRANDA, RAFAEL BITTENCOURT;
LOPES, FELIPE PERISSÉ DUARTE;
VIEIRA, CARLOS MAURÍCIO FONTES;
LOPERA, HENRY ALONSO COLORADO;
SOUZA, DJALMA.
DESENVOLVIMENTO DE MÁRMORE ARTIFICIAL REFORÇADO COM FIBRA NATURAL
,
p. 986-997.
In: 77º Congresso Anual da ABM - Internacional,
São Paulo, Brasil,
2024.
ISSN: 2594-5327
, DOI 10.5151/2594-5327-40641