ATUALMENTE, A BUSCA POR MATERIAIS QUE COMBINEM ALTO DESEMPENHO MECâNICO, BAIXO CUSTO E SUSTENTABILIDADE ECOLóGICA TEM SE INTENSIFICADO EM DIVERSAS APLICAçõES. ESTE ESTUDO FOCA NA APLICAçãO DE RESíDUOS DE CAULIM COMO AGENTE DE REFORçO EM UMA MATRIZ POLIMéRICA. OS COMPóSITOS FORAM FABRICADOS CORPOS DE PROVA MANUALMENTE, CONFORME AS NORMAS ASTM D638-2014 PARA TESTES DE RESISTêNCIA à TRAçãO E ASTM D790-2017 PARA TESTES DE FLEXãO EM TRêS PONTOS. OS MATERIAIS OBTIDOS FORAM CARACTERIZADOS MECANICAMENTE ATRAVéS DE ENSAIOS DE TRAçãO, ONDE FORAM AVALIADOS A TENSãO, O MóDULO DE YOUNG E A DEFORMAçãO, BEM COMO ATRAVéS DE ENSAIOS DE FLEXãO, QUE FORNECERAM DADOS DE TENSãO E MóDULO DE ELASTICIDADE. OS RESULTADOS INDICARAM QUE O AUMENTO NA QUANTIDADE DE RESíDUO DE CAULIM LEVOU A UMA REDUçãO NA RESISTêNCIA MECâNICA EM TRAçãO E FLEXãO EM COMPARAçãO COM A MATRIZ POLIMéRICA PURA. DESSA FORMA, A UTILIZAçãO DE RESíDUO CAULIM AINDA CONSTITUI-SE COMO UMA MATéRIA-PRIMA INFLUENTE NO DESENVOLVIMENTO DE MATERIAIS COMPóSITOS
CURRENTLY, THE SEARCH FOR MATERIALS THAT COMBINE HIGH MECHANICAL PERFORMANCE, LOW COST AND ECOLOGICAL SUSTAINABILITY HAS INTENSIFIED IN SEVERAL APPLICATIONS. THIS STUDY FOCUSES ON THE APPLICATION OF KAOLIN WASTE AS A REINFORCING AGENT IN A POLYMER MATRIX. THE MECHANICAL PROPERTIES OF THIS COMPOSITE WERE EVALUATED BY MANUFACTURING TEST SPECIMENS IN SILICONE MOLDS, IN ACCORDANCE WITH ASTM D638-2014 FOR TENSILE STRENGTH TESTS AND ASTM D790-2017 FOR THREE-POINT BENDING TESTS. THE MATERIALS OBTAINED WERE MECHANICALLY CHARACTERIZED THROUGH TENSILE TESTS, WHERE TENSION, YOUNG'S MODULUS AND DEFORMATION WERE MEASURED, AS WELL AS THROUGH FLEXION TESTS, WHICH ALSO PROVIDED TENSION AND YOUNG'S MODULUS DATA. THE RESULTS INDICATED THAT THE INCREASE IN THE AMOUNT OF KAOLIN RESIDUE LED TO A REDUCTION IN MECHANICAL STRENGTH COMPARED TO THE PURE POLYMER MATRIX. IT WAS OBSERVED THAT THE TENSILE AND FLEXURAL MODULI RESULTED IN F (CALCULATED) VALUES GREATER THAN THE CRITICAL F, AND FOR TRACTION, THE DEFORMATION ALSO PRESENTED A F (CALCULATED) VALUE GREATER THAN THE CRITICAL F
Palavras-chave
Caulim; Resíduo; Compósitos
Kaolin; Residue; Composites
Como citar
NASCIMENTO, JOELLY VERA;
SOUSA, PALOMA SUELLEN LIMA DE;
SOUZA, SARAH GABRIELLY BRANDÃO DE;
ROSA, DIEMISON LIRA SANTA;
NASCIMENTO, DAMARES DA CRUZ BARBOSA;
SILVA, ALISSON CLAY RIOS DA;
CANDIDO, VERÔNICA SCARPINI.
EFEITO DA ADIÇÃO DE RESÍDUO DE CAULIM NAS PROPRIEDADES MECÂNICAS DE COMPÓSITOS DE MATRIZ POLIMÉRICA
,
p. 318-327.
In: 22º Enemet - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas,
São Paulo, Brasil,
2024.
ISSN: 2594-4711
, DOI 10.5151/2594-4711-41013