DESENVOLVIMENTO DO AÇO SAE1045 LAMINADO A FRIO NA USIMINAS DE CUBATÃO

DEVELOPMENT OF SAE1045 COLD-ROLLED STEEL PROCESS AT USIMINAS’ CUBATÃO TANDEM COLD MILL

DOI

10.5151/2594-5297-34325

Downloads

Baixar Artigo 6 Downloads

Resumo

O DESENVOLVIMENTO DO AçO SAE1045 LAMINADO A FRIO PARA APLICAçãO NA INDúSTRIA DE CONSTRUçãO MECâNICA TEM COMO OBJETIVO ATENDER ESTE SETOR DO MERCADO DE AçOS PLANOS QUE VêM SE TORNANDO MAIS EXIGENTE QUANTO à QUALIDADE DO MATERIAL ADQUIRIDO, RELACIONADA, PRINCIPALMENTE àS CARACTERíSTICAS DIMENSIONAIS E PROPRIEDADES MECâNICAS. O PROCESSO DE LAMINAçãO A QUENTE GERA NA BOBINA UMA MICROESTRUTURA PERLíTICA FINA QUE CONFERE AO AçO UM ALTO GRAU DE RESISTêNCIA, ALCANçANDO UM LIMITE DE ESCOAMENTO DE ATé 600MPA . COMO CONSEQUêNCIA, ESTE AçO EXCEDE A CAPACIDADE DEFINIDA NO PROJETO DO LAMINADOR DE TIRAS A FRIO DA PLANTA DA USIMINAS DE CUBATãO, O QUAL FOI ESPECIFICADO PARA A LAMINAçãO DE AçOS COM BAIXO TEOR DE CARBONO. PARA O PROCESSO DO SAE1045 FORAM REALIZADAS ALTERAçõES NOS PARâMETROS DE LAMINAçãO, INCLUINDO O MODELO MATEMáTICO, O COROAMENTO MECâNICO DOS CILINDROS DE TRABALHO E O SISTEMA DE REFRIGERAçãO DAS CADEIRAS. AS ALTERAçõES VISARAM O ATENDIMENTO AO CLIENTE, GARANTINDO A QUALIDADE DA TIRA LAMINADA EM RELAçãO à ESPESSURA, PLANICIDADE E ACABAMENTO SUPERFICIAL, SEM COMPROMETER A SEGURANçA DO PROCESSO E A INTEGRIDADE DO EQUIPAMENTO. O PROCESSO DE LAMINAçãO E A QUALIDADE DO PRODUTO LAMINADO FORAM SATISFATóRIOS, POSSIBILITANDO O ATENDIMENTO AO CLIENTE COM QUALIDADE E REPETITIVIDADE DOS RESULTADOS.

 

THE DEVELOPMENT OF SAE1045 COLD-ROLLED STEEL FOR APPLICATION IN THE MECHANICAL CONSTRUCTION INDUSTRY AIMS TO MEET THE SECTOR OF THE FLAT STEEL MARKET THAT HAS BECOME MORE DEMANDING IN TERMS OF THE QUALITY OF THE MATERIAL ACQUIRED, RELATED MAINLY TO THE DIMENSIONAL CHARACTERISTICS AND MECHANICAL PROPERTIES. THE HOT ROLLING PROCESS GENERATES IN THE COIL A FINE PEARLITIC MICROSTRUCTURE THAT GIVES THE STEEL A HIGH DEGREE OF RESISTANCE, REACHING A YIELD STRENGTH UP TO 600MPA. CONSEQUENTLY, THIS STEEL EXCEEDS THE CAPACITY DEFINED IN THE PROJECT OF THE TANDEM COLD MILL AT USIMINAS’ CUBATãO PLANT, WHICH WAS SPECIFIED FOR ROLLING LOW CARBON STEELS. FOR THE PROCESS OF SAE1045 CHANGES WERE MADE IN THE PROCESS PARAMETERS, MATHEMATICAL MODEL, MECHANICAL CROWNING OF THE WORK ROLLS, AND IN THE STANDS’ COOLING SYSTEM. THE CHANGES WERE AIMED AT CUSTOMER SERVICE, ENSURING THE QUALITY OF THE ROLLED STRIP IN RELATION TO THICKNESS, FLATNESS, AND SURFACE FINISHING, WITHOUT COMPROMISING THE SAFETY OF THE PROCESS AND THE INTEGRITY OF THE EQUIPMENT. THE ROLLING PROCESS AND THE QUALITY OF THE ROLLED PRODUCT WERE SATISFACTORY, SERVING THE CUSTOMER WITH QUALITY AND REPEATABLE RESULTS.

Palavras-chave

SAE1045; laminado a frio

SAE1045; COLD-ROLLED STEEL.

Como citar

Apolonio, Gabriela Ribeiro. DESENVOLVIMENTO DO AÇO SAE1045 LAMINADO A FRIO NA USIMINAS DE CUBATÃO , p. 127-136. In: 57° Seminário de Laminação e Conformação de Metais, São Paulo, 2022.
ISSN: 2594-5297 , DOI 10.5151/2594-5297-34325