DESENVOLVIMENTO DE PROTOCOLO DE MEDIDA E OBTENÇÃO DO MÓDULO DE ELASTICIDADE DO CONE DE GUTA-PERCHA BIOCERÂMICA

DEVELOPMENT OF A PROTOCOL OF MEASUREMENT AND OBTAINING THE ELASTICITY MODULE OF THE BIOCERAMIC GUTAPERCHA CONE

Autoria

Nunes, Adriana Marques

Nunes, Adriana Marques

Eu sou esse autor

DOI

10.5151/2594-5327-34612

Downloads

Resumo

PURPOSE: O OBJETIVO DESTE TRABALHO FOI DESENVOLVER UM MÉTODO DE CARACTERIZAÇÃO E OBTER O VALOR DO MÓDULO DE ELASTICIDADE (E) DA GUTA-PERCHA (GP) ATRAVÉS DO ENSAIO DE DUREZA DINÂMICO COM CARGA E DESCARGA. METHODS: FOI UTILIZADO CONE DE GP CONVENCIONAL (C), CONE IMPREGNADO COM ÓXIDO DE ZIRCÔNIA, CONHECIDO COMO CONE DE GP BIOCERÂMICO (BC), E POR ÚLTIMO UM CORTE AXIAL DE UMA RAIZ DENTAL COM TRATAMENTO ENDODÔNTICO OBTURADO COM CIMENTO ENDODÔNTICO BIOCERÂMICO E CONE DE GUTA-PERCHA BIOCERÂMICO (BC). O ENSAIO PARA OBTENÇÃO DO PROTOCOLO DE MEDIDA FOI REALIZADO COM AS CARGAS DE 10MN, 20MN, 30MN, 50MN E 100MN. APÓS ANÁLISE DAS IMPRESSÕES NA GUTA-PERCHA E DOS RESULTADOS NUMÉRICOS OBTIDOS PODE-SE CONCLUIR QUE A CARGA DE 20MN PARA A GUTA-PERCHA FOI A IDEAL. EM SEGUIDA, APÓS DEFINIÇÃO DA CARGA IDEAL, FOI REALIZADO O ENSAIO DE DUREZA NA GP DA RAIZ COM TRATAMENTO DE CANAL, ONDE SE FEZ 10 IMPRESSÕES AO LONGO DO MATERIAL ESPAÇANDO A DISTÂNCIA DE 200 µM ENTRE AS IMPRESSÕES, RESPEITANDO A ÁREA QUE SOFRE COM TENSÕES RESIDUAIS APÓS O ENSAIO. OS 10 RESULTADOS FORAM SUBMETIDOS AO CÁLCULO DE MÉDIA E DESVIO PADRÃO DOS VALORES DE E OBTIDOS. RESULTS: O VALORES DE E OBTIDOS PARA AS GP C E BC FORAM DE 1.7MPA E PARA A GP DA RAIZ NO CORTE AXIAL FOI DE 0,7MPA, USANDO UMA CARGA 20MN NO ENSAIO DE DUREZA COM CARGA E DESCARGA.

PURPOSE: THE OBJECTIVE OF THIS WORK WAS TO DEVELOP A CHARACTERIZATION METHOD AND OBTAIN THE VALUE OF THE MODULUS OF ELASTICITY (E) OF GUTTA-PERCHA (GP) THROUGH THE DYNAMIC HARDNESS TEST WITH LOADING AND UNLOADING. METHODS: CONVENTIONAL GP CONE (C), CONE IMPREGNATED WITH ZIRCONIA OXIDE, KNOWN AS BIOCERAMIC GP CONE (BC), AND FINALLY AN AXIAL SECTION OF A DENTAL ROOT WITH ENDODONTIC TREATMENT FILLED WITH BIOCERAMIC ENDODONTIC CEMENT AND BIOCERAMIC GUTTA-PERCHA (BC). THE TEST TO OBTAIN THE MEASUREMENT PROTOCOL WAS PERFORMED WITH LOADS OF 10MN, 20MN, 30MN, 50MN AND 100MN. AFTER ANALYZING THE IMPRESSIONS ON THE GUTTA-PERCHA AND THE NUMERICAL RESULTS OBTAINED, IT CAN BE CONCLUDED THAT THE LOAD OF 20MN FOR THE GUTTA-PERCHA WAS IDEAL. THEN, AFTER DEFINING THE IDEAL LOAD, THE HARDNESS TEST WAS PERFORMED ON THE ROOT GP WITH ROOT CANAL TREATMENT, WHERE 10 IMPRESSIONS WERE MADE ALONG THE MATERIAL, SPACING A DISTANCE OF 200 µM BETWEEN THE IMPRESSIONS, RESPECTING THE AREA THAT SUFFERS FROM STRESSES AFTER THE TEST. THE 10 RESULTS WERE SUBJECTED TO THE CALCULATION OF THE MEAN AND STANDARD DEVIATION OF THE OBTAINED E VALUES. RESULTS: THE E VALUES ​​OBTAINED FOR THE GP C AND BC WERE 1.7MPA AND FOR THE ROOT GP IN THE AXIAL SECTION IT WAS 0.7MPA, USING A 20MN LOAD IN THE HARDNESS TEST WITH LOADING AND UNLOADING.

Palavras-chave

materiais obturadores, Biocerâmico; endodontia, dureza; módulo de young

Filling materials; Bioceramics; Endodontics; Hardness; Young Modulus.