DESENVOLVIMENTO DO GRANITO ARTIFICIAL PRETO SÃO BENEDITO EM MATRIZ EPÓXIDICA

DEVELOPMENT OF THE BLACK ARTIFICIAL GRANITE SÃO BENEDITO IN EPOXID MATRIX

Autoria

Souza, Vitor da Silva de

DOI

10.5151/2594-5327-34124

Downloads

Baixar Artigo 48 Downloads

Resumo

O GRANITO NATURAL PRETO SÃO BENEDITO É ATUALMENTE COMERCIALIZADO DEVIDO A SEU PERFIL ESTÉTICO E SUA COLORAÇÃO PRETA, UTILIZADA PARA DESTACAR ELEMENTOS. ESSE AUMENTO DA COMERCIALIZAÇÃO POR OUTRO LADO, ACABA GERANDO ELEVADOS NÚMEROS DE RESÍDUOS. O OBJETIVO DO PROJETO É PROPOR UMA FINALIDADE VIÁVEL AO RESÍDUO PARA O DESENVOLVIMENTO DE ROCHA ARTIFICIAL PARA COMERCIALIZAÇÃO E APLICAÇÃO EM CONSTRUÇÃO CIVIL. A METODOLOGIA UTILIZADA FOI O PROCESSO “VIBRAÇÃO, COMPRESSÃO E VÁCUO” QUE ATUALMENTE É UTILIZADA PELA INDÚSTRIA DE ROCHAS ARTIFICIAIS. NESSE PROCESSO O RESÍDUO FOI MISTURADO EM MATRIZ EPÓXI E POSTERIORMENTE SUBMETIDO A TEMPERATURA DE 90ºC SOB PRESSÃO DE 10TON A FIM DE PROMOVER A POLIMERIZAÇÃO. A ROCHA ARTIFICIAL DESENVOLVIDA FOI SUBMETIDA AOS TESTES DE ÍNDICE FÍSICO E MECÂNICO SEGUINDO AS NORMAS. OS RESULTADOS OBTIDOS PARA A RASB 20% PARA A DENSIDADE FOI DE 2,21G/CM³, POROSIDADE DE 0,23 ± 0,06% E ABSORÇÃO 0,1 ± 0,02%, SUPERIOR A RASB 30%. OS VALORES DEMONSTRAM COMPATÍVEL COM OS GRANITOS ARTIFICIAIS COMERCIALIZADOS. DE ACORDO COM A CLASSIFICAÇÃO PROPOSTA POR CHIODI E RODRIGUEZ, A ROCHA PRODUZIDA É CONSIDERADA MATERIAL DE ALTA RESISTÊNCIA QUANDO SUBMETIDOS A TENSÃO DE FLEXÃO. CONCLUÍSSE QUE OS VALORES APRESENTADOS OBTIVERAM MELHORIA NAS PROPRIEDADES FÍSICO-MECÂNICAS, DEIXANDO MAIS CONSISTENTES DO QUE OS NATURAIS.

 

SãO BENEDITO NATURAL GRANITE IS CURRENTLY MARKETED DUE TO ITS AESTHETIC PROFILE AND ITS BLACK COLOR, USED TO HIGHLIGHT ELEMENTS. THIS INCREASE IN SALES, ON THE OTHER HAND, ENDS UP GENERATING HIGH NUMBERS OF WASTE. THE OBJECTIVE OF THE PROJECT IS TO PROPOSE A VIABLE PURPOSE TO THE RESIDUE FOR THE DEVELOPMENT OF ARTIFICIAL STONE FOR COMMERCIALIZATION AND APPLICATION IN CIVIL CONSTRUCTION. THE METHODOLOGY USED WAS THE “VIBRATION, COMPRESSION AND VACUUM” PROCESS THAT IS CURRENTLY USED BY THE ARTIFICIAL STONE INDUSTRY. IN THIS PROCESS, THE RESIDUE WAS MIXED IN AN EPOXY MATRIX AND SUBSEQUENTLY SUBMITTED TO A TEMPERATURE OF 90ºC UNDER 10TON PRESSURE IN ORDER TO PROMOTE POLYMERIZATION. THE DEVELOPED ARTIFICIAL STONE WAS SUBJECTED TO PHYSICAL AND MECHANICAL INDEX TESTS FOLLOWING THE STANDARDS. THE RESULTS OBTAINED FOR THE RASB 20% FOR THE DENSITY WAS 2.21G/CM³, POROSITY OF 0.23 ± 0.06% AND ABSORPTION 0.1 ±0.02%, HIGHER THAN RASB 30%. THE VALUES SHOW COMPATIBILITY WITH THE ARTIFICIAL GRANITES COMMERCIALIZED. ACCORDING TO THE CLASSIFICATION PROPOSED BY CHIODI AND RODRIGUEZ, THE STONE PRODUCED IS CONSIDERED A HIGH-STRENGTH MATERIAL WHEN SUBJECTED TO BENDING STRESS. IT WAS CONCLUDED THAT THE VALUES PRESENTED OBTAINED AN IMPROVEMENT IN THE PHYSICAL-MECHANICAL PROPERTIES, MAKING THEM MORE CONSISTENT THAN THE NATURAL ONES.

Palavras-chave

Rocha Artificial; Granito; Resina Epóxi; Revestimento.

Artificial Stone; Granite; Resin Epoxy; Redress.